RESUMO

OBJECTIVES: Controversy exists about whether the elastic modulus (E) mismatch between the loading indenter and ceramic materials influences fatigue testing results. The research hypotheses were that for porcelain veneered Y-TZP crowns 1) A low modulus Steatite indenter (SB) leads to higher fatigue reliability compared to a high modulus tungsten carbide indenter (WC); 2) Different surface damage patterns are expected between low and high modulus indenters after sliding contact fatigue testing. All ceramic crowns will exhibit similar step-stress accelerated life testing (SSALT) contact fatigue reliability (hypothesis 1) and failure characteristics (hypothesis 2) when using high stiffness tungsten carbide (WC, E = 600 GPa) vs. enamel like steatite (SB, E = 90 GPa) indenters. METHODS: Manufacturer (3M Oral Care) prepared Y-TZP-veneered all-ceramic molar crowns were bonded to aged resin composite reproductions of a standard tooth preparation and subjected to mouth-motion SSALT fatigue (n = 18 per indenter type). Failure was defined either as initial inner cone crack (IC), or final fracture (FF) when porcelain fractured (chipping). Selected IC specimens that did not progress to FF were embedded in epoxy resin and sectioned for fractographic analysis. RESULTS: The distribution of failures across the load and cycle profiles lead to similar calculated Weibull Use Level Probability Plots with overlap of the 2-sided 90% confidence bounds. The calculated reliability for IC and FF was equivalent at a mission of 300 N or 700 N load and 50,000 cycles, although the WC indenter had a trend for lower reliability for IC at 700 N. Both indenters produced similar patterns of wear and cracking on crown surfaces. Fractographic landmarks showed competing failure modes, but sliding contact partial inner cone cracks were the most dominant for both groups. SIGNIFICANCE: The more compliant Steatite indenter had similar veneered crown fatigue reliability and failure modes to those found with use of a high stiffness tungsten carbide indenter (hypotheses 1 and 2 rejected).

Assuntos

RESUMO

OBJECTIVE: To evaluate the probability of survival of monolithic and porcelain veneered lithium disilicate crowns comprised by a conventional or modified core when loaded on marginal ridges. METHODS: Lithium disilicate molar crowns (n=30) were fabricated to be tested at mesial and distal marginal ridges and were divided as follows: (1) bilayered crowns with even-thickness 0.5mm framework (Bi-EV); (2) bilayered crowns with modified core design (Bi-M-lingual collar connected to proximal struts), and: (3) monolithic crowns (MON). After adhesively cemented onto composite-resin prepared replicas, mesial and distal marginal ridges of each crown (n=20) were individually cyclic loaded in water (30-300N) with a ceramic indenter at 2Hz until fracture. The 2-parameter Weibull was used to calculate the probability of survival (reliability) (90% 2-sided confidence bounds) at 1, 2, and 3 million cycles and mean life. RESULTS: The reliability at 1 and 2 million cycles was significantly higher for MON (47% and 19%) compared to Bi-EV (20% and 4%) and Bi-M (17% and 2%). No statistical difference was found between bilayered groups. Only the MON group presented crown survival (7%) at 3 million cycles. The mean life was highest for MON (1.73E+06), lowest for Bi-M (573,384) and intermediate for Bi-E (619,774). Fractographic analysis showed that the fracture originated at the occlusal surface. The highest reliability was found for MON crowns. The modified framework design did not improve the fatigue life of crowns. SIGNIFICANCE: Monolithic lithium disilicate crowns presented higher probability of survival and mean life than bilayered crowns with modified framework design when loaded at marginal ridges.

Assuntos

RESUMO

OBJECTIVE: To compare the fatigue life and damage modes of zirconia crowns fabricated with and without framework design modification when porcelain veneered using a fast or slow cooling protocol. METHODS: Composite resin replicas of a first molar full crown preparation were fabricated. Zirconia copings were milled as conventional (0.5mm even thickness, Zr-C, n=20,) or modified (lingual margin of 1.0mm thickness, 2.0mm height connected to two proximal struts of 3.5mm height, Zr-M, n=20). These groups were subdivided (n=10 each) according to the veneer cooling protocol employed: fast cooling (Zr-CFast and Zr-MFast) and slow cooling (Zr-CSlow and Zr-MSlow). Crowns were cemented and fatigued for 10(6) cycles in water. The number of cycles to failure was recorded and used to determine the interval databased 2-parameter probability Weibull distribution parameter Beta (ß) and characteristic life value Eta (η). RESULTS: 2-parameter Weibull calculation presented ß=5.53 and ß=4.38 for Zr-MFast and Zr-CFast, respectively. Slow cooled crowns did not fail by completion of 10(6) cycles, thereby Weibayes calculation was applied. Increased fatigue life was observed for slow cooled crowns compared to fast cooled ones. Groups Zr-MFast and Zr-MSlow presented no statistical difference. Porcelain cohesive fractures were mainly observed in fast cooled groups. Slow cooled crowns presented in some instances inner cone cracks not reaching the zirconia/veneer interface. SIGNIFICANCE: Improved fatigue life in tandem with the absence of porcelain fractures were observed in slow cooled crowns, regardless of framework design. Crowns fast cooled chiefly failed by porcelain cohesive fractures.

Assuntos

RESUMO

Hypodontia is the congenital absence of one or more teeth and may affect permanent teeth. Several options are indicated to treat hypodontia, including the maintenance of primary teeth or space redistribution for restorative treatment with partial adhesive bridges, tooth transplantation, and implants. However, a multidisciplinary approach is the most important requirement for the ideal treatment of hypodontia. This paper describes a multidisciplinary treatment plan for congenitally missing permanent mandibular second premolars involving orthodontics, implantology and prosthodontic specialties.

Assuntos

RESUMO

Hypodontia is the congenital absence of one or more teeth and may affect permanent teeth. Several options are indicated to treat hypodontia, including the maintenance of primary teeth or space redistribution for restorative treatment with partial adhesive bridges, tooth transplantation, and implants. However, a multidisciplinary approach is the most important requirement for the ideal treatment of hypodontia. This paper describes a multidisciplinary treatment plan for congenitally missing permanent mandibular second premolars involving orthodontics, implantology and prosthodontic specialties.

Assuntos

RESUMO

To evaluate the sealing capability of external hexagon implant systems and assess the marginal fit, two groups (n = 10 each) were employed: SIN (Sistema de Implantes Nacional, Brazil) and Osseotite, (Biomet 3i, USA). Sealing capability was determined by placing 0.7 µL of 1% acid-red solution in the implant wells before the torque of their respective abutments. Specimens were then placed into 2.5 mL vials filled with 1.3 mL of distilled water with the implant-abutment interface submerged. Three samples of 100 µL water were collected at previously determinate times. The absorbance was measured with a spectrophotometer, and the data were analyzed by Two-way ANOVA (P < .05) and Tukey's test. Marginal fit was determined using SEM. Leakage was observed for both groups at all times and was significantly higher at 144 hrs. SEM analysis depicted gaps in the implant-abutment interface of both groups. Gaps in the implant-abutment interface were observed along with leakage increased at the 144 hrs evaluation period.

RESUMO

OBJECTIVES: To evaluate the effect of framework design on the fatigue life and failure modes of metal ceramic (MC, Ni-Cr alloy core, VMK 95 porcelain veneer), glass-infiltrated alumina (ICA, In-Ceram Alumina/VM7), and veneered yttria-stabilized tetragonal zirconia polycrystals (Y-TZP, IPSe.max ZirCAD/IPS e.max,) crowns. METHODS: Sixty composite resin tooth replicas of a prepared maxillary first molar were produced to receive crowns systems of a standard (MCs, ICAs, and Y-TZPs, n=10 each) or a modified framework design (MCm, ICAm, and Y-TZPm, n=10 each). Fatigue loading was delivered with a spherical steel indenter (3.18mm radius) on the center of the occlusal surface using r-ratio fatigue (30-300N) until completion of 10(6) cycles or failure. Fatigue was interrupted every 125,000 cycles for damage evaluation. Weibull distribution fits and contour plots were used for examining differences between groups. Failure mode was evaluated by light polarized and SEM microscopy. RESULTS: Weibull analysis showed the highest fatigue life for MC crowns regardless of framework design. No significant difference (confidence bound overlaps) was observed between ICA and Y-TZP with or without framework design modification. Y-TZPm crowns presented fatigue life in the range of MC crowns. No porcelain veneer fracture was observed in the MC groups, whereas ICAs presented bulk fracture and ICAm failed mainly through the veneer. Y-TZP crowns failed through chipping within the veneer, without core fractures. CONCLUSIONS: Framework design modification did not improve the fatigue life of the crown systems investigated. Y-TZPm crowns showed comparable fatigue life to MC groups. Failure mode varied according to crown system.

Assuntos