RESUMO

This research assessed the effects of pre-heating on the physical-mechanical-chemical properties of different resin composites. For this, resin composites were evaluated in 6 levels: Admira/ADM, Vitra/VIT, Filtek Supreme/FS, Filtek Supreme Flowable/FSF, Filtek One/FO, and Filtek Bulk Fill Flowable/FBF; temperature was evaluated in 4 levels using a composite heater: room temperature/22 ºC, 37 ºC, 54 ºC, and 68 ºC. Response variables were: degree of conversion/DC, flexural strength/FS and color stability/ΔE (immediately after light curing/LC, after 7 days of dark-dry-storage, and after 24 h and 3 days of artificial aging in water at 60 ºC). Data were subjected to 2-way ANOVA (DC and FR) and 3-way repeated measurements ANOVA (ΔE), all followed by Tukey's test (α = 5%). DC were similar (FBF, FS, and FSF) or increased (ADM, FO, and VIT) as the temperature increased. Results of FR were unchanged or increased for all composites except VIT and ADM. High-viscosity composites (VIT and FS) showed higher FR values than low-viscosity composite (FSF). For bulk-fill composites, FBF and FO showed similar results, but lower than high-viscosity composites. Results of color stability showed acceptable values up to 3 days aging except for ADM and FSF. ΔE was not influenced by pre-heating and, overall, ΔE: FS < VIT < FO < FSF < ADM < FBF. Only VIT and FS showed ΔE ≤ 3.3 (clinical threshold). Therefore, the effects of pre-heating depend on the material. The tested materials generally showed similar or enhanced properties after pre-heating (except ADM and VIT).

RESUMO

The aim of this study was to evaluate the chemical and morphological effects of different lasers as a final surface treatment for endodontic therapy through energy dispersive X-ray spectroscopy (EDS) and scanning electron microscopy (SEM) respectively. Twenty-five maxillary canines were selected and instrumented with K3 system. Roots were randomly distributed into five groups (n = 5) according to the surface treatment: GI (distilled water), GII (NaOCl + EDTA), GIII (NaOCl + EDTA + 980 nm diode laser), GIV (NaOCl + EDTA+ 1,064 nm Nd:YAG laser), and GV (NaOCl + EDTA+ 2,780 nm Er, Cr:YSGG laser). Lasers were applied for 20 s and samples were bisected, exposing the treated surface and then subjected to elements quantification by EDS and morphological evaluation by scanning electron microscope (SEM). EDS data were submitted to ANOVA-two way, and SEM scores were submitted to two-way Kruskal-Wallis and Dunn's tests. The EDS analysis showed no difference for the chemical elements and Ca/P ratio between groups (p > .05). Statistical analysis showed more intense results for GV and less intense results for GI (p < .05). The GIII showed an amorphous organic matrix surface, while GV provided greater removal of intertubular dentin forming craters, and GIV promoted dentin fusion. The EDS method used in this study was not able to verify any chemical changes in root canal dentin; Nd:YAG, Er, Cr:YSGG, and 980 nm diode laser were capable of modifying the dentin morphology, correlating characteristics features for each one, which are essential clinical knowledge to establish the correct indication for each case. RESEARCH HIGHLIGHTS: EDS was not able to verify any chemical changes in root canal dentin after 980 nm diode, Nd:YAG and Er;Cr:YSGG laser treatments Nd:YAG, Er, Cr:YSGG, and 980 nm diode laser modified dentin morphology, correlating characteristics features for each one.

Assuntos

RESUMO

OBJECTIVES: To evaluate the effect of the bleaching with 35% hydrogen peroxide either activated or not by a 970nm diode laser on the chemical stability and dentin surface morphology of intracoronary dentin. METHODS: Twenty-seven slabs of intracoronary dentin specimens (3×3mm) were distributed into three groups (n=9), according to surface treatment: HP - 35% hydrogen peroxide (1×4'), DL - 970nm diode laser (1×30"/0,8W/10Hz), HP+DL - 35% HP activated with 970nm diode laser (1×30"/0,8W/10Hz leaving the gel in contact to the surface for 4' after activation). Three Raman spectra from each fragment were obtained to calculate the mean intensity of peaks of inorganic component (a.u.), organic collagen content (a.u.), and the ratio of inorganic/organic content, before and after treatment. Analyses of the samples by confocal laser microscopy were performed to evaluate the surface roughness, percentage of tubules, perimeter and area percentage of tubules, before and after treatment. Data were analyzed by Kruskal-Wallis, Dunn's, and Wilcoxon test (P<0.05). RESULTS: Data analysis showed that HP+DL did not change the inorganic content peaks 8.31 [29.78] or the inorganic/organic ratio 3.37 [14.67] (P>0.05). Similarly, DL did not affect the chemical stability of the dentin surface (P>0.05). However, HP significantly increased inorganic content peaks 10.87 [22.62], as well as the inorganic/organic ratio 6.25 [27.78] (P<0.05). Regarding the morphological alterations, all surface treatments increase tubules exposure; HP treatment significantly increases perimeter and area percentage; and HP+DL increases surface roughness. CONCLUSIONS: Bleaching HP combined with DL offers an improvement in terms of intracoronal dentin surface protection, yielding better maintenance of dentin chemical stability and morphology.

Assuntos