RESUMO

Background: Among the main advantages of self-adhesive resin cements comprise good aesthetics, strong restoration-tooth bond and biocompatibility. However, some disadvantages, such as high viscosity level, color limitation and short shelf life should be mentioned. Thus, the aim of the current study was to assess bond strength between fiberglass post and root dentin in teeth subjected to self-adhesive resin cements with expired shelf life and hardness. Material and Methods: Sixty (60) single-rooted human teeth were sectioned and divided into 2 groups of different cements: U200 3M and MaxCem Elite Kerr. Each group was divided into 3 subgroups, based on self-adhesive resin cements' shelf life, namely: Within the use-time recommended by the manufacturer or no expiration date; 6 months after opening the aluminum blister; 12 months after opening the aluminum blister. Bond strength was measured through push-out test conducted in universal testing machine; fracture pattern was analyzed, and microhardness was investigated through Knoop test, based on hardness readings. Data were subjected to Shapiro-Wilk normality test; nonparametric test was applied to hardness data, whereas parametric test was applied to bond strength data. Hardness data were subjected to Kruskal-Wallis test, whereas bond strength data were subjected to analysis of variance, which was followed by Tukey test; both tests were conducted at 5% significance level (α = 0.05). Results: There was no statistically significant difference in knoop hardness values recorded for the material / time / root thirds combination (p=0.483). There was no statistically significant difference in bond strength values recorded for the Material / Time / Thirds combination (p=0.237). Conclusions: It was possible concluding that shelf life did not influence material's hardness and bond strength. Key words:Dental cements, Resin Cements, Shelf Life of Products.

RESUMO

The aims of this clinical study were to evaluate the Color change - ΔE (based on spectrophotometry and visual analysis) and luminosity - L* (based on spectrophotometry) of dental enamel surface (after orthodontic treatment) around the area where orthodontic brackets were fixed, based on different cementing materials such as a resin (R group) and resin-modified glass ionomer cement (RMGIC group). The split-mouth study initially comprised 14 patients. Orthodontic brackets were fixed to the upper central incisors with resin or RMGIC. The color of the buccal surface of each tooth was measured through spectrophotometry and visual examination before the bracket-fixation process. Four individuals were excluded during the follow-up; thus 10 patients were evaluated (n=10). Brackets were removed after 12 months of orthodontic treatment, tooth color measurement and visual examination were performed again, and Adhesive Remaining Index (ARI) was also measured. ΔE and L* results were subjected to Student's t-test and by repeated-measures analysis of variance, respectively (α=0.05). ARI data were analyzed in percentages. There was statistically significant difference in ΔE between groups; the R group showed statistically higher values of L* after orthodontic treatment. ARI of 2 and 3 prevailed in the RMGIC group, whereas the R group presented 0 and 1. After orthodontic treatment, the RMGIC group presented smaller changes in ΔE, and the increase in the white scale was observed on the enamel surface around the area where brackets were fixed in the R group. The visual analysis did not show color change on the evaluated teeth.

Assuntos

RESUMO

Abstract The aims of this clinical study were to evaluate the Color change - ΔE (based on spectrophotometry and visual analysis) and luminosity - L* (based on spectrophotometry) of dental enamel surface (after orthodontic treatment) around the area where orthodontic brackets were fixed, based on different cementing materials such as a resin (R group) and resin-modified glass ionomer cement (RMGIC group). The split-mouth study initially comprised 14 patients. Orthodontic brackets were fixed to the upper central incisors with resin or RMGIC. The color of the buccal surface of each tooth was measured through spectrophotometry and visual examination before the bracket-fixation process. Four individuals were excluded during the follow-up; thus 10 patients were evaluated (n=10). Brackets were removed after 12 months of orthodontic treatment, tooth color measurement and visual examination were performed again, and Adhesive Remaining Index (ARI) was also measured. ΔE and L* results were subjected to Student's t-test and by repeated-measures analysis of variance, respectively (α=0.05). ARI data were analyzed in percentages. There was statistically significant difference in ΔE between groups; the R group showed statistically higher values of L* after orthodontic treatment. ARI of 2 and 3 prevailed in the RMGIC group, whereas the R group presented 0 and 1. After orthodontic treatment, the RMGIC group presented smaller changes in ΔE, and the increase in the white scale was observed on the enamel surface around the area where brackets were fixed in the R group. The visual analysis did not show color change on the evaluated teeth.

