RESUMO
Aim: To evaluate the retention of Y-TZP crowns cemented in aged composite cores ground with burs of different grit sizes. Methods: Sixty composite resin simplified full-crown preparations were scanned, while 60 Y-TZP crowns with occlusal retentions were milled. The composite preparations were stored for 120 days (wet environment-37°C) and randomly distributed into three groups (n=20) according to the type of composite core surface treatment. The groups were defined as: CTRL (control: No treatment), EFB (extra-fine diamond bur [25µm]), and CB (coarse diamond bur [107µm]). The grinding was performed with an adapted surveyor standardizing the speed and pressure of the grinding. The intaglio surfaces on the crowns were air-abraded with silica-coated alumina particles (30 µm) and then a silane was applied. The crowns were cemented with self-adhesive resin cement, thermocycled (12,000 cycles; 5/55°C), stored (120 days) and submitted to a retention test (0.5mm/min). The retentive strength data (MPa) were analyzed using one-way analysis of variance and Tukey test, as well as Weibull analysis. Failures were classified as 50C (above 50% of cement in the crown), 50S (above 50% of cement in the substrate) and COE (composite core cohesive failure). Results: No statistical difference was observed among the retention values (p=0.975). However, a higher Weibull modulus was observed in the CTRL group. The predominant type of failure was 50S (above 50% of cement in the substrate composite). Conclusion: The retention of zirconia crowns was not affected by grinding using diamond burs with different grit sizes (coarse/extra-fine) or when no grinding was performed
Assuntos
Propriedades de Superfície , Zircônio , Colagem Dentária , Retenção em Prótese Dentária , Resinas CompostasRESUMO
Aim: To evaluate the retention of an endodontic titanium postwith a spherical head for removable partial denture or overdentureattachment according to surface treatment type. Methods: Sixtyhealthy single-rooted teeth, sectioned at the enamel/cementumjunction, were treated endodontically and steadily fixed in theembedding acrylic resin. The titanium posts were subdivided intofour groups: control, no surface treatment (Ctrl); posts with macroretentivegrooves (MR); air abrasion of the post surface (AB); andposts with macro-retentive grooves and air abrasion of the postsurface (MR+AB). The posts were luted in the root canal usingself-adhesive dual resin cement. Pull-out testing was performedusing a universal testing machine until complete detachment wasachieved. After pull-out testing, the metallic posts were examinedunder an optical microscope and the failures were classifiedbased on the cement distribution pattern on the extracted posts:0, no cement left on the post (cement/post failure); 1, postsurface partially covered by adhered cement (post/cement anddentin/cement mixed failure); 2, post surface completely coveredby cement (dentin/cement failure). The retention data wereanalyzed by one-way ANOVA, BonferroniDunn test (p<0.05)and Weibull analysis. Results: AB showed the highest retentionvalue (485.37±68.36), followed by MR+AB (355.80±118.47), MR(224.63±42.54) and Ctrl (113.12 ± 51.32). AB and MR showedthe highest Weibull moduli. Conclusions: The data indicatedthat air abrasion alone could significantly increase the retentionof titanium posts/attachments for use with overdentures orremovable partial denture
Assuntos
Propriedades de Superfície , Retenção de Dentadura , Cimentação , Abrasão Dental por Ar , Titânio , Prótese Parcial RemovívelRESUMO
PURPOSE: To evaluate the influence of particle and air-abrasion on the surface characterization and shear bond strength (SBS) of a Y-TZP ceramic with a resin cement. MATERIALS AND METHODS: Y-TZP specimens were air-abraded with 50 µm alumina particles; 120 µm alumina particles; 30 µm silica-coated alumina particles (Rocatec Soft); 110 µm silica-coated alumina particles (Rocatec Plus). Air-abrasion was performed before (BS); after (AS); before and after (BAS) zirconia sintering. Surface characterization included roughness (n = 10), wettability (n = 10), morphology (n = 2), and elemental composition (n = 2). For SBS (n = 11), composite resin discs were bonded to the air-abraded and silane-treated zirconia surface, with the resin cement RelyX ARC. Failure mode was determined. Roughness, wettability, and SBS data were analyzed by two-way ANOVA with pairwise interaction and Tukey's test (α = 0.05). RESULTS: Air-abrasion performed with coarser particles at BS and BAS moments provided the highest roughness values, while the lowest roughness values were observed with particles combined with AS moment (p < 0.01). Rocatec Plus provided lower contact angle than the 120 µm alumina particles (p = 0.013), and BAS exhibited lower contact angle than BS (p = 0.002). The combinations 120 µm/BS and the silica-coated alumina particles/AS and /BAS showed the highest SBS (p < 0.05). The combination of each particle/BAS was statistically similar to the same particle/AS. Failure mode was 100% adhesive for all groups. The interaction particle size/air-abrasion moment determined the morphological pattern. Silicon was observed only in the Rocatec groups. CONCLUSIONS: Roughness was influenced by the particle size and was higher when the zirconia was air-abraded in its green stage. The particle composition played an important role in the wettability and both studied air-abrasion moments provided similar wettability than the one in which air-abrasion is usually performed. The highest SBS values were observed in the three moments, by using certain particles for each moment.
