RESUMO
OBJECTIVES: To evaluate the effect of framework design on the fatigue life and failure modes of metal ceramic (MC, Ni-Cr alloy core, VMK 95 porcelain veneer), glass-infiltrated alumina (ICA, In-Ceram Alumina/VM7), and veneered yttria-stabilized tetragonal zirconia polycrystals (Y-TZP, IPSe.max ZirCAD/IPS e.max,) crowns. METHODS: Sixty composite resin tooth replicas of a prepared maxillary first molar were produced to receive crowns systems of a standard (MCs, ICAs, and Y-TZPs, n=10 each) or a modified framework design (MCm, ICAm, and Y-TZPm, n=10 each). Fatigue loading was delivered with a spherical steel indenter (3.18mm radius) on the center of the occlusal surface using r-ratio fatigue (30-300N) until completion of 10(6) cycles or failure. Fatigue was interrupted every 125,000 cycles for damage evaluation. Weibull distribution fits and contour plots were used for examining differences between groups. Failure mode was evaluated by light polarized and SEM microscopy. RESULTS: Weibull analysis showed the highest fatigue life for MC crowns regardless of framework design. No significant difference (confidence bound overlaps) was observed between ICA and Y-TZP with or without framework design modification. Y-TZPm crowns presented fatigue life in the range of MC crowns. No porcelain veneer fracture was observed in the MC groups, whereas ICAs presented bulk fracture and ICAm failed mainly through the veneer. Y-TZP crowns failed through chipping within the veneer, without core fractures. CONCLUSIONS: Framework design modification did not improve the fatigue life of the crown systems investigated. Y-TZPm crowns showed comparable fatigue life to MC groups. Failure mode varied according to crown system.
Assuntos
Desenho Assistido por Computador , Coroas , Planejamento de Prótese Dentária , Falha de Restauração Dentária , Facetas Dentárias , Óxido de Alumínio , Bis-Fenol A-Glicidil Metacrilato , Ligas de Cromo , Porcelana Dentária , Manequins , Ligas Metalo-Cerâmicas , Polietilenoglicóis , Ácidos Polimetacrílicos , Distribuição Aleatória , Cimentos de Resina , Análise de Sobrevida , Ítrio , ZircônioRESUMO
OBJECTIVES: This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue. METHODS: Forty-two Y-TZP plates (12mm x 12mm x 0.5mm) veneered with pressable porcelain (12mm x 12mm x 1.2mm) and adhesively luted to water aged composite resin blocks (12mm x 12mm x 4mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n=3). Fatigue loading was delivered on specimen either on axial (n=18) or off-axis 30 degrees angulation (n=18) to simulate posterior tooth cusp inclination creating a 0.7mm slide. Single load and fatigue tests utilized a 6.25mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200N (90% CB) were calculated. RESULTS: The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed. CONCLUSIONS: Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer.