RESUMO
Abstract Objective: To compare porcelain and metal repair done with both nanocomposite and conventional composite. Material and Methods: A total of 30 cylinders were fabricated from Porcelain (I), Porcelain fused to metal (II), and metal (III) substrate each. Control group (A) was bonded with conventional micro-hybrid composite and experimental group (B) was bonded with nanocomposite in a 2 mm thickness. All specimens were thermocycled and stored in distilled water at 37 °C for 7 days. A universal testing machine was used to measure the Shear bond strength (SBS). The difference between bond strengths of the groups was compared using an independent t-test. Results: In all three groups, the SBS was higher in the experimental group as compared to the control group. The use of nanocomposite of metal alloy presented maximum shear bond strength, followed by samples of porcelain fused to metal and finally porcelain, showing the lowest values of SBS. Conclusion: Porcelain and alloys bonded with nanocomposite exhibit enhanced adhesiveness as well as aesthetic and mechanical properties. This subsequently would translate into providing higher clinical serviceability and durability and hence a cost-effective and accessible repair option for human welfare (AU).
Assuntos
Resistência ao Cisalhamento , Porcelana Dentária , Nanoestruturas/química , Nanocompostos/química , Análise de Variância , Ligas DentáriasRESUMO
Aminodextran (AMD) polymer was prepared via chemical grafting of hexamethylenediamine on oxidized dextran. Magnetic latex particles were successfully obtained by adsorption of positively charged AMD on negatively charged submicron magnetic emulsion. The adsorbed amount was found to be ranged from 20 to 1280mg of AMD per gram of dried magnetic dispersion. The AMD-coated magnetic emulsions were characterized by positive zeta potential in the pH range from 3 to 9 compared to bare seed magnetic emulsion. All the samples showed to be superparamagnetic property, even after the adsorption of the polymer. The developed magnetic submicron particles exhibited good potential for in vivo biomedical diagnosis applications as demonstrated by their higher T2 contrast-ability compared to Gd in magnetic resonance imaging (MRI) and hyperthermia.