Resumo Os objetivos deste estudo clínico foram avaliar a alteração de cor - ΔE (baseada em espectrofotometria e análise visual) e luminosidade - L* (baseada em espectrofotometria) da superfície do esmalte dentário (após tratamento ortodôntico) ao redor da área onde os braquetes ortodônticos foram fixados, com base em diferentes materiais de cimentação, como resina (grupo R) e cimento de ionômero de vidro modificado por resina (grupo RMGIC). Estudo boca dividida foi inicialmente composto por 14 pacientes. Os braquetes ortodônticos foram fixados nos incisivos centrais superiores com resina ou RMGIC. A cor da superfície vestibular de cada dente foi mensurada por espectrofotometria e avaliada por exame visual antes do processo de fixação dos braquetes. Quatro indivíduos foram excluídos durante o acompanhamento; assim, 10 pacientes foram avaliados (n=10). Os braquetes foram removidos após 12 meses de tratamento ortodôntico, a mensuração da cor do dente e o exame visual foram realizados novamente, e o Índice de Remanescente do Adesivo (IRA) também foi mensurado. Os resultados ΔE e L* foram submetidos ao teste t de Student e à análise de variância para medidas repetidas, respectivamente (α=0.05). Os dados do ARI foram analisados em porcentagens. Houve diferença estatisticamente significativa no ΔE entre os grupos; o grupo R apresentou valores estatisticamente maiores de L* após o tratamento ortodôntico. O IRA 2 e 3 prevaleceu no grupo RMGIC, enquanto o grupo R apresentou 0 e 1. Após o tratamento ortodôntico, o grupo RMGIC apresentou menores alterações no ΔE e o aumento da escala branca foi observado na superfície do esmalte ao redor da área onde os braquetes foram fixados no grupo R. A análise visual não mostrou mudança de cor nos dentes avaliados.

RESUMO

The longevity of prosthetic rehabilitation is determined by the stability of the implant and abutment interfaces. True morse taper connections on dental restorations have been effective, however activation force still empirical. This work compared the activation strength and internal contact of Morse taper system according to the removal force. Eighty sets, composed of implants and prosthetic abutments, were evaluated with different internal contact areas; 15.12mm2 (G3.3) and 21.25mm2 (G4.3). The specimens were activated at 0° and 30°, with loads of 10, 20, 40 and 60N. The specimens were submitted to tensile test and the data to ANOVA and Tukey's tests (α=0.05). Representative specimens were examined under SEM. Removal force of G3.3 (2.15±1.33MPa) did not differed to G4.3 (1.99±1.03MPa). The activation at 0º (2.95±0.98MPa) statistically differed to 30º (1.19±0.54MPa). The 60N load was statistically superior for G3.3 and there was no statistical difference between 20N to 60N in G4.3. The values of 10N at 30o and 20N at the long axis of the morse taper implant, independent of the frictional contact area showed the best settlement.

Assuntos

RESUMO

Abstract The longevity of prosthetic rehabilitation is determined by the stability of the implant and abutment interfaces. True morse taper connections on dental restorations have been effective, however activation force still empirical. This work compared the activation strength and internal contact of Morse taper system according to the removal force. Eighty sets, composed of implants and prosthetic abutments, were evaluated with different internal contact areas; 15.12mm2 (G3.3) and 21.25mm2 (G4.3). The specimens were activated at 0° and 30°, with loads of 10, 20, 40 and 60N. The specimens were submitted to tensile test and the data to ANOVA and Tukey's tests (α=0.05). Representative specimens were examined under SEM. Removal force of G3.3 (2.15±1.33MPa) did not differed to G4.3 (1.99±1.03MPa). The activation at 0º (2.95±0.98MPa) statistically differed to 30º (1.19±0.54MPa). The 60N load was statistically superior for G3.3 and there was no statistical difference between 20N to 60N in G4.3. The values of 10N at 30o and 20N at the long axis of the morse taper implant, independent of the frictional contact area showed the best settlement.