Assuntos
Abrasão Dental por Ar/métodos , Cimentos de Resina/química , Resistência ao Cisalhamento , Ítrio/química , Zircônio/química , Óxido de Alumínio/química , Análise de Variância , Bis-Fenol A-Glicidil Metacrilato , Resinas Compostas/química , Colagem Dentária , Cimentos Dentários , Materiais Dentários/química , Falha de Restauração Dentária , Análise do Estresse Dentário , Humanos , Teste de Materiais , Microscopia Eletrônica de Varredura , Tamanho da Partícula , Polietilenoglicóis , Ácidos Polimetacrílicos , Dióxido de Silício/química , Propriedades de Superfície , MolhabilidadeRESUMO
Aim: This study evaluated the fracture load and pattern failure of different prefabricated glass fiber posts (GFPs) of the same diameter. Methods: Seventy-eight (n=13 for six groups) GFPs of 1.6 mm coronal diameter of different brands were evaluated Exacto (Angelus), Power Post (BM4), White Post DC (FGM), HiRem (Overfibers), MAQ (Maquira), and SD (Supordont). The posts were subjected to fracture load testing (45° of inclination and 1 mm/min until fracture). Each factor (load (N) and shear stress (MPa)) was analyzed separately using one-way ANOVA followed by the Tukey test (α=0.05). Results: The type of failure was evaluated on a stereomicroscope (×10). The Power Post samples presented higher values of fracture load (p<0.001) followed by Maquira fiber post, White Post , HiRem, Superpost, and the Exacto posts. The failure pattern observed was intralaminar mode II in-plane shear, such as a failure occur parallel to fibers. Conclusion: Despite the same diameter of GFPs, the fracture load and shear resistance were brand-dependent
Assuntos
Estresse Mecânico , Teste de Materiais , Resistência ao Cisalhamento , VidroRESUMO
INTRODUCTION: This study evaluated the effects of endodontic treatment and retreatment on the fatigue failure load, numbers of cycles for failure, and survival rates of canine teeth. METHODS: Sixty extracted canine teeth, each with a single root canal, were selected and randomly divided into 4 groups (n = 15): untreated, teeth without endodontic intervention; prepared, teeth subjected only to rotary instrumentation; filled, teeth receiving complete endodontic treatment; and retreated, teeth retreated endodontically. After the different endodontic interventions, the specimens were subjected to fatigue testing by the stepwise method: 200 N (× 5000 load pulses), 300 N, 400 N, 500 N, 600 N, 800 N, and 900 N at a maximum of 30,000 load pulses each or the occurrence of fracture. Data from load to failure and numbers of cycles for fracture were recorded and subjected to Kaplan-Meier and Log Rank tests (P < .05), in addition to Weibull analysis. The fractures of the specimens were classified as repairable or catastrophic. RESULTS: The retreated, filled, and untreated groups presented statistically significantly higher fatigue failure loads and numbers of cycles for failure than did the prepared group. Weibull analysis showed no statistically significant difference among the treatments for characteristic load to failure and characteristic number of cycles for failure, although, for number of cycles, a higher Weibull modulus was observed in filled and retreated conditions. The predominant mode of failure was catastrophic. CONCLUSION: Teeth subjected to complete endodontic treatment and retreatment behaved similarly in terms of fatigue failure load and number of cycles to failure when compared with untreated teeth.
