RESUMO

This study aimed at evaluating the influence of glass-fiber post (GFP) relining with composites of different opacities on resin cement layer thickness (CLT), bond strength (BS) to root dentin, and resin cement degree of conversion (DC%). Standardized roots of 52 bovine incisors had their canals prepared and were distributed into 4 groups (n = 10 for CLT and BS; n = 3 for DC%) according to the post used: WP3 (Control)-Whitepost DC3; groups DE, EN and TR-Whitepost DC0.5 relined, respectively, with dentin, enamel, and translucent shade composites. After cementation, specimens were sectioned into six 1.0 mm-thick discs that were submitted to push-out BS test. CLT and failure pattern were evaluated using a stereomicroscope and DC% by micro-Raman spectroscopy. Data were analyzed by two-way ANOVA and Tukey test (α = 0.05). The control group showed greater CLT than all relined groups (p < 0.05), which did not differ from each other (p > 0.05). Groups relined with low opacity composites (TR; EN) showed the highest BS and DC% means (p < 0.05). BS was not different among root thirds (p > 0.05), while DC% decreased from cervical to apical third (p < 0.05). Adhesive failures between cement and dentin were predominant, except for group DE with frequent mixed failures. It could be concluded that composite opacity did not influence CLT, which was thinner when GFP were relined and that relining GFP with lower opacity composites led to higher BS and DC%.

Assuntos

RESUMO

This study aimed at evaluating the use of biological dentin post (BDP), achieved by milling bovine root, through the analyses of mechanical and optical properties. BDPs were compared to a glass fiber post (GFP) in the following tests (n = 10): a) elastic modulus (E) and flexural resistance (σ) by three point bending test; b) fracture resistance (FR) by compressive load at 45° and failure pattern; c) light transmitting (LT) ability and their influence on the resin cement's degree of conversion (DC%); d) bond strength (BS) by push-out test and failure pattern. Bovine teeth were decoronated and root length was standardized at 14 mm. The canals were prepared and irrigated with 2.5% NaOCl. GFP's surface was conditioned by 1 min immersion in 24% H2O2 solution before silanization. After root embedment, the root canal walls and the BDP's surface were hybridized (H3PO4 37% + self-cured adhesive) for FR and DC% analyses. Posts were fixed into the root canals using a conventional dual resin cement. For BS test, both posts were luted using the conventional and the self-adhesive cementation. A universal testing machine (EMIC DL2000; 1 mm/min) was employed for the mechanical tests (E, σ, FR and BS). For the LT analysis, opaque polyethylene discs were transfixed by the posts, leaving 10 mm of the posts' apical section for measurements. Posts' cervical portion was irradiated (800 mW/cm2) and a spectrometer recorded the number of photons transmitted to previously chosen lateral post regions and at the apical tip. The resin cement DC% was evaluated in several sites of the cement film. After normal distribution were checked (Shapiro-Wilk test), data were submitted to ANOVA (5%) and Scheffe post-hoc test (5%). Results showed that: a) E: BDP > GFP; b) σ: BDP < GFP; c) RF: BDP < GFP; d) LT could not be observed for BDP. For GFPs, the greatest number of photons was observed at the post apical tip. An exponential decay was observed from the cervical to the apical post region; e) resin cement DC% was statistically similar at all points of measurements for both posts; and, f) BS: BDP = GFP, regardless the adhesive protocol used. It was concluded that: a) teeth restored with BDP exhibited lower fracture resistance than those restored with GFP; b) resin cement DC% was not influenced by the light transmitting ability of the post; c) the retention provided by the BDP was similar to the one provided by GFP, independently of the luting protocol.

