RESUMO
The aim of this study was to evaluate the shear bond strength of resin cement and lithium disilicate ceramic after various surface treatments of the ceramic. Sixty blocks of ceramic (IPS e.max Press, Ivoclar Vivadent) were obtained. After cleaning, they were placed in polyvinyl chloride tubes with acrylic resin. The blocks were divided into six groups (n=10) depending on surface treatment: H/S/A - 10% Hydrofluoric Acid + Silane + Adhesive, H/S -10% Hydrofluoric Acid + Silane, H/S/UA - 10% Hydrofluoric Acid + Silane + Universal Adhesive, H/UA- 10% Hydrofluoric Acid + Universal Adhesive, MBEP/A - Monobond Etch & Prime + Adhesive, and MBEP - Monobond Etch & Prime. The light-cured resin cement (Variolink Esthetic LC, Ivoclar Vivadent) was inserted in a mold placed over the treated area of the ceramics and photocured with an LED for 20 s to produce cylinders (3 mm x 3 mm). The samples were subjected to a shear bond strength test in a universal test machine (Instron 5965) by 0.5 mm/min. ANOVA and Tukey tests showed a statistically significant difference between groups (p<0.05). The results of the shear strength test were H/S/A (9.61±2.50)A, H/S (10.22±3.28)A, H/S/UA (7.39±2.02)ABC, H/UA (4.28±1.32)C, MBEP/A (9.01±1.97)AB, and MBEP (6.18±2.75)BC. The H/S group showed cohesive failures, and the H/UA group was the only one that presented adhesive failures. The conventional treatment with hydrofluoric acid and silane showed the best bond strength. The use of a new ceramic primer associated with adhesive bonding obtained similar results to conventional surface treatment, being a satisfactory alternative to replace the use of hydrofluoric acid.
RESUMO
Objectives: The aim of this study was to evaluate the influence of the color of the resin luting cement in the final shade of minimally invasive porcelain veneers after accelerated artificial aging (AAA). Material and methods: 20 bovine teeth were collected, prepared and divided into two groups. The roots were removed and the buccal surfaces were polished to obtain a flat surface. Porcelain discs (IPS Empress Esthetic) were produced to a standardized shade (ET1) and thickness (0.6mm). The teeth and the veneers surfaces were prepared according to manufacturer recommendations. For group I (n=10), the White-Opaque (WO) base-paste was used and for group II (n=10) the Yellow (Y) base-paste. Each specimen was photocured for 60 s. The specimens were next subjected to AAA. They were submitted to color readings with a spectrophotometer in three moments: after the preparation (only the substrate), after the cementation and polymerization of the veneers and after the AAA. Were obtained values of L*, a* and b* and the total color change was calculated (?E*). Values obtained were subjected to statistical analysis in SPSS 17.0 for Windows with a significance of 0.05. Results: When comparing the cements, the Y cement showed higher ?E*, lower L* and higher b* after AAA than the WO. Conclusion: Both cements could mask the substrate color. With AAA, only the Y shade showed a ?E* clinically unacceptable, becoming more yellow (higher b*) and losing lightness (lower L*).
Objetivos: O objetivo do presente estudo foi avaliar a influência da cor do cimento resinoso na tonalidade final de facetas de porcelana minimamente invasivas, após envelhecimento artificial acelerado (EAA). Material e Métodos: 20 dentes bovinos foram coletados, preparados e divididos em dois grupos. As raízes foram removidas e a face vestibular foi polida para obter uma superfície plana. Discos de porcelana (IPS Empress Esthetic) foram confeccionados na cor ET1 e espessura de 0,6 mm. Os dentes e as superfícies dos discos foram preparados de acordo com as recomendações do fabricante. Para o grupo I (n=10) foi usado o cimento resinoso White-Opaque (WO) pasta-base, e para o grupo II (n-10) utilizou-se o Yellow (Y) pasta-base. Cada espécime foi fotopolimerizado por 60 s. Os espécimes foram então submetidos ao EAA. Eles foram submetidos a leituras de cor com auxílio de um espectro fotômetro em três momentos: após o preparo (apenas o substrato), após a cimentação e polimerização das facetas e após o EAA. Foram obtios valores de L*, a* e b* e o total da variação de cor foi calculado (?E*). Os valores obtidos foram submetidos à análise estatística no SPSS 17.0 para Windows, com nível de significância de 0,05. Resultados: O cimento Y apresentou maior ?E*, menor L* e maior b* após o EAA em comparação com o WO. Conclusão: Ambos os cimentos têm capacidade de mascarar a cor do substrato. Com o EAA, apenas o Y apresentou um valor de ?E* inaceitável clinicamente, se tornando mais amarelo (maior b*) e perdendo luminosidade (menor L*).