Assuntos
Dente Canino , Análise do Estresse Dentário , Tratamento do Canal Radicular , Humanos , Técnicas In Vitro , Distribuição Aleatória , Retratamento , Falha de TratamentoRESUMO
Objective: This study aimed to evaluate the fracture load and displacement of roots restored with posts of different elastic modulus. Material and method: Thirty-six replicas of epoxy resin mixed with glass microfibers were made from an endodontically-treated human premolar root prepared to a length of 12 mm with a custom drill, leaving the apical 4 mm unprepared. Replicas were randomly restored with (n = 12): FP-LM (fiber post with low elastic modulus- 50 GPa), FP-HM (fiber post with high elastic modulus - 67 GPa) and MP (metallic post - 208 GPa), using self-curing adhesive and dual resin cement. Cores were built up with composite resin and metallic crowns were cemented in all the roots with self-adhesive resin cement with self-curing mode. Specimens were subjected to a fracture load test (45° inclination/0.5 mm/min) and displacement was registered at 100 N. Result: One-way ANOVA showed that elastic modulus of the post did not affect the fracture load means (p = 0.203) (FP-LM: 237.4 ± 65.11 N; FP-HM: 236.7 ± 92.85 N; MP: 295.8 ± 108.7 N) but was statistically significant for the displacement (p < 0.00): Tukey's test showed that FP-LM displacement mean (0.81 ± 0.15 mm) was significantly higher than those for FP-HM (0.46 ± 0.26 mm; p = 0.00) and MP (0.62 ± 0.07 mm; p = 0.04). Conclusion: Posts with different elastic modulus exhibit similar fracture loads, but a lower displacement is achieved when fiber posts with a high elastic modulus and metallic posts are used.
Objetivo: Este trabalho avaliou a carga para fratura e deslocamento de raízes restauradas com pinos de diferentes módulos de elasticidade. Material e método: Trinta e seis réplicas de microfibras de vidro embutidas em resina epóxi foram fabricadas a partir de uma raiz de um pré-molar tratado endodonticamente preparado em 12 mm de comprimento com brocas customizadas, deixando 4 mm apicais sem preparo. As raízes foram randomicamente restauradas com (n = 12): FP-LM (pino de fibra com um baixo módulo de elasticidade - 50 GPa), FP-HM (pino de fibra com um alto módulo de elasticidade - 67 GPa) e MP (pinos metálicos - 208 GPa), usando adesivo autopolimerizável e cimento resinoso dual. Núcleos foram confeccionados com resina composta e coroas metálicas foram cimentadas em todas as raízes com cimento resinoso autoadesivo com modo de polimerização químico. Os espécimes foram submetidos ao teste de fratura em 45° (inclinação de 45° / 0,5 mm/min) e o deslocamento foi registrado aos 100 N. Resultado: Anova 1 fator mostrou que o módulo de elasticidade dos retentores não afetou as médias de fratura (p = 0,203) (FP-LM: 237,4 ± 65,11 N; FP-HM: 236,7 ± 92,85 N; MP: 295,8 ± 108,7 N) mas foi estatisticamente significante para o deslocamento (p < 0,00): o teste de Tukey mostrou que a média de deslocamento do grupo FP-LM (0,81 ± 0,15 mm) foi significativamente maior do que o grupo FP-HM (0,46 ± 0,26 mm; p = 0,00) e MP (0,62 ± 0,07 mm; p = 0,47). Conclusão: Pinos com diferentes módulos de elasticidade mostram resistência similar, porém um menor deslocamento é obtido quando pinos de fibra com alto módulo de elasticidade (FP-HM/MP) são usados.
