RESUMO

This study evaluated the hardness of a composite resin used for root reinforcement, considering the light-curing time, root canal region and ageing due to long-term storage. Twenty incisor roots were reinforced using composite resin, varying the photopolymerisation time (40 or 120 s). Following fibre post cementation, the roots were transversely sectioned into coronal, middle and apical regions. Composite hardness was measured initially and after 18 months of water storage. Data underwent repeated measures analysis of variance and Tukey's post hoc tests. The factors 'light-curing time', 'root region' and 'ageing' affected the hardness. Significant interactions were observed between 'light-curing time × root region' and 'ageing × light-curing time'. Regardless of time, resin hardness in the apical region was lower. After ageing, hardness in the coronal and middle regions decreased when the light-curing time was 40 s, while no significant effect on hardness was noted with a light-curing time of 120 s.

RESUMO

This study investigated the effect of the timing of primary endodontic treatment and dosage of radiotherapy on the remaining filling material (RFM) during endodontic reintervention. 60 single-rooted human mandibular premolars were distributed into five groups (n = 12), according to the timing and dosage of radiation (55Gy or 70Gy): NegativeCG-non-irradiated teeth; Endo-pre-RT55/70-obturation before irradiation (55Gy or 70Gy); Endo-post-RT55/70-obturation and reintervention after irradiation (55Gy or 70Gy). Roots were cleaved and analysed under stereomicroscope and Scanning Electron Microscope to quantify (%) the RFM. Experimental groups had a significantly greater amount (p < 0.05) of RFM in the middle and apical thirds than the control group, except for Endo-pre-RT55 in the middle third (p < 0.0001). The apical third had greater amount of RFM (p < 0.05). Radiation therapy, before and after primary endodontic treatment, increased the amount of RFM, regardless of the dose delivered. When necessary, reintervention preferably must be performed before radiation therapy.

Assuntos

RESUMO

OBJECTIVES: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin. MATERIALS AND METHODS: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA). Data were statistically compared after BS test (ANOVA, Tukey's post hoc test, and Fisher's exact test). RESULTS: In the SA mode, BS was significantly higher in nonirradiated teeth compared with 70RT and 70 + 70RT (p < 0.0001). There were no significant differences between SE and SA modes in nonirradiated teeth (p = 0.14). In the 70RT group, SE mode increased BS compared with SA mode (p < 0.0001). Most specimens had adhesive and mixed failures in SA and SE modes, respectively. CONCLUSIONS: The universal resin cement in the SE mode had greater BS to the irradiated dentin. When teeth were re-irradiated, the universal resin cement had similar performance in terms of BS, regardless of the adhesive approach. CLINICAL SIGNIFICANCE: There is no research establishing a correlation between radiotherapy and its impact on the BS of a universal resin cement used in SE and SA modes to intraradicular dentin.

Assuntos

RESUMO

This study assessed the influence of the type of endodontic access cavity on endodontic reintervention. Twenty mandibular central incisors were distributed into two groups (n = 10): TradAC group-traditional access cavities and UltraAC.Inc group-ultraconservative access cavities. After endodontic access, the root canals were prepared and obturated by the single cone technique. The filling material was removed with the Reciproc R25 instrument, followed by reinstrumentation with the R40 instrument. Images acquisition of each root canal hemisection was performed in a stereomicroscope to quantify the amount of remaining filling material. The amount of remaining filling material attached to the root canal walls was expressed in square millimeter (mm2). Data were statistically analyzed (one-way ANOVA and post hoc Student's t-tests). There was no statistically significant difference between TradAC and UltraAC.Inc groups (p > 0.05). None of the tested endodontics' access showed root canal walls completely free of filling material. Ultraconservative access cavities in mandibular incisors had no negative impact on the filling material removal.

