RESUMO

To evaluate the effect of adhesive coats application on the enamel microtensile bond strength (µTBS) of universal adhesives, morphological etching pattern and their chemical interaction with hydroxyapatite (HA). Two universal adhesives were investigated: Scotchbond Universal (SBU, 3 M) and Prime&Bond Universal (PBU, Dentsply). The adhesives were applied in self-etching mode on bovine enamel (n = 8) in one (1L), two (2L) or three coats (3L) and light-cured as per manufacturers' instructions. As controls adhesives were applied to etched enamel (H3PO4-37% phosphoric acid). Bonded specimens were cut into sticks that were stored in deionized water for 24 h or 6 months prior to µTBS testing. Two-way ANOVA and Tukey's test were used for statistical analysis of bond strength with α = 5%. For morphological SEM analysis, enamel surfaces were treated as aforementioned and immediately rinsed with acetone. The intensity of monomer-calcium salt formation from each treatment was measured via infrared spectroscopy (ATR-FTIR). All treatments presented no significant reduction on µTBS after aging (p > 0.05). However, SBU attained highest µTBS when applied in 3L. PBU showed higher µTBS when applied to H3PO4 etched enamel than 1L or 2L. Etching pattern was enhanced by 3L application, particularly with PBU. Chemical interaction was notably higher for SBU than PBU, with no relevant differences with more layers or prior H3PO4-etching. The application of three adhesive coats of universal adhesives in self-etch mode using may enhance the bonding performance and etching pattern to enamel, surpassing the H3PO4-etched enamel bond for SBU. The chemical interaction with calcium from enamel is not affected by number of coats or prior phosphoric acid etching.

RESUMO

Objective: To evaluate the enamel bonding ability and orthodontic adhesive resin degree of conversion using the experimental bracket design. Material and Methods. Thirteen bovine teeth were used in the study. The experimental bracket was modified with a translucent region in the center of its body. After enamel etching, Orthocem orthodontic adhesive (FGM, Joinville, Brazil) was applied on the bracket base for bonding. The groups were divided as follows (n = 10 per group): (1) control (CB) with standard brackets and (2) spot bracket (SB) with experimental brackets featuring a 0.8 mm translucent region at the center using carbide bur. Shear bond strength (SBS) was evaluated after 24 hours in a universal testing machine and adhesive remnant index (ARI). The degree of conversion (DC) was analyzed using Raman spectroscopy (n = 3 per group). Data were then analyzed using Student's t-test and Mann-Whitney statistical methods. Results: The SB group exhibited a higher mean SBS (10.33 MPa) compared to the CB Group (8.77 MPa). However, there was no statistical difference between the groups (p = 0.376). Both SB and CB groups had a mean ARI score of 1. Raman analysis revealed a higher degree of conversion in the SB group (49.3%) compared to the CB group (25.9%). Conclusions: The experimental support showed a higher degree of adhesive conversion, although there was no significant increase in bond strength.

Assuntos

RESUMO

BACKGROUND: Alternatively to conventional treatments, chemo-mechanical caries removal agents can be used. A modality of treatment that has been increasing in dentistry is antimicrobial photodynamic therapy (aPDT). Bixa orellana is being researched for application in aPDT. This protocol aims to determine the effectiveness of aPDT with Bixa orellana extract in deep caries lesions. METHODS: A total of 160 teeth with deep occlusal dental caries will be selected and divided into 4 groups: G1 - control group (Caries removal with a low-speed drill); G2 - Partial Caries Removal with Papacarie™ (Fórmula e Ação, São Paulo, SP, Brazil); G3 - Partial Caries Removal with Papacarie™ and application Bixa orellana extract (20%) (Fórmula e Ação, São Paulo, SP, Brazil); G4 - Partial Caries Removal with Papacarie™ and application Bixa orellana extract (20%) with LED (Valo Cordless Ultradent®, South Jordan, UT, USA) (aPDT). After treatment, all the teeth will be restored with glass ionomer cement and followed up clinically and radiographically, with evaluations at immediately, 1 week, and 1, 3, 6, and 12 months. Dentin samples before and after treatment will be analyzed microbiologically. The efficacy of treatments will be assessed with microbiological (colony-forming units, before and after carious tissue removal), radiographic (integrity of the periapical area and eventual changes in the radiolucent zones), and clinical examinations (retention of the restorative material in the cavity and occurrence of secondary caries), as well as with the time required for the procedures and the need for anesthesia during the procedures. In case data distribution is normal, analysis of variance (ANOVA) will be used for both the dependent and independent variables. In case the data distribution is not normal, the Friedman test will be used for the dependent variables. For independent variables, the Kruskal-Wallis test will be used. DISCUSSION: Procedures using aPDT have been developed for the treatment of dental caries, but there are few controlled clinical trials in the literature confirming its efficacy. TRIAL REGISTRATION: This protocol is registered at ClinicalTrials.gov under the number NCT05236205 and it was first posted on 01/21/2022 and last updated on 05/10/2022.

