RESUMO
Objective: To evaluate the effect of different irrigation solutions prior to post cementation on the resin bonding to bovine root dentine. Material and Methods: 60 bovine roots (16 mm) were prepared to 12 mm with specific drill of a double-tapered fiber post system, included in PMMA, and divided into 6 groups, considering the irrigation solutions (IS) prior to cementation: Gr1- saline solution (control), Gr2- NaOCl 0.5 %, Gr3- NaOCl 1 %, Gr4- NaOCl 2.5 %, Gr5- NaOCl 5 %, Gr6- Chlorexidine 2 % (solution). The root canals were irrigated with IS 20 ml during 10 min. Then they were rinsed with 20 ml of distilled water and dried with paper points. One fiber post was molded with polyvinylsiloxane and 60 posts made of resin cement (PRC) were obtained moments before the cementation. The root canal dentin was etched with H2PO3 37 %/15 s + washing/drying, a multi-bottle etch&rinse adhesive system was applied and the PRC were resin luted with dual resin cement (DuolinkTM, Bisco). Each specimen was cut into 4 slices of ±1.8mm in thickness and submitted to push-out test (1 mm/min). Results: ANOVA showed that bond strength was significantly affected by IS (P < 0.0001). The highest bond strengths (MPa) were those for the groups 4 (3.51 ± 1.52) and 5 (3.0 ± 1.16). The groups 1 (0.70 ± 0.30), 2 (0.80 ± 0.24), 3 (1.26 ± 0.57) and 6 (0.90 ± 0.41) were statistically similar to each other. Conclusion: The resin bonding to the root dentine was higher when higher concentrations of hypochlorite solutions were used. (AU)
Objetivo: Avaliar o efeito de diferentes soluções de irrigação antes da cimentação do pino na resistência de união da resina à dentina radicular bovina. Material e Métodos: Foram preparadas 60 raízes bovinas (16 mm) a 12 mm com broca específica de um sistema de pino de fibra com dupla conicidade, incluídas no PMMA, e divididas em 6 grupos, considerando as soluções irrigadoras (IS) antes da cimentação: Gr1-Solução salina (controle), Gr2-NaOCl 0,5 %, Gr3-NaOCl 1 %, Gr4-NaOCl 2,5 %, Gr5-NaOCl 5 %, Gr6-Clorexidina 2 % (solução). Os canais radiculares foram irrigados com 20 ml de IS durante 10 min. Depois, foram lavados com 20 ml de água destilada e secos com pontas de papel. Um pino de fibra foi moldado com polivinilsiloxano e 60 pinos de cimento resinoso (PRC) foram obtidos momentos antes da cimentação. A dentina radicular foi condicionada com H2PO3 37 %/15 s + lavagem/ secagem, aplicou-se o sistema de adesivo e o PRC foi cimentado com cimento resinoso dual (DuolinkTM, Bisco). Cada amostra foi cortada em 4 fatias de ± 1,8 mm de espessura e submetida a teste push-out (1 mm/ min). Resultados: ANOVA mostrou que a força de união foi significativamente afetada pelo IS (P< 0,0001). As maiores resistências de união (MPa) foram para os grupos 4 (3,51 ± 1,52) e 5 (3,0 ± 1,16). Os grupos 1 (0,70 ± 0,30), 2 (0,80 ± 0,24), 3 (1,26 ± 0,57) e 6 (0,90 ± 0,41) foram estatisticamente semelhantes entre si. Conclusão: A resistência de união da resina à dentina radicular foi maior quando foram utilizadas concentrações maiores de soluções de hipoclorito. (AU)
Assuntos
Animais , Bovinos , Dentina , Cimentos de ResinaRESUMO
BACKGROUND: The aim of this study was to evaluate, by means of pull-out test, the bond strength of fiberglass posts when cemented with different lengths in endodontically treated teeth. MATERIALS AND METHODS: Sixty single-rooted bovine roots were cut in the cementoenamel junction with 21 mm length. They were endodontically treated and randomly divided into three groups (n = 20). Group 1 - Preparation of 2/3 of the remaining roots; Group 2 - Preparation of ½ of the remaining roots and Group 3 - Preparation of » of remaining roots. For all groups it were used posts n = 3 (Exacto, Angelus, Brazil), and cemented with self-etching resin cement (RelyXU200). After cementing posts, the samples were thermocycled (10.000 cycles/5°C and 55°C). The pull-out test was performed on a universal testing machine (EMIC - DL500) and the values obtained were statistically analyzed by analysis of variance (one-factor ANOVA) and multiple comparison test of Tukey, with level of significance of 5%. RESULTS: The mean values ± standard deviation in Newtons (N) were: Group 1 = 120.5 (±42.8) A, Group 2 = 103.1 (±31.2) AB, Group 3 = 41.2 (±22.4) C, P < 0.005. CONCLUSION: The preparation of ½ of remaining root appears to be a viable alternative when 2/3 of the preparation of the remaining root is not possible, but more results are needed for clinical validation.
