RESUMO
AIM: In the present study, we evaluated the influence of the photo-curing delay time and energy density on the degree of conversion and the Knoop microhardness of a resin cement. METHODS: Seventy-eight samples were assigned to 13 groups (n = 6), one of which received no light curing (control). The samples were made of a dual-cured resin cement (RelyX ARC) with the aid of a Teflon matrix, submitted to one of the following energy densities (J/cm²): 7, 14, 20, and 28. Delay times were immediate (0), 1 min, or 2 min. After 24 h, the degree of conversion and microhardness were measured at three segments: cervical, medium, and apical. Data were submitted to three-way anova and Tukey's and Dunnett's tests, the latest of which was used to compare the control to the experimental groups. RESULTS: No interaction was observed between delay time and energy density regarding the degree of conversion. The cervical segment showed the highest values, while the apical showed the lowest. Microhardness values concerning the cervical segment in all groups were statistically different from that obtained for the control. CONCLUSION: A high-irradiance light-curing unit allows for a reduced irradiation exposure time with a short delay time, aimed at tooth restorations using a dual-cured resin cement.