Assuntos
Raiz Dentária , Dente Pré-Molar , Técnica para Retentor Intrarradicular , Prótese Dentária , Resinas Compostas , Cimentos de Resina , Força Compressiva , Coroas , Pinos Dentários , Análise de Variância , Materiais Dentários , Resinas EpóxiRESUMO
STATEMENT OF PROBLEM: Because zirconia is a glass-free material, alternative surface treatments such as airborne-particle abrasion or silica coating should be used for long-term bonding. However, these surface treatments in combination with different bonding agents and luting cements have not yet been studied. PURPOSE: The purpose of the study was to evaluate the effect of surface treatments on the shear bond strength (SBS) of luting cements to Y-TZP ceramic. MATERIAL AND METHODS: Zirconia disks (N=240) were airborne-particle abraded with the following particles (n=48): 50 µm Al2O3; 120 µm Al2O3; 30 µm silica-coated Al2O3 (Rocatec Soft); 120 µm Al2O3+110 µm silica-coated Al2O3 (Rocatec Plus); and Rocatec Plus. After silanization of the zirconia surface, composite resin disks were bonded with (n=12) RelyX Luting 2; RelyX ARC; RelyX U100; and Panavia F. The bonded specimens were thermocycled (10 000 cycles) and tested for SBS. Failure mode was determined with a stereomicroscope (×20). The morphology and elemental composition of airborne-particle abraded surfaces were evaluated with scanning electron microscopy (×500) and energy-dispersive x-ray spectroscopy (×50). RESULTS: Surface treatments, cements, and their interaction were significant (P<.001). For RelyX ARC, Rocatec Soft and Rocatec Plus provided the highest SBS. In general, surface treatments did not influence the SBS of RelyX U100 and Panavia F. Regardless of the cement, no significant difference was found between 50 µm and 120 µm Al2O3 particles, between Rocatec Soft and Rocatec Plus, or between Rocatec Plus and 120 µm Al2O3 particles+Rocatec Plus. All groups showed adhesive failures. Different particle sizes provided differences in morphological patterns. The elemental composition comprised Al and Al/Si for alumina and silica-abraded zirconia. CONCLUSIONS: Particle size did not influence the SBS of the groups abraded exclusively with alumina or silica-coated particles. RelyX ARC was more surface-treatment dependent than RelyX U100 or Panavia F.
Assuntos
Cerâmica/química , Colagem Dentária , Corrosão Dentária/métodos , Materiais Dentários/química , Cimentos de Resina/química , Ítrio/química , Zircônio/química , Óxido de Alumínio/química , Bis-Fenol A-Glicidil Metacrilato/química , Materiais Revestidos Biocompatíveis/química , Resinas Compostas/química , Análise do Estresse Dentário/instrumentação , Cimentos de Ionômeros de Vidro/química , Temperatura Alta , Humanos , Teste de Materiais , Microscopia Eletrônica de Varredura , Tamanho da Partícula , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Resistência ao Cisalhamento , Silanos/química , Dióxido de Silício/química , Espectrometria por Raios X , Estresse Mecânico , Propriedades de SuperfícieRESUMO
OBJECTIVE: To evaluate the impact of the type of root canal preparation, intraradicular post and mechanical cycling on the fracture strength of roots. MATERIAL AND METHODS: eighty human single rooted teeth were divided into 8 groups according to the instruments used for root canal preparation (manual or rotary instruments), the type of intraradicular post (fiber posts- FRC and cast post and core- CPC) and the use of mechanical cycling (MC) as follows: Manual and FRC; Manual, FRC and MC; Manual and CPC; Manual, CPC and MC; Rotary and FRC; Rotary, FRC and MC; Rotary and CPC; Rotary, CPC and MC. The filling was performed by lateral compactation. All root canals were prepared for a post with a 10 mm length, using the custom #2 bur of the glass fiber post system. For mechanical cycling, the protocol was applied as follows: an angle of incidence of 45°, 37°C, 88 N, 4 Hz, 2 million pulses. All groups were submitted to fracture strength test in a 45° device with 1 mm/ min cross-head speed until failure occurred. RESULTS: The 3-way ANOVA showed that the root canal preparation strategy (p<0.03) and post type (p<0.0001) affected the fracture strength results, while mechanical cycling (p=0.29) did not. CONCLUSION: The root canal preparation strategy only influenced the root fracture strength when restoring with a fiber post and mechanical cycling, so it does not seem to be an important factor in this scenario.
