RESUMO
In the present work, reduced graphene oxide was obtained by green synthesis, using extracts of Larrea tridentata (gobernadora) and Capsicum Chinense (habanero). Graphene oxide was synthesized by the modified Hummers' method and subsequently reduced using natural extracts to obtain a stable and environmentally friendly graphene precursor. Consequently, the gobernadora aqueous extract was found to have a better reducing power than the habanero aqueous extract. This opportunity for green synthesis allows the application of RGO in photocatalysis for the degradation of the methylene blue dye. Degradation efficiencies of 60% and 90% were obtained with these materials.
RESUMO
In this study, (1 - x) BFO-xCFO (CFO, x = 0.00, 0.05, 0.10 and 0.30) ceramics were synthesized by a solid-state reaction method; their compositions were driven by structural, microstructural, vibrational, electrical, magnetic properties; their enhanced magneto capacitance (MC) effect have also been carried out. Reitveld refinement studies of X-ray diffraction data shows composition-driven structural phase transformation from rhombohedral (R3c) to tetragonal (P4mm). Two phonon scattering Raman modes were observed for the higher wavenumber which supports the crystal structural transition in the BFO-CFO. Ferroelectric polarization shows that the polarization increased with increasing CFO concentration, which describes the changes of the polar symmetry of the crystal structure from rhombohedral (R3c) to tetragonal (P4mm). In Further, the maximum efficiency of energy density (η = 68.65%), reversible energy density of 0.138 J/cm3 and the strong magneto capacitance was observed in 0.9BFO-0.1CFO, which belongs to the morphotropic phase boundary (MPB) region near to the BiFeO3-rich region. The magnetic response analysis has shown, the saturation magnetization (Ms) values of 83 emu/gm and 139 emu/gm for pure CFO and 0.7BFO-0.3CFO composite, respectively, and their magnetic behaviours were also confirmed with Arrott-Belov-Kouvel (ABK) plot.