RESUMO

The interaction of sodium hypochlorite (NaOCl) and chlorhexidine gluconate (CHX) produces an orange-brown precipitate. The present study evaluated the influence of distilled water (H2 O) in different irrigation protocols designed to prevent the formation of precipitate with NaOCl and CHX. Fifty canine teeth were instrumented and split longitudinally. The canal was examined with a stereomicroscope and photographed by canal-thirds. The tooth halves were repositioned and distributed randomly into five groups, according to the final irrigation protocol (n = 10): G1 (control)-Ethylenediaminetetraacetic acid (EDTA) + NaOCl + CHX, conventional irrigation (CI); G2-EDTA + NaOCl + CHX, activated with passive ultrasonic irrigation (PUI); G3-EDTA (PUI) + NaOCl (PUI) + H2 O (CI) + CHX (PUI); G4-EDTA + NaOCl + H2 O + CHX (PUI); G5-EDTA (PUI) + NaOCl (PUI) + H2 O (continuous ultrasonic irrigation [CUI]) + CHX (PUI). The specimens were evaluated with a stereomicroscope and scanning electron microscope (SEM). Energy dispersive x-ray spectroscopy analysis was performed to identify the elemental profile of the irrigated canal walls. The images were scored according to the extensiveness of precipitate. Data were analyzed (Kruskal-Wallis test, α = 5%). Under the stereomicroscope, G1 had significantly higher scores than all the other groups in all canal-thirds (p < .05). All four experimental groups showed similar scores (p > .05). There were no significant differences in precipitate formation among root-thirds in intragroup analysis (p > .05). Upon SEM examination, overall, only G5 had lower scores than G1 (p < .05). Analysis by canal-thirds showed no significant difference among groups and among canal-thirds in the intragroup analysis (p > .05). G1 showed high Cl peaks. In-between irrigation with H2 O activated by CUI is effective in preventing precipitate formation during canal debridement with NaOCl and CHX. RESEARCH HIGHLIGHTS: Continuous ultrasonic irrigation with distilled water was capable to prevent the precipitate formation. The precipitate can be classified as a chemical smear layer.

Assuntos

RESUMO

BACKGROUND: The literature is scanty regarding the effect of radiation therapy (RT) on the mechanical properties of immature permanent teeth. AIM: To evaluate the effect of RT on the fracture resistance of simulated immature teeth submitted to different types of root reinforcement. DESIGN: Sixty-four human teeth simulating the Cvek stage 3 of root development were distributed into eight groups (n = 8), according to exposure or not to RT (70 Gy) and the root reinforcement method: Group NR (control)-no reinforcement/no RT; Group NR + RT (control)-no reinforcement/RT; Group PO-tricalcium silicate-based cement (TS) apical plug/canal obturation/no RT; Group PO + RT-TS apical plug/canal obturation/RT; Group TS-canal filling with TS/no RT; Group TS + RT-canal filling with TS/RT; Group FP-TS apical plug/fibreglass post/no RT; and Group FP + RT-TS apical plug/fibreglass post/RT. Fracture resistance was determined using a universal testing machine (0.5 mm/min). RESULTS: In the intergroup comparison, nonirradiated teeth had higher fracture resistance (p < .05). Groups FP and FP + RT had higher fracture resistance (p < .001). CONCLUSION: Radiotherapy affected the fracture resistance of simulated immature teeth. Reinforcement with fibreglass posts increased the fracture resistance, regardless of the radiation.

