RESUMO

This study evaluated the effect of fluoride varnishes containing micrometric or nanosized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. Bovine root dentin blocks were selected by surface hardness and randomly divided into five experimental groups/varnishes (n = 20/group): placebo, 5% sodium fluoride (NaF); 5% NaF+5% micrometric TMP; 5% NaF+2.5% nanosized TMP; and 5% NaF+5% nanosized TMP. Half of the surface of all blocks received a single application of the assigned varnish, with subsequent immersion in artificial saliva for 6 h. Varnishes were then removed and the blocks were immersed in citric acid (90 s, 4×/day, 5 days). After each erosive cycle, ten blocks of each group were immersed in a placebo dentifrice for 15 s (ERO), while the other ten blocks were subjected to abrasion by brushing (ERO+ABR). Dentin erosive wear was assessed by profilometry. Data were submitted to 2-way ANOVA and to the Holm-Sidak test (p<0.05). Dentin erosive wear was significantly higher for ERO+ABR than for ERO for all varnishes. TMP-containing varnishes promoted superior effects against dentin erosive wear compared with 5% NaF alone; and 5% nanosized TMP led to the lowest wear among all varnishes. In conclusion, the addition of TMP to conventional fluoride varnish (i.e., varnish containing only NaF) enhanced its protective effects against bovine root dentin erosion and erosion+abrasion. Additionally, the use of 5% nanosized TMP led to superior effects in comparison to 5% micrometric TMP, both for erosion and erosion+abrasion in vitro.

Assuntos

Dentina , Fluoretos Tópicos , Teste de Materiais , Polifosfatos , Fluoreto de Sódio , Propriedades de Superfície , Erosão Dentária , Bovinos , Animais , Polifosfatos/farmacologia , Polifosfatos/química , Dentina/efeitos dos fármacos , Fluoreto de Sódio/farmacologia , Erosão Dentária/prevenção & controle , Fluoretos Tópicos/farmacologia , Análise de Variância , Fatores de Tempo , Propriedades de Superfície/efeitos dos fármacos , Distribuição Aleatória , Reprodutibilidade dos Testes , Nanopartículas/química , Abrasão Dentária/prevenção & controle , Saliva Artificial/química , Ácido Cítrico/farmacologia , Valores de Referência , Testes de Dureza

RESUMO

OBJECTIVES: To develop a protocol for forming subsurface caries lesions on bovine enamel by dual-species biofilms of Streptococcus mutans and Candida albicans in vitro. DESIGN: Biofilms were grown on bovine enamel specimens in artificial saliva (AS) for seven days. After 24 h of formation, the AS was supplemented or not with fluoride (F) using sodium fluoride (0.005 or 0.008 ppm F), and the biofilms were exposed or not to a 20 % sucrose solution (reproducing a cariogenic challenge) once/day. On the seventh day, the biofilms were harvested and had their extracellular polysaccharides (EPS) and inorganic components analyzed. The specimens were subjected to computed X-ray microtomography analysis to determine their mineral concentration. Data were compared using two-way analyses of variance, followed by Fisher's LSD or Student-Newman-Keuls tests (p < 0.05). RESULTS: Biofilms exposed to the cariogenic challenge had significantly higher EPS concentrations than those not exposed, regardless of the presence of F. For biofilms grown with 0.008 ppm F, those exposed to the cariogenic challenge had lower F levels than those not exposed. For biofilms exposed to the cariogenic challenge, those grown with 0.008 ppm F had lower lesion depths and integrated mineral loss, and higher outer layers than those grown without F. CONCLUSIONS: The dual biofilm model assessed was able to create subsurface caries lesions in bovine enamel in vitro, which was influenced by the presence of F in the culture medium and exposure to sucrose.

