RESUMO
Magnetic iron oxide nanoparticles (MNPs) have been prepared and stabilized with three organic acids (tartaric, malic and ascorbic) in order to obtain biocompatible and water dispersible MNPs with potential to bind specifically to tumoral cancer cells. An in deep characterization was performed aiming to verify the presence and effect of the coating and stabilizer on MNPs surface. Besides the mechanisms followed by the different acids to bind MNPs were elucidated and used to justify the differences in the physicochemical properties of each formulation. Data related to characterization revealed that MNPs coated with ascorbic acid (MNPs-AA) resulted the most suitable in terms of their size, surface charge and stability along the time. Besides, ascorbic acid may be recognized by GLUTs receptors that are overexpressed in several kinds of tumoral cells. Therefore, MNPs-AA was selected to explore its performance in both MRI and in vitro assays using human colon cancer cells HCT 116. MRI experiments were performed in clinical equipment using a series of aqueous dispersions of MNPs-AA that were evaluated as T2 contrast agent. The T2- weighted images obtained as well as the calculated r2, indicated that MNPs-AA could act as efficient T2 contrast agent for MRI. Regarding in vitro assays, MNPs-AA did not alter the cellular function neither exert cytotoxicity using the three explored doses. The internalization of the nanoparticles on the cellular structure was confirmed quanti and qualitatively using atomic absorption spectroscopy and Prussian blue techniques respectively. From these results, it emerges that ascorbic acid coated-magnetite nanoparticles may be used as alternative contrast agent to avoid or minimize some toxicological issues related to the widely used gadolinium.
Assuntos
Meios de Contraste/química , Compostos Férricos/química , Imageamento por Ressonância Magnética , Nanopartículas de Magnetita/química , Neoplasias/diagnóstico por imagem , Ácido Ascórbico/química , Humanos , Tamanho da Partícula , Propriedades de SuperfícieRESUMO
Magnetic nanoparticles have attracted much interest due to their broad applications in biomedicine and pollutant remediation. In this work, the optical, magnetic, and structural characteristics of colloids produced by ultrashort pulsed laser ablation of a solid Fe target were studied in four different media: HPLC water, an aqueous solution of trisodium citrate, acetone, and ethanol. Optical extinction spectroscopy revealed an absorption band in the UV region for all, in contrast to the results obtained with nanosecond lasers. Micro-Raman spectroscopy showed that the samples are heterogeneous in their composition, with hematite, maghemite, and magnetite nanoparticles in all four solvents. Similar results were obtained by electron diffraction, which also found α-Fe. Magnetic properties were studied by vibrating-sample magnetometry, and showed nanoparticles in the superparamagnetic state. Under certain experimental conditions, submicrometer-sized iron oxide nanoparticles agglomerate into fractal patterns that show self-similar properties. Self-assembled annular structures on the nanometer scale were also observed and are reported for the first time.