Resumo A longevidade da reabilitação protética é determinada pela estabilidade das interfaces implante e pilar. Conexões de cone Morse em restaurações dentárias têm se mostrado eficazes, porém a força de ativação ainda é empírica. Este trabalho comparou a força de ativação e contato interno do sistema cone Morse de acordo com a força de remoção. Oitenta conjuntos, compostos por implantes e pilares protéticos, foram avaliados com diferentes áreas de contato interno; 15,12mm2 (G3.3) e 21,25mm2 (G4.3). Os corpos-de-prova foram ativados a 0° e 30°, com cargas de 10, 20, 40 e 60N. Os corpos de prova foram submetidos ao ensaio de tração e os dados aos testes ANOVA e Tukey (α=0,05). Espécimes representativos foram examinados em MEV. A força de deslocamento do G3.3 (2,15±1,33MPa) não diferiu do G4.3 (1,99±1,03MPa). A ativação a 0º (2,95±0,98MPa) diferiu estatisticamente para 30º (1,19±0,54MPa). A carga de 60N foi estatisticamente superior para G3.3 e não houve diferença estatística entre 20N a 60N no G4.3. Os valores de 10N em 30o e 20N no longo eixo do implante cone morse, independente da área de contato friccional apresentaram o melhor assentamento.

RESUMO

This paper evaluates the physicochemical and biological properties of experimental resin-based dual-cured calcium aluminate (CA) and calcium titanate (CTi) materials for vital pulp therapy (VPT). The experimental dual-cured materials were obtained as two pastes: a) Bis-EMA 10, PEG 400, DHEPT, EDAB, camphorquinone, and butylated hydroxytoluene; and b) fluoride ytterbium, Bis-EMA 10, Bis-EMA 30, benzoyl peroxide, and butylated hydroxytoluene. The materials were divided into six groups based on the added calcium component: MTA (MTA®, Angelus); CLQ (Clinker-Fillapex®, Angelus); CA (calcined at ,1200°C in pastes a and b); CA800 (calcined at 800°C in paste a); CA1200 (calcined at 1,200°C in paste a); and CTi (paste a). The real-time degree of conversion and rate of polymerization (n = 3), diametral tensile strength (n = 10), hydrogen potential (n = 15), calcium ion release (n = 10), water sorption and solubility (n = 10), and cell viability (n = 6) were evaluated. One- and two-way ANOVA and Tukey's post hoc test were used in the analysis of the parametric data, and Kruskal-Wallis and Dunn's multiple tests were used to analyze the nonparametric data (α = 0.05). CLQ, CA800 and CA1200 had the highest diametral tensile strength. The water solubility of MTA was similar to that of CA800, CA1200 and CTi. CA800 and CA1200 resulted in cell viabilities similar to those of MTA and CLQ. The experimental dual-cured CA-based material that calcined at 800°C showed physicochemical and biological properties suitable for VPT, and similar to those of MTA.

Assuntos

RESUMO

Abstract: This paper evaluates the physicochemical and biological properties of experimental resin-based dual-cured calcium aluminate (CA) and calcium titanate (CTi) materials for vital pulp therapy (VPT). The experimental dual-cured materials were obtained as two pastes: a) Bis-EMA 10, PEG 400, DHEPT, EDAB, camphorquinone, and butylated hydroxytoluene; and b) fluoride ytterbium, Bis-EMA 10, Bis-EMA 30, benzoyl peroxide, and butylated hydroxytoluene. The materials were divided into six groups based on the added calcium component: MTA (MTA®, Angelus); CLQ (Clinker-Fillapex®, Angelus); CA (calcined at ,1200°C in pastes a and b); CA800 (calcined at 800°C in paste a); CA1200 (calcined at 1,200°C in paste a); and CTi (paste a). The real-time degree of conversion and rate of polymerization (n = 3), diametral tensile strength (n = 10), hydrogen potential (n = 15), calcium ion release (n = 10), water sorption and solubility (n = 10), and cell viability (n = 6) were evaluated. One- and two-way ANOVA and Tukey's post hoc test were used in the analysis of the parametric data, and Kruskal-Wallis and Dunn's multiple tests were used to analyze the nonparametric data (α = 0.05). CLQ, CA800 and CA1200 had the highest diametral tensile strength. The water solubility of MTA was similar to that of CA800, CA1200 and CTi. CA800 and CA1200 resulted in cell viabilities similar to those of MTA and CLQ. The experimental dual-cured CA-based material that calcined at 800°C showed physicochemical and biological properties suitable for VPT, and similar to those of MTA.