Assuntos
Técnica para Retentor Intrarradicular/instrumentação , Preparo de Canal Radicular/instrumentação , Preparo de Canal Radicular/métodos , Fraturas dos Dentes/etiologia , Raiz Dentária/lesões , Análise de Variância , Resinas Compostas/química , Instrumentos Odontológicos , Análise do Estresse Dentário , Dentina/anatomia & histologia , Humanos , Teste de Materiais , Reprodutibilidade dos Testes , Estresse Mecânico , Propriedades de Superfície , Fraturas dos Dentes/fisiopatologia , Raiz Dentária/anatomia & histologiaRESUMO
Objective: To evaluate the impact of the type of root canal preparation, intraradicular post and mechanical cycling on the fracture strength of roots. Material and Methods: eighty human single rooted teeth were divided into 8 groups according to the instruments used for root canal preparation (manual or rotary instruments), the type of intraradicular post (fiber posts- FRC and cast post and core- CPC) and the use of mechanical cycling (MC) as follows: Manual and FRC; Manual, FRC and MC; Manual and CPC; Manual, CPC and MC; Rotary and FRC; Rotary, FRC and MC; Rotary and CPC; Rotary, CPC and MC. The filling was performed by lateral compactation. All root canals were prepared for a post with a 10 mm length, using the custom #2 bur of the glass fiber post system. For mechanical cycling, the protocol was applied as follows: an angle of incidence of 45°, 37°C, 88 N, 4 Hz, 2 million pulses. All groups were submitted to fracture strength test in a 45° device with 1 mm/ min cross-head speed until failure occurred. Results: The 3-way ANOVA showed that the root canal preparation strategy (p<0.03) and post type (p<0.0001) affected the fracture strength results, while mechanical cycling (p=0.29) did not. Conclusion: The root canal preparation strategy only influenced the root fracture strength when restoring with a fiber post and mechanical cycling, so it does not seem to be an important factor in this scenario. .
Assuntos
Humanos , Técnica para Retentor Intrarradicular/instrumentação , Preparo de Canal Radicular/instrumentação , Preparo de Canal Radicular/métodos , Fraturas dos Dentes/etiologia , Raiz Dentária/lesões , Análise de Variância , Resinas Compostas/química , Instrumentos Odontológicos , Análise do Estresse Dentário , Dentina/anatomia & histologia , Teste de Materiais , Reprodutibilidade dos Testes , Estresse Mecânico , Propriedades de Superfície , Fraturas dos Dentes/fisiopatologia , Raiz Dentária/anatomia & histologiaRESUMO
This study sought to evaluate how different post cementation strategies affected the fatigue resistance of bovine teeth restored with glass fiber posts. The canals of 63 single-rooted bovine teeth (each 16 mm in length) were prepared to 9 mm using a preparation drill from a double-tapered fiber post system. Each specimen was embedded in a PVC cylinder using acrylic resin up to 3 mm of the most coronal portion of the specimen and was allocated into one of seven groups (n = 9) based on the strategies for cementation. After cementation, a standard core build-up was made with composite resin. The specimens were stored for seven days and submitted to mechanical cycling (50 N, 8 Hz, 37 degrees C). After fatigue testing, a score was given to each specimen, based on the number of fatigue cycles required to fracture the specimens; the scores were submitted to statistic analysis (Kruskal-Wallis, alpha = 0.05). The strategy for post cementation did not affect the resistance to fatigue (P = 0.8669). Based on the results, the resistance to fatigue does not appear to depend on the post cementation strategy.