RESUMO
PURPOSE: The objective of this in vitro study was to evaluate the influence of ceramic thickness and pre-heating of luting agents on their physical properties. MATERIALS AND METHODS: The materials RelyX Arc, RelyX Ultimate, RelyX Veneer, and Filtek Z350 Flow were handled at different temperatures (23°C or 54°C), inserted into matrix, and photoactivated through ceramic disks (0.75 mm or 1.5 mm). The following tests were performed ( n=8): degree of conversion, Knoop Hardness, cross-link density, water sorption, solubility, and ultimate tensile strength. Data were analyzed using three-way analysis of variance and Tukey's test (α=0.05). RESULTS: Regarding ceramic thickness, the thinnest ceramic resulted in higher values of Knoop Hardness ( p=0.027). The lowest temperature (23°C) resulted in a higher solubility ( p=0.0257), and water sorption ( p=0.0229) values. There was also statistical difference among the materials: RelyX Arc showed a higher degree of conversion and ultimate tensile strength, followed by RelyX Veneer, RelyX Ultimate, and Filtek Z350 Flow. For Knoop Hardness and cross-link density tests, RelyX Ultimate showed the highest values, followed by RelyX Arc, RelyX Veneer, and Filtek Z350 Flow. For water sorption and solubility, RelyX Veneer showed the highest values, followed by RelyX Arc, RelyX Ultimate, and Filtek Z350 Flow. CONCLUSION: Pre-heating interfered with water sorption and solubility, whereas ceramic thickness only affected Knoop Hardness; the physical properties of the materials are dependent on their composition.
Assuntos
Cimentos Dentários/química , Cemento Dentário/química , Bis-Fenol A-Glicidil Metacrilato/química , Cimentação , Resinas Compostas/química , Porcelana Dentária/química , Dureza , Calefação , Humanos , Fenômenos Mecânicos , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Solubilidade , Propriedades de Superfície , Temperatura , ÁguaRESUMO
AIM: To evaluate the push-out bond strength (BS) of direct anatomic posts (DAPs) and conventional fiber posts (CFPs) cemented with different luting agents in different thirds of flared root canals. MATERIALS AND METHODS: A total of 60 human single-rooted canine teeth were transversally sectioned 16 mm from the radicular apex. After endodontic treatment, canals were flared with diamond burs. Samples were divided into six groups according to post type and luting agent: DAP and RelyX U100 (RXU); DAP and RelyX ARC (RXA); DAP and RelyX Luting 2 (RXL); CFP and RXU; CFP and RXA; CFP and RXL. Roots were sectioned transversely into six 1-mm-thick slices. The push-out test was performed and failure modes were observed. RESULTS: The DAP groups (7.23 ± 2.05) showed highest BS values (p < 0.05) when compared with CFP (5.93 ± 1.76). RelyX U100 (8.17 ± 1.70) showed higher BS values (p < 0.05) than RXA (6.46 ± 1.38), and RXL (5.10 ± 1.65) showed the lowest values. Bond strength on the apical third was statistically lower (p < 0.05) than that on the other thirds of the root canals. There was a predominance of adhesive failure for all groups. CONCLUSION: The DAPs improved retention in flared root canals, and RXU was the most effective luting agent. The apical third showed the lowest BS values. CLINICAL SIGNIFICANCE: The relining procedure of fiber posts with composite and the proper selection of luting resin cement are important for increasing bonding effectiveness in flared root canals.