Assuntos

RESUMO

The aim of this study was to evaluate the fatigue behavior of strength-graded zirconia polycrystals used as monolithic three-unit implant-supported prosthesis; complementarily, crystalline phase and micromorphology were also assessed. Fixed prostheses with 3 elements supported by 2 implants were confectioned, as follows: Group 3Y/5Y - monolithic structures of a graded 3Y-TZP/5Y-TZP zirconia (IPS e.max® ZirCAD PRIME); Group 4Y/5Y - monolithic structures of a graded 4Y-TZP/5Y-TZP zirconia (IPS e.max® ZirCAD MT Multi); Group Bilayer - framework of a 3Y-TZP zirconia (Zenostar T) veneered with porcelain (IPS e.max Ceram). The samples were tested for fatigue performance with step-stress analysis. The fatigue failure load (FFL), the number of cycles required until failure (CFF), and the survival rates in each cycle were recorded. The Weibull module was calculated and the fractography analyzed. The crystalline structural content via Micro-Raman spectroscopy and the crystalline grain size via Scanning Electron microscopy were also assessed for graded structures. Group 3Y/5Y showed the highest FFL, CFF, probability of survival, and reliability (based on Weibull modulus). Group 4Y/5Y showed significantly superior FFL and probability of survival than group bilayer. Fractographic analysis revealed catastrophic flaws in the monolithic structure and cohesive fracture of porcelain in bilayer prostheses, all originating from the occlusal contact point. The graded zirconia presented small grain size (≤0.61 µm), with the smallest values at the cervical region. The main composition of graded zirconia was of grains at tetragonal phase. The strength-graded monolithic zirconia, especially the 3Y-TZP/5Y-TZP, showed to be promising for use as monolithic three-unit implant-supported prosthesis.

Assuntos

RESUMO

Objective: To evaluate different concentrations of solvents (tetrahydrofuran (THF) and dimethyl sulfoxide (DMSO) and monomers on the degree of conversion, microtensile bond strength, and mechanical properties of experimental resin infiltrants. Materials and Methods: Resin infiltrants were formulated and divided into eleven groups: (1) Icon, (2) 75% TEGDMA (T) +25% UDMA (U), (3) T +25% BIS-EMA (B), (4) T + U +0.5%DMSO, (5) T + U +5% DMSO, (6) T + U +0.5% THF, (7) T + U +5% THF, (8) T + B +0.5% DMSO, (9) T + B +5% DMSO, (10) T + B +0.5% THF, and (11) T + B +5% THF. One hundred and ten bovine mandibular incisors were sectioned, treated, and destined to the degree of conversion, tensile cohesive strength, microtensile bond strength, flexural strength, and elastic modulus. Data were submitted to one-way ANOVA and Tukey's test (α = 0.05). Results: The degree of conversion was lowest for T + B +5%THF (41.9%) and highest for T + U +5%THF (62.1%). In flexural strength and E-modulus, the T + B (96.5 MPa and 0.49 GPa) obtained the highest values and the lowest for T + U +5% DMSO (18.5 MPa and 9.7 GPa). Icon showed the highest bond strength (19.3 MPa) and cohesive strength (62.2 MPa), while T + U +5%DMSO (9.7 MPa) and T + B +5% DMSO (9.8 MPa) the lowest values and T + B +0.5% DMSO (12.3 MPa) the lowest cohesive strength. Conclusions: The addition of lower concentrations of DMSO or THF (0.5%) did not impair bond strength or significantly affect monomer conversion, but reduced the mechanical properties of resin infiltration.