Assuntos

RESUMO

This study evaluated the effect of heating on the physicochemical properties and surface changes of tricalcium silicate sealers. Three tricalcium silicate root canal sealers (Bio-C Sealer, BioRoot-RCS, EndoSequence BC Sealer), and one epoxy resin-based sealer (AH Plus; control) were tested. The effect of heating on setting time (ST) and flowability were assessed according to ANSI/ADA 57 and ISO 6876 standards. Solubility and dimensional change (DC) of the set sealers were evaluated at 24 hours and after 30 days; the pH of the water used in the DC testing was also measured. Tests were repeated with heated sealers in an oven at 100 °C for 1 min. SEM and EDS analysis were performed. Data were analyzed using One-Way ANOVA and Tukey post-hoc tests (α=5%). Heating decreased the ST for AH Plus and EndoSequence (p<0.05). Heating reduced flowability (p<0.05) and increased pH for AH Plus (p<0.05). The solubility of Bio-C (dried specimens) was not in accordance with the ANSI/ADA standard. The solubility of EndoSequence was significantly higher (p<0.05) when it was heated and dried after 30 days. DC of Bio-C (24 h and 30 days), BioRoot-RCS (30 days) and AH Plus (24 h and 30 days) were not in accordance with the standards. SEM and EDS analysis showed significant changes in sealer microstructure after heating. In conclusion, heating decreased the ST and increased the solubility of EndoSequence BC sealer. No significant changes in flowability, DC, and pH were identified for all three tricalcium silicate sealers after heat application. However, all sealers had significant surface changes.

Assuntos

RESUMO

Introduction: The aim of this study was to evaluate the effect of heating of bioceramic and epoxy resin-based sealers on their micro-push-out bond strength (BS) to root canal dentin. Methods: After criterial selection, 30 human teeth were decoronated and 1-mm thick slices (n = 60) were obtained perpendicularly along tooth axis, from cervical and middle root thirds, with a diamond disc attached to a cutting machine. In each slice, three 1.0-mm diameter orifices were made. After rinsing with 17% EDTA and 2.5% NaOCl, each orifice was filled with Bio-C Sealer or BioRoot RCS or AH Plus, according to the manufacturers' instructions. After filling, half of the slices (n = 30) were heated at 100°C for 1 min, and the other half were kept at room temperature. After 7 days-controlled storage, micro-push-out test was performed in a Universal Testing Machine. Failures were analyzed using a stereomicroscope. Statistical analysis was performed with One-Way ANOVA and post hoc Tukey (α = 5%) tests. Results: AH Plus demonstrated higher BS values after heating (p=0.001) when compared to nonheated. The other sealers did not show a statistically significant difference (p > 0.05). When heated, the average BS values for AH Plus were higher than for BioRoot RCS and Bio-C Sealer (p < 0.001). Cohesive failure mode was the most frequent, followed by adhesive and mixed ones. Conclusion: Heating provided a higher push-out BS to root dentin for AH Plus and did not influence BioRoot RCS or Bio-C sealer.

RESUMO

Objectives: This study was conducted to evaluate and compare the tip and taper compatibility of accessory gutta-percha points (AGPs) with various rotary and reciprocating instruments. Materials and Methods: Using a profile analyzer, tip and taper measurements were taken of 10 AGPs of each of the 14 models available from Odous de Deus and the 4 models available from Dentsply-Maillefer. Diameter measurements were taken at 1-mm intervals, from 3 mm from the tip (D3) to 16 mm. Results: Based on the mean values obtained, 3-dimensional (3D) models of the AGPs were drawn in Autodesk Fusion 360 and superimposed on 3D models of each instrument selected (Mtwo, Reciproc, RaCe, K3, and ProDesign Logic) to determine the compatibility between the instrument and the AGP. Data corresponding to the tips and tapers of the various AGPs, as well as the tip and taper differences between the AGPs and the instruments, were analyzed using descriptive statistics. The tapers of the AGPs were subject to the American National Standards Institute/American Dental Association No. 57 standard. The Odous de Deus extra-long medium and extra-long extra-medium AGPs were shown to be compatible with Mtwo, K3, and ProDesign Logic instruments with taper 0.06 and tip sizes 25 and 30, while the Dentsply fine and fine medium cones were compatible with Mtwo, RaCe, and K3 instruments with conicity of 0.04 and tip sizes 35 and 40. Conclusions: Both the Odous de Deus and Dentsply commercial brands included 2 AGP models with tip (D3) and taper compatibility with Mtwo, RaCe, K3, and/or Prodesign Logic instruments.