RESUMO
A proposta deste estudo foi avaliar a adaptação de barras metálicas confeccionadas por técnica de moldeira aberta com união dos transferentes em diferentes resinas acrílicas. Foi utilizada uma mandíbula acrílica (modelo-mestre) com três implantes (Neodent/4.1HE) simetricamente posicionados com os respectivos minipilares cônicos. Sobre os minipilares foram posicionados transferentes de moldeira aberta, os quais foram unidos com fio dental e com os seguintes materiais: G1: resina bisacrílica autopolimerizável Structur 2 SC (VOCO GMBH, Alemanha); G2: resina acrílica Pattern (GC América Inc., Alsip, IL); G3: resina acrílica Duralay (Reliance Dental MFG Company,USA); G4: resina acrílica Dencrilay Speed (Dencril Brasil); G5: resina acrílica JET (Artigos Odontológicos Clássico LTDA, Brasil). Foram realizadas 10 esplintagens por grupo (n=10) e obtidos corpos-de-prova (cp) em gesso especial tipo IV melhorado. A barra, previamente confeccionada sobre o modelo mestre através do sistema de barra cimentada e sem soldas, foi adaptada sobre os análogos e realizadas 18 leituras por cp. As análises de desadaptação (µm) foram realizadas em microscópio óptico (Mitutoyo TM-500) com aumento de 30x. Os resultados obtidos foram analisados por meio do teste de ANOVA 1-fator (a=1%) e Teste de Múltipla Comparação de Tukey. Valores de média e desvio-padrão foram os seguintes: G1 23,945±5,53a; G2 19,49±6,43a; G3 16,50±0,86a; G4 41,33±24,82a e G5 - 264,12±141,71b. Conclui-se que os grupos G1, G2, G3 E G4 apresentaram melhor adaptação da barra metálica sobre implantes
Assuntos
Resinas Acrílicas , Implantação Dentária , Técnica de Moldagem Odontológica , Materiais Dentários , Teste de MateriaisRESUMO
O objetivo do presente trabalho foi comparar a presença ou ausência de harmonia do sorriso entre homens e mulheres, tendo os parâmetros dentários e periodontais em consideração. Para esse estudo, foram selecionados 42 voluntários, sendo 21 do sexo feminino e 21 do sexo masculino.Após a realização de tomadas fotográfcas do sorriso, dentes e gengiva, os pacientes foram avaliados de acordo com os seguintes parâmetros: 1) biótipo periodontal; 2) altura do sorriso; 3) abertura do sorriso; 4) espessura do lábio; 5) comprimento e largura da coroa dentária; 6) formato do dente; 7) posição do zênite gengival; 8) posição do ponto de contato; 9) altura da gengiva bilateral; 10) altura e largura da papila interdentária; 11) presença ou ausência de proporção áurea. Após análise estatística de cada parâmetro clínico avaliado, com o teste t, e considerando p<0,05, foi possível notar que a maioria das características analisadas nos pacientes não apresentou diferença estatisticamente signifcativa entre os grupos feminino e masculino. Além disso, pôde- -se concluir que para um resultado estético satisfatório, tanto para o paciente quanto para o profssional, é indispensável a harmonia entre os tecidos dentário e periodontal.
