RESUMO
Different types of hair were submitted to different milling procedures and their resulting powders were analyzed by scanning electron microscopy (SEM) and laser diffraction (LD). SEM results were qualitative whereas LD results were quantitative and accurately characterized the hair powders through their particle size distribution (PSD). Different types of hair were submitted to an optimized milling conditions and their PSD was quite similar. A good correlation was obtained between PSD results and ketamine concentration in a hair sample analyzed by LC-MS/MS. Hair samples were frozen in liquid nitrogen for 5min and pulverized at 25Hz for 10min, resulting in 61% of particles <104µm and 39% from 104 to 1000µm. Doing so, a 359% increment on ketamine concentration was obtained for an authentic sample extracted after pulverization comparing with the same sample cut in 1mm fragments. When milling time was extended to 25min, >90% of particles were <60µm and an additional increment of 52.4% in ketamine content was obtained. PSD is a key feature on analysis of pulverized hair as it can affect the method recovery and reproducibility. In addition, PSD is an important issue on sample retesting and quality control procedures.