Assuntos

RESUMO

Besides the effects on the health of individuals, cigarette smoking can also interfere with the appearance of their teeth. To evaluate the effect of cigarette smoking-toothbrushing-cycling (CSTC) with whitening toothpastes on the roughness and optical behavior of bovine enamel for eight weeks. Thirty bovine dentin/enamel discs, 8.0 mm in diameter and 2.0 mm thick, were randomly divided into three groups according to the toothpastes: whitening (Colgate Luminous White - CW and Oral B 3D White - OW), and a non-whitening (Colgate - C). The roughness, color (CIE L*a*b* system), translucency and gloss were measured before and after the specimens were submitted to CSTC. The topography of the specimens was analyzed by scanning electron microscopy. During the first week, the specimens were daily subjected to the consumption of 20 cigarettes and brushed (40 strokes/100 g) with the toothpastes' slurries. Thereafter, the CSTC was weekly applied in an accumulated model (140 cigarettes/280 strokes) for seven weeks. The data were submitted to two-way ANOVA, Tukey's HSD test, and paired-t test (α=0.05). The three toothpastes produced significant changes in roughness, color, translucency and gloss (p<0.05). After eight weeks, the roughness and the gloss produced by the three toothpastes were similar (p>0.05), while OW produced the lowest color change and the translucency of C was lower than that of CW (p<0.05). The three toothpastes produced a significant decrease in L* values and a significant increase in a* values after eight weeks (p<0.05). No significant difference in the b* coordinate was found for OW (p=0.13) There were topographic changes in the enamel surfaces. The whitening toothpastes increased the roughness, changed the topography and were not able to maintain the optical stability of enamel exposed over eight weeks.

Assuntos

RESUMO

Abstract Besides the effects on the health of individuals, cigarette smoking can also interfere with the appearance of their teeth. Objective: To evaluate the effect of cigarette smoking-toothbrushing-cycling (CSTC) with whitening toothpastes on the roughness and optical behavior of bovine enamel for eight weeks. Material and Methods: Thirty bovine dentin/enamel discs, 8.0 mm in diameter and 2.0 mm thick, were randomly divided into three groups according to the toothpastes: whitening (Colgate Luminous White - CW and Oral B 3D White - OW), and a non-whitening (Colgate - C). The roughness, color (CIE L*a*b* system), translucency and gloss were measured before and after the specimens were submitted to CSTC. The topography of the specimens was analyzed by scanning electron microscopy. During the first week, the specimens were daily subjected to the consumption of 20 cigarettes and brushed (40 strokes/100 g) with the toothpastes' slurries. Thereafter, the CSTC was weekly applied in an accumulated model (140 cigarettes/280 strokes) for seven weeks. The data were submitted to two-way ANOVA, Tukey's HSD test, and paired-t test (α=0.05). Results: The three toothpastes produced significant changes in roughness, color, translucency and gloss (p<0.05). After eight weeks, the roughness and the gloss produced by the three toothpastes were similar (p>0.05), while OW produced the lowest color change and the translucency of C was lower than that of CW (p<0.05). The three toothpastes produced a significant decrease in L* values and a significant increase in a* values after eight weeks (p<0.05). No significant difference in the b* coordinate was found for OW (p=0.13) There were topographic changes in the enamel surfaces. Conclusions: The whitening toothpastes increased the roughness, changed the topography and were not able to maintain the optical stability of enamel exposed over eight weeks.

Assuntos

RESUMO

The aim of this study was to evaluate the degree of conversion (DC%), water sorption (WS), solubility (SO), and resin-dentin bonding stability of experimental adhesive systems containing ZnCl2. Different concentrations (wt.%) of ZnCl2 were added to a model etch-and-rinse adhesive system consisting of BISGMA, HEMA, UDMA, GDMA, water, and ethanol: Zn0 (0%-control group); Zn2 (2%); Zn3.5 (3.5%); and Zn5 (5%). Adper Single Bond 2 (SB) was used as commercial reference. The samples were light cured for 20s using a quartz-tungsten-halogen unit (650 mW/cm2). DC% (n = 5) was measured using FT-IR spectroscopy, and WS and SO (n = 5) were calculated based on ISO4049. Microtensile bond strength (µTBS) and nanoleakage (NL) were measured after 24 h and 12 months of water storage (n = 10). Data were analyzed using ANOVA and Tukey's HSD test (5%). Zn5 presented the lowest DC% and the highest WS and SO (p < 0.05). Zn0 and Zn2 presented statistically similar DC%, WS, SO, and immediate µTBS. All adhesives containing ZnCl2 maintained a µTBS stability after 12 months, but only Zn2 and Zn3.5 did not suffer an increase in NL. SB presented the highest immediate µTBS but the greatest reduction after 12 months (p < 0.05). The addition of 2 wt.% of ZnCl2 in adhesive formulations seems to be a promising way to improve the resin-dentin bonding stability. Higher concentrations than 2 wt.% could impair some physicochemical properties.