This aim of this study was to clinically evaluate the presence or absence of smile harmony, considering dental and periodontal parameters. For this study 42 patients were selected, 21 females and 21 males. Photographs were taken from the smile, teeth and gingiva of the patients. They were evaluated in accordance with the following parameters: 1) Periodontal biotype, 2) smile height, 3) smile opening, 4) thickness of the lip, 5) length and width of the tooth, 6) format of the tooth, 7) position of the gingival zenith, 8) position of the contact point; 9) bilateral height of gingiva; 10) height and width of the interdental papilla, 11) presence or absence of golden proportion. After statistical analysis of each group, with the t-test and considering the p-value <0.05, it was clear that most of the variables analyzed in the patients did not show a statistically signifcant difference between female and male groups. Furthermore, for a satisfactory fnal result for both patient and professional, it is essential the harmony between the dental and periodontal tissues.
Assuntos
Humanos , Masculino , Feminino , Prótese Dentária , Estética Dentária , SorrisoRESUMO
Justificativa: estudos epidemiológicos sugerem aumento de evidências de que infecções crônicas, como periodontite, com seu mecanismo inflamatório, desempenham papéis importantes na formação de placa aterosclerótica e doença cardiovascular, principalmente pelo aumento dos níveis de proteína C-reatlva (PCR). Desta forma, o objetivo do presente estudo foi avaliar se a presença de periodontite crônica e seu subsequente tratamento podem alterar os níveis séricos de PCR. Métodos: foram selecionados 15 pacientes saudáveis do grupo controle e 15 pacientes com doença periodontal que foram submetidos a exames de proteína C-reativa ultrassensível, imediatamente antes do início e após o tratamento periodontal não cirúrgico de raspagem e alisamento radiculares. A determinação quantitativa da PCR ultrassensível foi realizada no soro humano através do método de turbidimetria. Resultados: o valor médio dos níveis de PCR encontrados nos indivíduos foi de 0,57 mg/L para o grupo controle, 2,45 mg/L e 0,44 mg/L para o grupo teste antes e após o tratamento periodontal, respectivamente. Conclusão: os resultados encontrados indicam que a doença periodontal promove aumento nos níveis de PCR e que o seu tratamento pode causar diminuição dessa proteína, podendo ser um meio de diminuir o risco para doença cardiovascular.
Assuntos
Humanos , Doenças Cardiovasculares , Técnicas de Diagnóstico Cardiovascular , PeriodontiteRESUMO
Neste estudo avaliou-se a influência do tratamento de superfície para cimentação na resistência à flexão de 4 pontos de zircônia tetragonal poli cristalina estabilizada por óxido de ítrio (Y-TZP). Por meio de blocos pré-sinterizados de Y-TZP (InCeram 2000 YZ Cubes, Vita Zahnfabrik) foram confeccionadas 120 barras (20mm x 4mm x 1,2mm) de acordo com a norma ISO 6872:2008 e aleatoriamente divididas em 4 grupos: Grupo 1: silicatização (Cojet 30 μm) (n=29); Grupo 2: jateamento com óxido de alumínio (44 μm) (n=29); Grupo 3: ponta diamantada de granulação extra-fina (30 μm) (n=27); Grupo 4: (controle) sem tratamento de superfície (n=29). Em seguida, todas as amostras foram submetidas ao ensaio de flexão de 4 pontos (imersos em água destilada à 370C) em máquina de ensaio universal com velocidade de 0,5 mm/min até o rompimento das mesmas. A análise de difração de raios-X foi utilizada para determinar a transformação de fase. A microestrutura da Y-TZP e o padrão de tratamento de superfície foram analisados por meio de perfilometria óptica e microscopia eletrônica de varredura. Os dados de resistência à flexão foram estatisticamente analisados por meio de ANOVA 1-fator, teste de Tukey HSD (α=0,05) e Weibull (m=módulo; σ0=resistência característica). As médias±desvio-padrão (MPa) foram os seguintes: G1:1207,1±229,7a; G2: 1369,7±272,3a; G3: 874,4±365,4b e G4: 1196,2±284,2a. Os valores de (m) e (σ0) foram: G1: 6,0 e 1300,28; G2: 5,9 e 1477,88; G3: 2,6 e 985,901 e G4: 4,5 e 1308,12. Concluiu-se que a utilização de pontas diamantadas de granulação extra-fina deve ser evitada nos procedimentos prévios à cimentação resinosa de Y-TZP.