RESUMO
Introdução: O estágio atual dos materiais dentários, especificamente os cimentos resinosos e sistemas cerâmicos tem proporcionado uma ampliação do uso das restaurações adesivas estéticas indiretas. Estas têm se destacado pelas excelentes propriedades ópticas, maior facilidade de restabelecer contorno e contatos proximais durante a confecção da restauração no laboratório, diminuição da contração de polimerização e a maior resistência. Objetivo: Apresentar a sequência clínica de execução de uma onlay cerâmica com ênfase na seleção do sistema cerâmico e cimento resinoso. Relato: Paciente J.C.F.A, 16 anos, apresentou-se na Clínica da Faculdade de Odontologia da UFG com extensa restauração de amálgama e fratura da cúspide disto-vestibular no dente 46. A sequência clínica enfatiza a técnica de preparo, polimento do preparo com multiplicador (T2 Revo/Sirona), escolha do sistema cerâmico (sistema IPS Empress Esthetic), técnica de moldagem com duplo fio retrator e silicona de adição e uso do cimento resinoso auto-adesivo (U100, 3M Espe). Resultados: Restauração indireta onlay confeccionada com escolha adequada do sistema cerâmico e correta indicação da técnica com cimento auto-adesivo oferece solução restauradora que equilibra as necessidades funcionais e estéticas nos dentes posteriores.
Introduction: The current status of dental materials, especially resin cements and ceramic systems has provided an expanded use of indirect esthetic restorative. These have been highlighted by the excellent optical properties, the ease restoring contour and proximal contact during the restoration making in laboratory, reduced polymerization contraction and high strength. Objective: To present the clinical sequence of execution of indirect restoration type onlay with emphasis on the selection of ceramic and resin cement systems. Report: JCFA patient, 16 years, presented at UFG School of Clinical Dentistry, with extensive amalgam restoration and cusp fracture on tooth 46. The sequence emphasizes the clinical technique of preparation, polishing with multiplier (T2 Revo / Sirona), choice of ceramic system (IPS Empress Esthetic) impression technique with double wire retractor and addition silicone resin cement and use of self-adhesive (U100, 3M Espe). Results: The indirect ceramic onlay restoration cemented with self-adhesive cement offers restorative solution that balances with functional and esthetic teeth restorations in posterior teeth.
RESUMO
As facetas cerâmicas tem se destacado na Odontologia Estética Contemporânea pela excelente propriedade óptica e biomimética. A sedimentação da longevidade vem associada à previsibilidade do resultado pelas técnicas protocolares de planejamento e execução, favorecendo a relação paciente/ profissional e superando positivamente as expectativas mútuas. Esse artigo tem como objetivo apresentar um caso clínico com ênfase na importância da utilização da pasta de prova previamente à cimentação de facetas cerâmicas, caracterizando como ferramenta fundamental para minimização de erros, definição de previsibilidade do resultado estético e consequente satisfação do paciente. Concluiu-se que o uso das pastas Try-In é uma etapa essencial no processo de reabilitação com facetas cerâmicas.