Assuntos

RESUMO

The study investigated allogenic pulp transplantation as an innovative method of regenerative endodontic therapy. Three patients were selected for the endodontic treatment of single-root teeth, who also had a son/daughter with deciduous teeth or third molars scheduled for extraction. Receptor teeth were endodontically instrumented and irrigated using a tri-antibiotic solution. During the transplant procedures, the teeth from the son/daughter were extracted, sectioned, and the pulp was carefully removed. The harvested pulp from the donor was inserted into the root canal of the host tooth (father/mother), followed by direct pulp capping and resin composite restoration. The teeth were followed-up with for 2 years and were surveyed with computed tomography, the electric pulp vitality test, and Doppler ultrasound examination. At the 6-month follow-up, positive pulp vitality and the formation of periapical lesions were verified in cases 1 and 2. Case 3 showed remarkable periapical radiolucency before transplantation, but after 1 year, such lesions disappeared and there was positive vitality. All teeth were revascularized as determined by Doppler imaging after 2 years with no signs of endodontic/periodontal radiolucency. In conclusion, although this was a case series with only three patients and four teeth treated, it is possible to suppose that this allogenic pulp transplantation protocol could represent a potential strategy for pulp revitalization in specific endodontic cases.

RESUMO

OBJECTIVES: The aim of this study was to evaluate the influence on MMP inhibition, dentin adhesion and physicochemical properties of an adhesive system incorporated with polymerizable collagen crosslinker monomer derived from cardanol. METHODS: The intermediary cardanol epoxy (CNE) was synthesized through cardanol epoxidation, followed by synthesis of cardanol methacrylate through methacrylic acid solvent-free esterification. Zymographic analysis was performed to evaluate the substances' ability to inhibit gelatinolytic enzymes. Collagen crosslinkers were added into adhesives systems according to the following groups: Ybond Universal® (Control), Ybond® + 2 % proanthocyanidin (PAC), Ybond® + 2 % unsaturated cardanol (Cardanol) and Ybond® + 2 % cardanol methacrylate (CNMA). Degree of conversion (DC) of the adhesives was assessed by FT-IR. Disk-shaped specimens were prepared for water sorption (WS) and solubility (SL) tests. Human third molars were sectioned to expose medium dentin and restored according to the different adhesives used (n = 5). Then, the specimens were cut into 1 mm2 sticks to evaluate, after 24 h and 6-month aging, microtensile bond strength (µTBS) and nanoleakage by scanning electron microscopy. Data were analysed with ANOVA and Tukey's post-test (α = 0.05). RESULTS: CNMA and PAC completely inhibited all forms of gelatinolytic enzymes. Cardanol achieved a significantly lowest DC, while the other groups did not differ from each other (p > 0.05). PAC achieved significantly higher water sorption, while CNMA solubility was significantly lower when compared to the other adhesives (p < 0.05). PAC provided a statistically higher 24 h and 6-month aging bond strength. Intermediary similar µTBS were presented by control and CNMA (p = 0.108). All adhesives applied attained significantly reduced bond strength after aging (p < 0.05). Interfaces created using CNMA were almost devoid of silver deposits initially, however all groups showed large amounts of silver deposits on resin-dentin interface subjected to water aging. SIGNIFICANCE: Although CNMA was effective in inhibiting gelatinolytic enzymes, when incorporated into a universal adhesive it could not promote less degradation of the adhesive interface after water aging. Since it is a hydrophobic monomer, CNMA did not interact well with dentin collagen, however it reduced the solubility of the adhesive system besides not interfering in its polymerization.