This study evaluated the influence of surface treatment on 4-point bending test of yttrium stabilized poli cristaline tetragonal zirconia (Y-TZP). From Y-TZP blocks (InCeram 2000 YZ Cubes, Vita Zahnfabrik) were obtained 120 bars (20mm×4mm×1.2mm) according to norm ISO 6872:2008 and randomly divided in 4 groups: Group 1: silicatization (Cojet 30 μm) (n=29); Group 2: sandblasting with aluminium oxide (44 μm) (n=29); Group 3: fine coarse diamond bur (30 μm) (n=27); Group 4: (control) without surface treatment (n=29). As follow, all samples were submitted to the 4-point bending test (immersed in distilled water at 370C) in an universal testing machine with cross-head speed of 0.5 mm/min until the rupture of the samples. X-ray diffraction analysis was utilized to quantify the monoclinic phase. The microstructure of Y-TZP and pattern of surface treatment were analyzed by optic profilometer and scanning electron microscopy. The data of flexural strength (σ4p) were statistically analyzed by 1-factor ANOVA, Tukey HSD (α= 0.05) and Weibull (m= modulus, σ0 = characteristic strength). The mean±standard deviation (MPa) were the following: G1:1207.1±229.7a; G2: 1369.7±272.3a; G3: 874.4±365.4b and G4: 1196.2±284.2a. The values of (m) and (σ0) were: G1: 6.0 and 1300.28; G2: 5.9 and 1477.88; G3: 2.6 and 985.901 and G4: 4.5 and 1308.12. It was concluded that silicatization and sandblasting increased the flexural strength of Y-TZP, diminished the roughness of surface and present higher reliability for cementation of Y-TZP restorations.
Assuntos
Abrasão Dental por Ar , Materiais Dentários , Ciência dos Materiais , Microscopia Eletrônica de Varredura , Propriedades de SuperfícieRESUMO
OBJECTIVES: The aim of this study was to evaluate the intrapulpal temperature variation after bleaching treatment with 35% hydrogen peroxide using different sources of activation. MATERIAL AND METHODS: Twenty-four human teeth were sectioned in the mesiodistal direction providing 48 specimens, and were divided into 4 groups (n=12): (G1) Control - Bleaching gel without light activation, (G2) Bleaching gel + halogen light, (G3) Bleaching gel + LED, (G4) Bleaching gel + Nd:YAG Laser. The temperatures were recorded using a digital thermometer at 4 time points: before bleaching gel application, 1 min after bleaching gel application, during activation of the bleaching gel, and after the bleaching agent turned from a dark-red into a clear gel. Data were analyzed statistically by the Dunnet's test, ANOVA and Tukey's test (a=0.05). RESULTS: The mean intrapulpal temperature values ( degrees C) in the groups were: G1: 0.617 +/- 0.41; G2: 1.800 +/- 0.68; G3: 0.975 +/- 0.51; and G4: 4.325 +/- 1.09. The mean maximum temperature variation (MTV) values were: 1.5 degrees C (G1), 2.9 degrees C (G2), 1.7 degrees C (G3) and 6.9 degrees C (G4). When comparing the experimental groups to the control group, G3 was not statistically different from G1 (p>0.05), but G2 and G4 presented significantly higher (p<0.05) intrapulpal temperatures and MTV. The three experimental groups differed significantly (p<0.05) from each other. CONCLUSIONS: The Nd:YAG laser was the activation method that presented the highest values of intrapulpal temperature variation when compared with LED and halogen light. The group activated by LED light presented the lowest values of temperature variation, which were similar to that of the control group.