Assuntos

RESUMO

This study evaluated the effect of air-abrasion on t®m phase transformation, roughness, topography and the elemental composition of three Y-TZP (Yttria-stabilized tetragonal zirconia polycrystal) dental ceramics: two conventional (Lava Frame and IPS ZirCad) and one with high-translucency (Lava Plus). Plates obtained from sintered blocks of each ceramic were divided into four groups: AS (as-sintered); 30 (air-abrasion with 30 mm Si-coated Al2O3 particles); 50 (air-abrasion with 50 mm Al2O3 particles) and 150 (air-abrasion with 150 mm Al2O3 particles). After the treatments, the plates were submitted to X-ray diffractometry; 3-D profilometry and SEM/EDS. The AS surfaces were composed of Zr and t phases. All treatments produced t®m phase transformation in the ceramics. The diameter of air-abrasion particles influenced the roughness (150>50>30>AS) and the topography. SEM analysis showed that the three treatments produced groove-shaped microretentions on the ceramic surfaces, which increased with the diameter of air-abrasion particles. EDS showed a decrease in Zr content along with the emergence of O and Al elements after air-abrasion. Presence of Si was also detected on the plates air-abraded with 30 mm Si-coated Al2O3 particles. It was concluded that irrespective of the type and diameter of the particles, air-abrasion produced t®m phase transformation, increased the roughness and changed the elemental composition of the three Y-TZP dental ceramics. Lava Plus also behaved similarly to the conventional Y-TZP ceramics, indicating that this high translucency ceramic could be more suitable to build monolithic ceramic restorations in the aesthetic restorative dentistry field.

Assuntos

RESUMO

Abstract This study evaluated the effect of air-abrasion on t®m phase transformation, roughness, topography and the elemental composition of three Y-TZP (Yttria-stabilized tetragonal zirconia polycrystal) dental ceramics: two conventional (Lava Frame and IPS ZirCad) and one with high-translucency (Lava Plus). Plates obtained from sintered blocks of each ceramic were divided into four groups: AS (as-sintered); 30 (air-abrasion with 30 mm Si-coated Al2O3 particles); 50 (air-abrasion with 50 mm Al2O3 particles) and 150 (air-abrasion with 150 mm Al2O3 particles). After the treatments, the plates were submitted to X-ray diffractometry; 3-D profilometry and SEM/EDS. The AS surfaces were composed of Zr and t phases. All treatments produced t®m phase transformation in the ceramics. The diameter of air-abrasion particles influenced the roughness (150>50>30>AS) and the topography. SEM analysis showed that the three treatments produced groove-shaped microretentions on the ceramic surfaces, which increased with the diameter of air-abrasion particles. EDS showed a decrease in Zr content along with the emergence of O and Al elements after air-abrasion. Presence of Si was also detected on the plates air-abraded with 30 mm Si-coated Al2O3 particles. It was concluded that irrespective of the type and diameter of the particles, air-abrasion produced t®m phase transformation, increased the roughness and changed the elemental composition of the three Y-TZP dental ceramics. Lava Plus also behaved similarly to the conventional Y-TZP ceramics, indicating that this high translucency ceramic could be more suitable to build monolithic ceramic restorations in the aesthetic restorative dentistry field.