Assuntos

RESUMO

The aim of the study was to evaluate how the association of solvents (tetrahydrofuran [THF], dimethyl sulfoxide [DMSO], ethanol [ET] or acetone [ACT]) with experimental dental adhesives affects selected properties of experimental dental adhesives and dentin bond durability. Six adhesive combinations were prepared containing: 30 % ET, 30 % ACT, 30 % THF, 28 % ET + 2 % DMSO (ET+DMSO), 15 % ethanol + 15 % THF (ET+THF), or 28 % THF + 2 % DMSO (THF+DMSO). Thirty-six molars (n = 6) were cut to expose the coronary dentin, and were randomly divided according to the adhesives. They were restored, and then cut into resindentin sticks (1 mm²), and stored in distilled water for 24 h or 6 months, until conducting the microtensile bond strength and nanoleakage tests. Other experiments performed with adhesives included viscosity assessment using a rheometer, and degree of conversion using Fourier-transform infrared spectroscopy (FTIR). The data were analyzed statistically using two-way ANOVA and Tukey's test (p < 0.05). The adhesive formulated exclusively with THF showed the highest viscosity, followed by ET+THF, which obtained the highest degree of conversion compared to ET, and THF alone. ET+DMSO obtained the highest 24-h and aged bond strengths (p < 0.05). ET+THF increased the nanoleakage slightly after 6 months, but attained the only gap-free adhesive interface among all the groups. The combination of alternative solvents, particularly THF, with conventional ones (ET) has improved chemical properties, and the dentin bonding of experimental simplified adhesives.

Assuntos

RESUMO

This study aimed at evaluating the influence of glass-fiber post (GFP) relining with composites of different opacities on resin cement layer thickness (CLT), bond strength (BS) to root dentin, and resin cement degree of conversion (DC%). Standardized roots of 52 bovine incisors had their canals prepared and were distributed into 4 groups (n = 10 for CLT and BS; n = 3 for DC%) according to the post used: WP3 (Control)-Whitepost DC3; groups DE, EN and TR-Whitepost DC0.5 relined, respectively, with dentin, enamel, and translucent shade composites. After cementation, specimens were sectioned into six 1.0 mm-thick discs that were submitted to push-out BS test. CLT and failure pattern were evaluated using a stereomicroscope and DC% by micro-Raman spectroscopy. Data were analyzed by two-way ANOVA and Tukey test (α = 0.05). The control group showed greater CLT than all relined groups (p < 0.05), which did not differ from each other (p > 0.05). Groups relined with low opacity composites (TR; EN) showed the highest BS and DC% means (p < 0.05). BS was not different among root thirds (p > 0.05), while DC% decreased from cervical to apical third (p < 0.05). Adhesive failures between cement and dentin were predominant, except for group DE with frequent mixed failures. It could be concluded that composite opacity did not influence CLT, which was thinner when GFP were relined and that relining GFP with lower opacity composites led to higher BS and DC%.

Assuntos

RESUMO

OBJECTIVE: To evaluate the influence of shades of a multilayered zirconia on light transmission, resin cement degree of conversion, and shear bond strength of resin cement. MATERIALS AND METHODS: The light transmission through opaque (OPQ) and translucent (TNS) regions of Katana UTML zirconia (Kuraray Noritake Dental) were evaluated for using a spectroradiometer (n = 5). Degree of conversion of dual-cure resin cement (Panavia V5, Kuraray Noritake Dental) was measured after light-activation through OPQ or TNS regions and direct exposure. Composition of the zirconia was analyzed with energy dispersive x-ray spectroscopy (EDS). Shear bond strength (SBS) was evaluated on the OPQ and TNS regions after 24 h and 1 year from specimen preparation (n = 15). RESULTS: The OPQ region produced higher irradiance loss (95.1%) than TNS one (92.9%), and lower degree of conversion (52.4%) than TNS (71.2%) at 24 h post-light activation. EDS analysis did not show differences on the microstructure of the OPQ and TNS regions. There were no significant differences on the SBS between zirconia regions. For both zirconia regions, a significant reduction on the SBS occurred after aging, being 31.7% for OPQ and 38% for TNS. CONCLUSION: Both OPQ and TNS regions affected the light transmission through the multilayered zirconia. The OPQ region yielded the highest light attenuation and the lowest degree of conversion of resin cement. Different regions of the zirconia did not influence the SBS. Clinical significance Although opaque and translucent regions of the multilayered zirconia reduced the light transmission from LED curing unit and the degree of conversion of resin cement, the regions did not affect the resin cement adhesion.

Assuntos