RESUMO

The aims of this in vivo study were to evaluate the effect of bonding with resin-modified glass ionomer cement (RMGIC) and to assess enamel surface roughness before and after the removal of brackets bonded with composite or RMGIC from the maxillary central incisors. Fifteen orthodontic patients were selected for the study. For each patient, the teeth were rinsed and dried, and brackets were bonded with composite (Transbond XT) and RMGIC (Vitremer Core Buildup/Restorative). At the conclusion of orthodontic treatment, their brackets were removed. Dental replicas were made of epoxy resin in initial conditions (before bonded) and after polishing with an aluminum oxide disc system. Adhesive remnant index (ARI) and surface roughness was measured on the dental replicas and data were evaluated statistically by Mann-Whitney and paired t-test, respectively. No bracket debonding occurred during patients' treatment periods. It was verified that the ARI values of the two maxillary central incisors were similar (p = 0.665). For both bonding materials, the ARI value of 3 was predominant. After polishing, surface roughness was similar in the composite and RMGIC groups (0.245 µm and 0.248 µm, respectively; p = 0.07). In both groups, enamel surface roughness values were significantly lower after polishing compared with the initial condition (p < 0.001). RMGIC promoted efficiency in cementing brackets without fail during treatment; the choice of composite or RMGIC materials was not a factor that influenced the roughness of the enamel surface, however, polishing led to smoother surfaces than those found at the beginning of the treatment.

Assuntos

RESUMO

Abstract The aims of this in vivo study were to evaluate the effect of bonding with resin-modified glass ionomer cement (RMGIC) and to assess enamel surface roughness before and after the removal of brackets bonded with composite or RMGIC from the maxillary central incisors. Fifteen orthodontic patients were selected for the study. For each patient, the teeth were rinsed and dried, and brackets were bonded with composite (Transbond XT) and RMGIC (Vitremer Core Buildup/Restorative). At the conclusion of orthodontic treatment, their brackets were removed. Dental replicas were made of epoxy resin in initial conditions (before bonded) and after polishing with an aluminum oxide disc system. Adhesive remnant index (ARI) and surface roughness was measured on the dental replicas and data were evaluated statistically by Mann-Whitney and paired t-test, respectively. No bracket debonding occurred during patients' treatment periods. It was verified that the ARI values of the two maxillary central incisors were similar (p = 0.665). For both bonding materials, the ARI value of 3 was predominant. After polishing, surface roughness was similar in the composite and RMGIC groups (0.245 μm and 0.248 μm, respectively; p = 0.07). In both groups, enamel surface roughness values were significantly lower after polishing compared with the initial condition (p < 0.001). RMGIC promoted efficiency in cementing brackets without fail during treatment; the choice of composite or RMGIC materials was not a factor that influenced the roughness of the enamel surface, however, polishing led to smoother surfaces than those found at the beginning of the treatment.

Resumo Os objetivos deste estudo in vivo foram avaliar o efeito da colagem com cimento de ionômero de vidro modificado por resina (CIVMR) e a rugosidade da superfície do esmalte antes e após a remoção dos braquetes colados com compósito ou CIVMR em incisivos centrais superiores. Quinze pacientes ortodônticos foram selecionados para o estudo. Para cada paciente, os dentes foram lavados e secos, e os braquetes colados com compósito (Transbond XT) e CIVMR (Vitremer Core Buildup / Restorative). Ao término do tratamento ortodôntico, os braquetes foram removidos. As réplicas dentais foram confeccionadas em resina epóxica nas condições iniciais (antes da colagem) e após o polimento com sistema de discos de óxido de alumínio. O índice de remanescente adesivo (IRA) e a rugosidade da superfície foram mensurados nas réplicas dentais e os dados foram avaliados estatisticamente por Mann-Whitney e teste t pareado, respectivamente. Não ocorreu descolagem de braquetes durante os períodos de tratamento dos pacientes. Verificou-se que os valores do IRA dos dois incisivos centrais superiores foram semelhantes (p = 0,665). Para ambos os materiais de colagem, o valor de IRA predominante foi 3. Após o polimento, a rugosidade da superfície do esmalte foi semelhante nos grupos compósito (0,245 μm) e CIVMR (0,248 μm) (p = 0,07). Em ambos os grupos, os valores de rugosidade da superfície do esmalte foram significativamente menores após o polimento em comparação com a condição inicial (p <0,001). CIVMR promoveu eficiência na colagem de braquetes sem falhas durante o tratamento; a escolha dos materiais compósito ou CIVMR não foi um fator que influenciou na rugosidade da superfície do esmalte, porém, o polimento levou a superfícies mais lisas do que as encontradas no início do tratamento.