Resumo Este estudo avaliou o efeito da abrasão a ar na transformação de fase t®m, na rugosidade, topografia e composição elementar de três cerâmicas Y-TZP (Zircônia tetragonal policristalina estabilizada por ítrio): duas convencionais (Lava Frame e ZirCad) e uma de alta translucidez (Lava Plus). Placas obtidas de blocos sinterizados de cada cerâmica foram divididos em quatro grupos: AS (pré-sinterizado); 30 (jateamento com partículas de Al2O3 de 30 mm cobertas com Si); 50 (jateamento com partículas de Al2O3 de 50 mm) e 150 (jateamento com partículas de Al2O3 de 150 mm). Após os tratamentos, as placas foram submetidas à difratometria de Rx, perfilometria 3-D e microscopia eletrônica de varredura com espectroscopia de energia dispersiva de Rx (SEM/EDS). As superfícies pré-sinterizadas apresentaram predominantemente Zr e fase tetragonal. Todos os tratamentos superficiais produziram transformação t®m nas cerâmicas avaliadas. A topografia e a rugosidade foram influenciadas pelo diâmetro das partículas abrasivas (150>50>30>AS). A análise através de SEM mostrou que os três tratamentos produziram fendas retentivas nas superfícies das cerâmicas, por influência do tamanho das partículas. A análise através de EDS mostrou uma diminuição da concentração de Zr, paralela ao surgimento de O e Al, após o jateamento. No grupo tratado com partículas de Al2O3 de 30 mm cobertas com Si foi também observado um aumento de Si após o jateamento. Concluiu-se que, independente do tipo e do diâmetro das partículas, o jateamento produziu transformação t®m, aumentou a rugosidade e alterou a composição elementar das cerâmicas avaliadas. A Lava Plus apresentou comportamento semelhante às cerâmicas convencionais, indicando que esta cerâmica de alta translucidez pode ser mais adequada à confecção de restaurações monolíticas no campo da odontologia estética restauradora.

Assuntos

RESUMO

OBJECTIVES: This study compared the influence of cement film thickness (CFT) on bond strength (BS) and fracture resistance (FR) of fiber-reinforced composite (FRC) posts to root canal. MATERIALS AND METHODS: One hundred bovine incisors were used for BS and FR analysis (n = 10) and distributed into five experimental groups according to FRC post diameters (WhitePost DC no. 0.5, no. 1, no. 2, no. 3, no. 4), leading to five different CFTs. The canals were prepared using drill no. 4 provided by the post manufacturer and irrigated with 2.5% NaOCl. After conditioning (24% H2O2/5 min) and silanization, posts were cemented with resin cement. BS was evaluated using push-out test and FR using the compression test at 45°. A stereomicroscope was used to measure CFT and to analyze failure pattern. BS data were subjected to two-way ANOVA and Scheffé test for contrast (α = 0.05); FR data were subjected to one-way ANOVA. RESULTS: BS was significantly affected by CFT, as the most well-adapted post achieved the highest values (p < 0.05). BS was similar for all root thirds. CFT did not affect fracture resistance. No root fractures were observed. CONCLUSIONS: A FRC post well adapted to the root canal results in higher BS values. Different CFTs did not influence the FR of teeth restored with FRC posts. CLINICAL RELEVANCE: The results indicate that post retention is improved when a well-adapted post is used, although this has not been critical to fracture resistance.

