RESUMO
In this work, a comparison was made between the synthesis of niobium-based materials (Nb2O5), both in terms of material characterization and catalytic performance. The methods used were chemical mixtures: modified sol-gel and Pechini. The materials were calcined at different temperatures (753, 873 and 993K) and characterized by the following techniques: photoacousticspectroscopy (PAS), zero charge point (pHPZC), scanning electron microscopy (SEM/EDS), thermogravimetric analysis (TGA/DTG) and X-ray diffraction (XRD). The photocatalytic process was carried out to evaluate the degradation of 2,4-dichlorophenoxyacetic acid (2,4-D) under UV radiation (250 W mercury vapor lamp) and different experimental conditions. In addition, to better understand the influence of parameters such as pH, catalyst concentration (0.2, 0.5 and 0.8 g L-1) and calcination temperature, a Design of Experiments (DoE) was used. The results indicated that despite having similar structures and phases in the XRD analysis, the morphology presents two distinct surfaces, due to the preparation method. Differences in the synthesis method affected the catalytic activity in the parameters studied. Although the zero charge point values are close (6.18-6.36), we observed differences in the band gap depending on the calcination temperature. In the optimal condition studied, the catalyst prepared by the sol-gel method obtained the best results.
Assuntos
Herbicidas , Nióbio/química , Raios Ultravioleta , Microscopia Eletrônica de Varredura , Ácido 2,4-DiclorofenoxiacéticoRESUMO
This study describes the experimental design and optimization of application TiO2 catalysts doped with 0.5, 1, 1.5, 2.0% of Fe. The catalysts were prepared using the impregnation method applied in Paraquat herbicide degradation. The catalysts were characterized by the following techniques: specific surface area and volume, mean pore diameter (BET method), scanning electron microscopy and photoacoustic spectroscopy. The characterization presented results indicating that both calcination temperature and the increase nominal metallic load affected by the structure of catalysts, changing the textural properties, as well as the band gap. The catalyst that presented the best herbicide removal percentage was TiO2 calcined at 773 K with removal of 90.2%. However, according to the experimental design and optimization, both variables (calcination temperature and Fe percentage) are significant in the process. In addition, a positive effect was found in the interaction between the two variables. The values show that a third order kinetic model better described the Paraquat photocatalytic degradation.