RESUMO
OBJECTIVES: The study aimed to assess the impact of diphenyliodonium hexafluorophosphate (DPI) on the physicochemical properties of experimental resin composites (ECRs) featuring reduced concentrations of camphorquinone (CQ)/amine. METHODS: Five concentrations of CQ (0.125, 0.25, 0.5, 0.75, and 1 mol%) with dimethylaminoethyl amine benzoate (EDAB) in a 1:2 mol% ratio (CQ:EDAB) were incorporated into a 50:50 mass% monomer blend of bisphenol glycidyl methacrylate (BisGMA) and triethyleneglycol dimethacrylate (TEGDMA). An additional 5 groups with the same CQ:EDAB concentrations had 0.5 mol% DPI added. Each resin group contained 60 wt% of 0.7 µm barium-alumino-silicate glass. Light transmission (n = 3), real-time degree of polymerization (n = 3), temperature change during polymerization (n = 5), polymerization shrinkage strain (n = 3), flexural strength, and modulus (n = 12), as well as water sorption and solubility (n = 5), were evaluated. Data were analyzed using two-way ANOVA and Tukey's post-hoc test (α = 0.05). RESULTS: Light transmission was reduced in groups containing 0.125 and 0.25 mol% of CQ without DPI. DPI increased temperature, degree and rate of polymerization, despite the reduction in CQ/amine concentration. Additionally, there was an increase in polymerization shrinkage strain, flexural strength and modulus, and a reduction in water sorption and solubility in ECRs with DPI, even with lower concentrations of CQ/EDAB. SIGNIFICANCE: DPI improved the assessed properties of composites across various concentrations of CQ/EDAB, showing the benefit of reducing the quantity of CQ used without compromising the properties and curing of the resin composites.
Assuntos
Resinas Compostas , Teste de Materiais , Polietilenoglicóis , Polimerização , Ácidos Polimetacrílicos , Terpenos , Resinas Compostas/química , Terpenos/química , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Bis-Fenol A-Glicidil Metacrilato/química , Propriedades de Superfície , Oniocompostos/química , Poliuretanos/química , Resinas Acrílicas , Compostos de Bifenilo , Cânfora/análogos & derivadosRESUMO
OBJECTIVE: The aim of this study was to evaluate the effect of surface treatments and adhesive protocols on the microtensile bond strength of a low-shrinkage composite repair. MATERIALS AND METHODS: Ninety-six blocks of composite resin Filtek LS were prepared using a half-hourglass-shaped silicone matrix. The specimens were storage for 24 h in distilled water and were randomly divided into the experimental (6) and negative control (2) groups (n = 12) according to the surface treatment (diamond bur and aluminum oxide sandblasting) and adhesive protocol (none; Filtek LS adhesive; phosphoric acid + Filtek LS adhesive; and phosphoric acid + silane + Filtek LS adhesive). After the adhesive procedure, the specimens were fixed in an hourglass-shaped silicone matrix and the other half of the specimen was restored. Hourglass shaped specimens (n = 12) were used as positive control (cohesive strength of the resin). The microtensile bonding test was performed at a crosshead speed of 0.5 mm/min. The data were analyzed using ANOVA, Tukey's and Dunnett's tests (α = 0.05). RESULTS: The bond strength values were similar for all experimental groups, except the groups without adhesive application. None of the experimental groups presented results similar to the positive control group. CONCLUSIONS: The repair of silorane restorations is viable; nevertheless, the different bonding procedures tested were incapable to produce bond strengths similar to the cohesive strength of the material.
Assuntos
Resinas Compostas , Colagem Dentária/métodos , Resinas de Silorano , Propriedades de SuperfícieRESUMO
The aim of the present study was to evaluate the degree of conversion (DC), elastic modulus (E), and flexural strength (FS) of five adhesive systems (only the bonding component of both Scotchbond MP-SBMP and Clearfil Protect Bond-CP; Single Bond 2-SB2; One-up Bond F Plus-OUP; and P90 System Adhesive: primer-P90P and bond-P90B) cured with a quartz tungsten halogen (QTH) lamp and a light-emitting diode (LED). Two groups per adhesive were formed (n=5), according to the light source (quartz tungsten halogen-QTH: Demetron LC; and light-emitting diode-LED: UltraLume 5). Bar-shaped specimens were evaluated using three-point bending. The DC was obtained by Fourier transform infrared spectroscopy (FTIR). SB2 and P90P exhibited better DC values for QTH curing. However, SB2 and P90P presented the worst results overall. The light source was statistically significant for all adhesives, except for P90B and OUP. Non-solvated adhesives presented the best E and FS values. It could be concluded that the DC and E values can be influenced by the light source; however, this interference is material dependent.