Assuntos
Temperatura Corporal/efeitos dos fármacos , Polpa Dentária/efeitos dos fármacos , Peróxido de Hidrogênio/uso terapêutico , Luz , Oxidantes/uso terapêutico , Clareamento Dental/métodos , Géis , Humanos , Peróxido de Hidrogênio/administração & dosagem , Peróxido de Hidrogênio/efeitos da radiação , Lasers de Estado Sólido/uso terapêutico , Iluminação/instrumentação , Teste de Materiais , Oxidantes/administração & dosagem , Oxidantes/efeitos da radiação , Termômetros , Fatores de TempoRESUMO
OBJECTIVES: The aim of this study was to evaluate the intrapulpal temperature variation after bleaching treatment with 35 percent hydrogen peroxide using different sources of activation. MATERIAL AND METHODS: Twenty-four human teeth were sectioned in the mesiodistal direction providing 48 specimens, and were divided into 4 groups (n=12): (G1) Control - Bleaching gel without light activation, (G2) Bleaching gel + halogen light, (G3) Bleaching gel + LED, (G4) Bleaching gel + Nd:YAG Laser. The temperatures were recorded using a digital thermometer at 4 time points: before bleaching gel application, 1 min after bleaching gel application, during activation of the bleaching gel, and after the bleaching agent turned from a dark-red into a clear gel. Data were analyzed statistically by the Dunnet's test, ANOVA and Tukey's test (a=0.05). RESULTS: The mean intrapulpal temperature values (ºC) in the groups were: G1: 0.617 ± 0.41; G2: 1.800 ± 0.68; G3: 0.975 ± 0.51; and G4: 4.325 ± 1.09. The mean maximum temperature variation (MTV) values were: 1.5ºC (G1), 2.9ºC (G2), 1.7ºC (G3) and 6.9ºC (G4). When comparing the experimental groups to the control group, G3 was not statistically different from G1 (p>0.05), but G2 and G4 presented significantly higher (p<0.05) intrapulpal temperatures and MTV. The three experimental groups differed significantly (p<0.05) from each other. CONCLUSIONS: The Nd:YAG laser was the activation method that presented the highest values of intrapulpal temperature variation when compared with LED and halogen light. The group activated by LED light presented the lowest values of temperature variation, which were similar to that of the control group.
Assuntos
Humanos , Temperatura Corporal/efeitos dos fármacos , Polpa Dentária/efeitos dos fármacos , Peróxido de Hidrogênio/uso terapêutico , Luz , Oxidantes/uso terapêutico , Clareamento Dental/métodos , Géis , Peróxido de Hidrogênio/administração & dosagem , Peróxido de Hidrogênio/efeitos da radiação , Lasers de Estado Sólido/uso terapêutico , Iluminação/instrumentação , Teste de Materiais , Oxidantes/administração & dosagem , Oxidantes/efeitos da radiação , Termômetros , Fatores de TempoRESUMO
Objetivo: Este estudo propôs avaliar a microdureza de diferentes resinas compostas de uso direto (rcd) e indireto (rci). Materiais e Métodos: Com o auxílio de uma matriz metálica (diâmetro: 5,0mm; espessura: 2,0mm) foram confeccionadas 70 amostras, sendo (n=10) três resinas de uso direto: Gr1- Z250(3M ESPE/EUA), Gr2- W3D(Wilcos/Brasil) e Gr3- Esthetic X(Dentisply/EUA); e quatro de uso indireto: Gr4- Resilab Master (Wilcos/Brasil), Gr5- Vita VM LC (Vita Zahnfabrik/Alemanha), Gr6- Vita Zeta (Vita Zahnfabrik/Alemanha) e Gr7- Sinfony (3M ESPE/EUA). As amostras das rcd foram confeccionadas utilizando a técnica incremental, onde cada incremento de resina foi fotopolimerizado durante 40 segundos. Já as amostras da rci foram polimerizadas segundo recomendações dos fabricantes. Todos os espécimes foram armazenados em água destilada a 37ºC durante 24 horas. O teste de microdureza foi realizado em microdurômetro digital (Future-Tech,Modelo FM 700), com carga de 50 kgf por 15 segundos. Os dados obtidos (Kgf/mm2) foram analisados utilizando o teste não paramétrico de Kruskal-Wallis e o de comparação múltipla de Dunn (p<0.05). Resultados: As medidas resumo-numéricas de microdureza obtidas foram (mediana; média ± desvio padrão): Gr1 (100,12; 101,07± 5,99 Kgf/mm2), Gr2 (83,55; 84,20± 5,07 Kgf/mm2), Gr3 (73,98; 73,95± 6,55 Kgf/mm2), Gr4 (52,50; 52,54± 5,9 Kgf/mm2), Gr5 (33,25; 34,36± 2,29 Kgf/mm2), Gr6 (29,60; 29.68± 1.52 Kgf/mm2), Gr7 (25,39; 25.13± 2.08 Kgf/mm2). Verificou-se que os valores de microdureza das rcd analisadas não diferiram estatisticamente entre si (p<0,05). O mesmo não se pode estabelecer para as resinas indiretas, pois a Sinfony diferiu da Resilab (p<0,05). Conclusão: Baseado nos resultados pôde-se concluir que apenas a resina composta direta Z250 apresentou valores de microdureza Vickers superior às demais resinas indiretas.