The Ceramic Venners has excelled greatly in Contemporary Esthetic Dentistry for the excellent optical property and biomimetics. The sedimentation of longevity is associated with predictability of the result by the thecniques of planning and implementing protocol, favoring the patient-professional and positively overcoming mutual expectations. This article aims to present a case report emphasizing the importance of using a folder of evidence prior tocementing ceramic venners, featuring as a fundamental tool tominimize errors, definition of predictability of the aesthetic results and subsequent patient satisfaction. It was concluded that the use offolders Try-In is na essential step in the rehabilitation process with ceramic venners.
RESUMO
As facetas cerâmicas se destacam na Odontologia atual pela longevidade e excelentes propriedades ópticas. Esse artigo tem como objetivo apresentar um caso clínico, incluindo um minucioso planejamento, a importância da inter-relação Periodontia e Dentística e o protocolo reabilitador para realização de laminados cerâmicos para se alcançar sucesso no tratamento e satisfação do paciente.
The porcelain laminates veneers in dentistry today stand for longevity and excellent optical properties. This aim of this paper is to present a clinical case, including a thorough planning, the importance of the interrelationship and Dentistry, Periodontology and rehabilitative protocol for conducting porcelain laminates veneers to achieve treatment success and patient satisfaction.
RESUMO
BACKGROUND: The daily application time for 10 percent carbamide peroxide (CP) typically is between four and eight hours. However, to the authors' knowledge, no investigators in clinical studies have compared different application times; this is the aim of this study. METHODS: The authors recruited 60 patients and categorized each of them into one of four groups. All participants used 10 percent CP in a bleaching tray. The daily application times were 15 minutes, 30 minutes, one hour or eight hours. Participants bleached their teeth for 16 days and those who were not satisfied with the results extended the bleaching time until they were satisfied. Patients recorded their tooth sensitivity on a 0 to 4 scale. The authors measured the shade changes by using a digital spectrophotometer and shade guide. They performed appropriate statistical analysis of the data (α = .05). RESULTS: Participants in the one- and eight-hour groups bleached their teeth for 18 and 16 days, respectively (P > .05), while statistically longer periods were required for participants in the other two groups (P < .001) to be satisfied with the results. Participants' tooth sensitivity ratings were similar for the 15-minute, 30-minute and one-hour application times (P > .05), and they were statistically lower than those for participants in the eight-hour group. CONCLUSIONS: The eight-hour bleaching protocol yielded faster bleaching; however, participants experienced higher sensitivity levels. The one-hour group most closely approached the eight-hour group with regard to bleaching speed, while those in the one-hour group experienced lower sensitivity levels. CLINICAL IMPLICATIONS: In this study, the difference in bleaching speed between the eight- and one-hour application times after 16 days was small, and the results showed less tooth sensitivity for patients in the one-hour group.
Assuntos
Sensibilidade da Dentina/etiologia , Peróxidos/administração & dosagem , Clareadores Dentários/administração & dosagem , Clareamento Dental/métodos , Ureia/análogos & derivados , Adolescente , Adulto , Peróxido de Carbamida , Cor , Feminino , Géis , Humanos , Incisivo/efeitos dos fármacos , Incisivo/patologia , Masculino , Maxila , Medição da Dor , Satisfação do Paciente , Método Simples-Cego , Espectrofotometria , Fatores de Tempo , Clareamento Dental/instrumentação , Descoloração de Dente/tratamento farmacológico , Descoloração de Dente/patologia , Resultado do Tratamento , Ureia/administração & dosagem , Adulto JovemRESUMO
O objetivo deste trabalho foi comparar, in vitro, diferentes técnicas de acabamento de preparos por meio da análise da rugosidade superficial e microscopia eletrônica de varredora (MEV). Cinquenta e seis pré-molares humanos foram divididos em quatro grupos, (n= 10): Grupo I - sem acabamento (grupo controle); Grupo II - ponta diamantada 2135 F e 2135 FF; Grupo III - ponta 2135 acopladas em um contra ângulo multiplicador (Kavo Koncept 1:5) e Grupo IV - ponta CVD cilíndrica 8.2137 (CVDentus- Clorovale) em aparelho de ultra-som (Profi II - Dabi Atlante). Após o acabamento, dez espécimes de cada grupo foram submetidos à leitura rugosimétrica e quatro foram analisados no MEV (Microscopia eletrônica de varredura). Sessenta e quatro micrografias foram analisadas por doze examinadores. Os valores de Ra (média±dp) foram: GI- 1,46±0,2; GII- 0,87±0,3; GIII- 1,6±0,4 e GIV- 1,34±0,2. Após teste de t-Student, observou-se que não houve diferença significativa entre os grupos I (controle), III (multiplicador) e IV (CVD). Entretanto, houve diferença entre o grupo I e II; Grupo II e III; GII e I. Após teste de Mann-Whitney para análise em MEV, observou-se que não houve diferença significativa entre os grupos I (controle), II (ponta diamantada fina e extra-fina) e III (multiplicador). Conclui-se que o grupo que apresentou menor valor de rugosidade (Ra) foi o grupo II, realizado com pontas diamantadas 2135 F e 2135FF montadas em alta rotação. Para análise em MEV, concluiu-se que a superfície produzida pelo grupo IV (CVD) foi a mais rugosa.