RESUMO

The aim of this study was to compare the microshear bond strength of different resin cements to CAD/CAM-created lithium disilicate ceramics after 24 hours and after 1 year (10,000 thermocycles). Forty (40) ceramic bars were subjected to pretreatment comprising airborne abrasion with aluminum oxide particles, etching with 10% hydrofluoric acid and Monobond N application. Bars were divided into 4 groups (n = 10), based on cement type: light-cured Variolink Esthetic LC (VLC) and dual-cured Variolink N (VN) at two different times: after 24 hours and after 1 year. Silicone molds were used to prepare cement cylinders on a ceramic surface. The set was stored in distilled water at 37ºC, for 24 hours or subjected to 10,000 thermocycles. The molds were removed and microshear bond strength was tested. Data were submitted to two-way analysis of variance and Tukey's test (α = 0.05). Based on the comparison between cement values at different aging times (p = 0.035), VN after 24 hours (27.10 ± 0.92) and after 1 year (20.62 ± 1.25) presented significantly higher values than VLC after 24 hours (14.79 ± 0.76) and after 1 year (6.61 ± 0.81). Bond strength recorded for both cements after 24 hours (VN: 27.10 ± 0.92 and VLC: 14.79 ± 0.76) was significantly higher than the one recorded after 1 year (VN: 20.62 ± 1.25 and VLC: 6.61 ± 0.81). The thermocycling reduced the values observed for both investigated cements; bond strength was greater for dual-cure resin cement than for light-cured resin cement.

O objetivo nesse estudo foi comparar a resistência de união de diferentes cimentos resinosos à cerâmica de dissilicato de lítio processada por CAD/CAM após 24 horas e após 1 ano (10.000 termociclos). Foram utilizadas 40 barras cerâmicas com tratamento prévio por jateamento com óxido de alumínio, condicionamento com ácido fluorídrico 10% e aplicação do Monobond N. As barras foram divididas em 4 grupos (n=10) de acordo com o tipo de cimento: fotopolimerizável Variolink Esthetic LC (VLC) e dual Variolink N (VN) em diferentes tempos: após 24 horas e 1 ano. Matrizes de silicone foram usadas para preparar cilindros de cimento na superfície cerâmica. O conjunto foi armazenado em água destilada a 37ºC por 24 horas ou submetidos protocolo de termociclagem com 10.000 ciclos. As matrizes foram removidas e o teste de microcisalhamento realizado. Os dados foram avaliados por análise de variância a dois fatores e teste de Tukey (α=0,05). Ao comparar os valores dos cimentos em diferentes tempos de envelhecimento (p=0,035), observou-se que VN, após 24 horas (27,10 ± 0,92) e 1 ano (20,62 ± 1,25) apresentou valores significativamente superior a VLC após 24 horas (14,79 ± 0,76) e 1 ano (6,61 ± 0,81). A resistência para ambos os cimentos após 24 horas (VN: 27,10 ± 0,92 e VLC: 14,79 ± 0,76) foi significativamente superior que 1 ano (VN: 20,62 ± 1,25 e VLC: 6,61 ± 0,81). A termociclagem promoveu diminuição nos valores de ambos os cimentos estudados e o cimento resinoso dual mostrou maior resistência de união que o cimento resinoso fotopolimerizável.

Assuntos