Assuntos
Adesivos/química , Materiais Biocompatíveis/química , Cimentos de Resina/química , Adesividade , Lâmpadas de Polimerização Dentária , Módulo de Elasticidade , Halogênios/química , Luz , Teste de Materiais , Polímeros/química , Espectroscopia de Infravermelho com Transformada de Fourier/métodos , Estresse Mecânico , Tungstênio/químicaRESUMO
We compared polymerization stress in two commercial composites and three experimental composites made using camphorquinone (CQ) and/or phenylpropanedione (PPD) as photoinitiators. The internal surfaces of photoelastic resin discs with cylindrical cavities were roughened and treated with adhesive. Composites were divided into five groups: two commercial composites (Filtek Silorane and Filtek Z250) and three experimental composites with CQ/amine, CQ/PPD/amine, and PPD/amine. Composites were photopolymerized inside cavities, and subjected to photoelastic analysis immediately and at 24 hours and 7 days later using a plane polariscope. Stress created by Silorane (3.08 ± 0.09 MPa) was similar to that of Z250 (3.19 ± 0.13 MPa) immediately after photopolymerization (p > 0.05). After 24 hours and 7 days, Z250 (3.53 ± 0.15 and 3.69 ± 0.10 MPa, respectively) showed higher stress than Silorane (3.19 ± 0.10 and 3.16 ± 0.10 MPa, respectively). Qualitative analysis immediately after photopolymerization showed composite/CQ promoted higher stress than PPD, but stress levels at other evaluated times were statistically similar, varying between 3.45 ± 0.11 MPa and 3.92 ± 0.13 MPa. At 24 hours and 7 days, Silorane created the lowest stress. All photoinitiators created comparable tensions during polymerization.
Assuntos
Humanos , Cânfora/análogos & derivados , Resinas Compostas/química , Polimerização , Fotoiniciadores Dentários/química , Análise de Variância , Cânfora/química , Módulo de Elasticidade , Teste de Materiais , Transição de Fase , Estresse Mecânico , Propriedades de Superfície , Fatores de TempoRESUMO
We compared polymerization stress in two commercial composites and three experimental composites made using camphorquinone (CQ) and/or phenylpropanedione (PPD) as photoinitiators. The internal surfaces of photoelastic resin discs with cylindrical cavities were roughened and treated with adhesive. Composites were divided into five groups: two commercial composites (Filtek Silorane and Filtek Z250) and three experimental composites with CQ/amine, CQ/PPD/amine, and PPD/amine. Composites were photopolymerized inside cavities, and subjected to photoelastic analysis immediately and at 24 hours and 7 days later using a plane polariscope. Stress created by Silorane (3.08 ± 0.09 MPa) was similar to that of Z250 (3.19 ± 0.13 MPa) immediately after photopolymerization (p > 0.05). After 24 hours and 7 days, Z250 (3.53 ± 0.15 and 3.69 ± 0.10 MPa, respectively) showed higher stress than Silorane (3.19 ± 0.10 and 3.16 ± 0.10 MPa, respectively). Qualitative analysis immediately after photopolymerization showed composite/CQ promoted higher stress than PPD, but stress levels at other evaluated times were statistically similar, varying between 3.45 ± 0.11 MPa and 3.92 ± 0.13 MPa. At 24 hours and 7 days, Silorane created the lowest stress. All photoinitiators created comparable tensions during polymerization.
Assuntos
Cânfora/análogos & derivados , Resinas Compostas/química , Fotoiniciadores Dentários/química , Polimerização , Análise de Variância , Cânfora/química , Módulo de Elasticidade , Humanos , Teste de Materiais , Transição de Fase , Estresse Mecânico , Propriedades de Superfície , Fatores de TempoRESUMO
This study evaluated the effect of sterilization method on the bond strength of caries-affected dentin before artificial caries development and after restoration. Twelve bovine incisors were sectioned perpendicularly to their long axes at 7 mm from the amelodentinal junction. They were painted with acid-resistant nail varnish, except on an exposed coronal dentin area. Four groups were formed (n = 3) in accordance with the sterilization method used, before artificial caries development and after complete restoration: NE - no sterilization (control group); G - gamma-rays before and after; A - steam autoclave before and after; AG - steam autoclave before and gamma-rays after. For artificial caries development, dentin sections were immersed in BHI broth with S. mutans. After the soft carious tissue was removed, dentin was restored with Scotchbond Multi-Purpose and Filtek Z250. Next, the samples were sterilized in accordance with the methods described above and microtensile testing was performed. The data were analyzed by the Mann-Whitney test (p < 0.05). The G (22.7 MPa) and AG groups (16.3 MPa) were not statistically different from the NE group (17.5 MPa). Nevertheless, there were statistical differences between groups A (6.3 MPa) and NE, A and G, A and AG, G and AG. The bond strength of caries-affected dentin was not influenced by gamma-ray sterilization irrespective of whether the sterilization was performed before or after restoration.
Assuntos
Resinas Compostas/uso terapêutico , Cárie Dentária/terapia , Restauração Dentária Permanente , Esterilização/métodos , Resistência à Tração , Animais , BovinosRESUMO
This study evaluated the effect of sterilization method on the bond strength of caries-affected dentin before artificial caries development and after restoration. Twelve bovine incisors were sectioned perpendicularly to their long axes at 7 mm from the amelodentinal junction. They were painted with acid-resistant nail varnish, except on an exposed coronal dentin area. Four groups were formed (n = 3) in accordance with the sterilization method used, before artificial caries development and after complete restoration: NE - no sterilization (control group); G - gamma-rays before and after; A - steam autoclave before and after; AG - steam autoclave before and gamma-rays after. For artificial caries development, dentin sections were immersed in BHI broth with S. mutans. After the soft carious tissue was removed, dentin was restored with Scotchbond Multi-Purpose and Filtek Z250. Next, the samples were sterilized in accordance with the methods described above and microtensile testing was performed. The data were analyzed by the Mann-Whitney test (p < 0.05). The G (22.7 MPa) and AG groups (16.3 MPa) were not statistically different from the NE group (17.5 MPa). Nevertheless, there were statistical differences between groups A (6.3 MPa) and NE, A and G, A and AG, G and AG. The bond strength of caries-affected dentin was not influenced by gamma-ray sterilization irrespective of whether the sterilization was performed before or after restoration.