The objective of this study was to compare, in vitro, different techniques for finishing preparations of facets indirect through the analysis of surface roughness and electron microscopy sweeper (SEM). Forty human premolars were divided into 4 groups according to the finishing of the cavity preparation for indirect facets: Group I (n = 10) - unfinished (control group), Group II (n = 10) - diamond bur 2135 F and 2135FF, Group III (n = 10)- tip in 2135 engaged in a multiplier (Contra angle multiplier Koncept Kavo 1:5) and Group IV (n = 10) tip cylindrical CVDcat. 8.2137 (CVDentus - Clorovale) in equipment ultrasound (Profi II- Dabi Atlante). The reading was held rugosimetric relief meter Mitutoyo SJ-201. For SEM analysis were prepared 16 teeth were divided into four groups according to the finishing technique described above, with four teeth in each group, totaling 64 images, analyzed by twelve examiners. The values of Ra (mean ± SD) were: GI-1.46 ± 0.2, GII - 0.87 ± 0.3, GIII, 1.6 ± 0.4 and GIV-1.34 ± 0.2 . After test t-test (Figure 1), it was observed that there was no significant difference between groups I (control),III (multiplier) and IV (CVD). However, there was difference between group I and II, Group II and III, GII and I. After the Mann-Whitney test for analysis by SEM, it was observed that there was no significant difference between groups I (control), II (thin diamond point) and III (multiplier). However, there was difference between group I, II, III with group IV (CVD), with p <0.001. It follows that the group with lowest roughness (Ra) (smoother) the group II was performed with diamond burs and 2135 F 2135FF mounted on heavy rotation. For SEM analysis, itwas concluded that surface produced by the group IV (CVD) was the most wrinkled. The values assigned by examiners through the analysis of SEM were low averaging less than 5.0 for all groups.
RESUMO
O propósito desta pesquisa foi avaliar a atratividade e percepção da idade do sorriso por leigos e cirurgiões-dentistas frente ao aumento do comprimento de incisivos superiores em fotografias aproximadas e frontais da face. Foram obtidas fotografas iniciais e finais do sorriso aproximado e da face. Os resultados apresentaram uma diferença estatisticamente signifcativa (P menor ou igual a 0,001) com maior atratividade na fotografia final para leigos e cirurgiões-dentistas. O aumento do comprimento dos incisivos superiores proporcionou sete anos de rejuvenescimento considerando a percepção dos cirurgiões-dentistas, quatro anos para os leigos e um impacto positivo na atratividade entre as fotos iniciais e finais, sendo uma alternativa de tratamento estético para alcançar um sorriso agradável.
The purpose of this study was to evaluate atractiveness and perception of aging on smile by laypersons and dental professionals on close-up and facial photographs. The results show that increasing superior incisors length provides seven years of youthful appearance by dental professionals, four years by laypersons and positive impact on atractiveness between initial and final photographs, providing an alternative treatment that enhances an agreeable smile.