Assuntos

RESUMO

BACKGROUND: Several surface treatments could be used to improve the bond strength (BS) between indirect composites and cement. AIM: To evaluate the BS of an indirect composite submitted to different surface treatments, cemented to bovine dentin. SETTINGS AND DESIGN: One hundred and fifty conical cavities were prepared in slices of bovine dentin and bulk filled with the composite. MATERIALS AND METHODS: After curing and removal from the cavity, the restorations were treated according to the groups (n = 10): C-untreated, S-Sandblasting; SS-Sandblasting + silane; F-hydrofluoric acid; FS-hydrofluoric acid + silane; SF-Sandblasting + hydrofluoric acid; SFS-Sandblasting + hydrofluoric acid + silane; E-ethanol; ES-ethanol + silane; SE-Sandblasting + ethanol; SES-Sandblasting + ethanol + silane; P-H2O2; PS-H2O2 + silane; SP-Sandblasting + H2O2; SPS-Sandblasting + H2O2 + silane. After cementation, push-out test was performed in a universal testing machine. STATISTICAL ANALYSIS: Data were submitted to nonparametric tests (Kruskal-Wallis and Mann-Whitney U-tests, α = 0.05). The failure mode was observed under a stereomicroscope and the topography by scanning electronic microscopy (SEM). RESULTS: Sandblasted groups led to the highest BS values, (P < 0.001), except for the SFS group. SE, SES, and SPS led to higher BS values than S and SS groups (P < 0.05). F, E and P groups showed the lowest BS values. The number of cohesive or mixed failures was related to higher BS values. SEM evaluation showed major irregularities only for sandblasted groups. CONCLUSIONS: Sandblasting was a safe surface treatment for the indirect composite, increasing the BS values. Hydrofluoric acid applied after sandblasting damaged the BS values and should not be recommended while ethanol and H2O2, when applied after sandblasting, were effective in increasing BS values.

Assuntos

RESUMO

The aim of this study was to analyze the sorption and solubility of a nanofilled (Filtek Z350) and a midifilled (Filtek P60) resin composite in oral environment-like substances, in a simulated deep cavity. A cylindrical cavity prepared in a bovine incisor root was incrementally filled with resin composites. The obtained resin composite cylinders were cut perpendicularly to the axis to obtain 1-mm-thick discs that were divided into fifteen groups (n=5) according to depth (1, 2, 3, 4 and 5 mm) and immersion media (distilled water - DW, artificial saliva - AS and lactic acid - LA). The sorption and solubility were calculated based on ISO 4049:2000. Additionally, the degree of conversion (DC%) was calculated by FT-IR spectroscopy. Data were analyzed using multifactor analysis of variance (MANOVA) followed by Tukey's HSD post-hoc test and linear regression analysis (a=0.05). The DC% was higher for the midifilled resin composite and was negatively influenced by cavity depth (p<0.05). The nanofilled resin composite presented higher sorption and solubility than did the midifilled (p<0.05). The immersion media influenced the sorption and the solubility as follows: LA>AS>DW, (p<0.05). Both phenomena were influenced by cavity depth, with the sorption and solubility increasing from 1 to 5 mm (p<0.05). The degradation of resin composite restorations may be greater in the deepest regions of class II restorations when the composite is exposed to organic acids present in the oral biofilm (lactic acid).

O objetivo deste estudo foi analisar a absorção e a solubilidade de uma resina composta nanopartículada (Filtek Z350) e de uma híbrida (Filtek P60) em substâncias simuladoras do ambiente oral em um modelo de cavidade profunda. Uma cavidade cilíndrica, construída em uma raiz de um incisivo bovino, foi preenchida incrementalmente com as resinas compostas. Os cilindros obtidos foram seccionados perpendicularmente ao eixo para obtenção de discos com 1 mm de espessura, que foram divididos em 15 grupos (n=5) de acordo com a profundidade (1, 2, 3, 4 e 5 mm) e o meio de imersão (água destilada - AD, saliva artificial - SA e ácido lático - AL). A absorção e a solubilidade foram calculadas com base na norma ISO 4049:2000(E). Adicionalmente, o grau de conversão (GC%) foi calculado através de espectroscopia FT-IR. Os dados obtidos foram analisados usando análise de variância multifatorial, teste de Tukey HSD e análise de regressão linear (a=0,05). A resina composta híbrida apresentou o maior grau de conversão, sendo este influenciado pela profundidade da cavidade (p<0,05). A resina composta nanopartículada apresentou maiores valores de absorção e solubilidade (p<0,05). O meio de imersão influenciou a absorção e a solubilidade: AL>SA>AD (p<0,05). Ambos os fenômenos foram influenciados pela profundidade da cavidade, com os valores aumentando de 1 para 5 mm (p<0,05). A degradação de restaurações de resinas compostas pode ser maior em regiões profundas de restaurações classe II e quando o material é exposto à ácidos orgânicos produzidos pelo biofilme oral (ácido lático).

Assuntos