Assuntos

Biofilmes , Candida albicans , Cárie Dentária , Esmalte Dentário , Streptococcus mutans , Candida albicans/fisiologia , Streptococcus mutans/fisiologia , Cárie Dentária/microbiologia , Animais , Bovinos , Polissacarídeos Bacterianos/metabolismo , Sacarose/farmacologia , Fluoretos/farmacologia , Esmalte Dentário/química , Esmalte Dentário/microbiologia , Esmalte Dentário/patologia , Modelos Animais

RESUMO

BACKGROUND: This study aimed to evaluate dentin wear and biological performance of desensitizing materials. METHODS: Seventy bovine root dentin blocks were sectioned. Half of the surface of each specimen was untreated (control) and the other half was immersed in EDTA and treated with the following desensitizing materials: placebo varnish (PLA), fluoride varnish (FLU), sodium fluoride (NaF) varnish + sodium trimetaphosphate (TMP), universal adhesive (SBU), S-PRG varnish (SPRG), biosilicate (BIOS), and amelotin solution (AMTN). After application, the specimens were submitted to an erosive-abrasive challenge and the wear analyzed by optical profilometer. Serial dilutions of extracts obtained from the culture medium containing discs impregnated with those desensitizers were applied on fibroblasts and odontoblasts-like cells cultures. Cytotoxicity and production of total protein (TP) by colorimetric assays were determined after 24 h. Data were statistically analyzed using Kruskal-Wallis, Dunn's, One-way ANOVA and Tukey tests (p ≤ 0.05). RESULTS: No dentin wear was observed only for SBU. The lowest dentin wear was observed for AMTN and TMP. Cell viability was significantly reduced after treatment with undiluted extracts of PLA, FLU, TMP and SBU in fibroblasts and TMP and SBU in odontoblast-like cells. SPRG, BIOS and AMTN were cytocompatible at all dilutions tested. Considering TP results, no statistical difference was observed among the groups and high levels for TP were observed after TMP and FLU treatments. CONCLUSIONS: Universal adhesive system may protect dentin with opened tubules from wear after challenge. Extracts of adhesive and fluoride varnishes presented cytotoxic mainly on fibroblasts. The enamel protein may be a future alternative to treat dentin with opened tubules because it may cause low wear under erosive-abrasive challenge with low cytotoxic effects.

Assuntos

Dessensibilizantes Dentinários , Dentina , Fluoreto de Sódio , Animais , Bovinos , Dessensibilizantes Dentinários/farmacologia , Fluoreto de Sódio/farmacologia , Dentina/efeitos dos fármacos , Fluoretos Tópicos/farmacologia , Fibroblastos/efeitos dos fármacos , Sobrevivência Celular/efeitos dos fármacos , Desgaste dos Dentes , Teste de Materiais , Polifosfatos/farmacologia

RESUMO

OBJECTIVE: To assess the effects of arginine, with or without sodium fluoride (NaF; 1,450 ppm), on saliva-derived microcosm biofilms and enamel demineralization. METHODS: Saliva-derived biofilms were grown on bovine enamel blocks in 0.2 % sucrose-containing modified McBain medium, according to six experimental groups: control (McBain 0.2 %); 2.5 % arginine; 8 % arginine; NaF; 2.5 % arginine with NaF; and 8 % arginine with NaF. After 5 days of growth, biofilm viability was assessed by colony-forming units counting, laser scanning confocal microscopy was used to determine biofilm vitality and extracellular polysaccharide (EPS) production, while biofilm metabolism was evaluated using the resazurin assay and lactic acid quantification. Demineralization was evaluated by measuring pH in the culture medium and calcium release. Data were analyzed by Kruskal-Wallis' and Dunn's tests (p < 0.05). RESULTS: 8 % arginine with NaF showed the strongest reduction in total streptococci and total microorganism counts, with no significant difference compared to arginine without NaF. Neither 2.5 % arginine alone nor NaF alone significantly reduced microbial counts compared to the control, although in combination, a reduction in all microbial groups was observed. Similar trends were found for biofilm vitality and EPS, and calcium released to the growth medium. CONCLUSIONS: 8 % Arginine, with or without NaF, exhibited the strongest antimicrobial activity and reduced enamel calcium loss. Also, NaF enhanced the effects of 2.5 % arginine, yielding similar results to 8 % arginine for most parameters analyzed. CLINICAL SIGNIFICANCE: The results provided further evidence on how arginine, with or without NaF, affects oral microcosm biofilms and enamel mineral loss.

Assuntos

Arginina , Biofilmes , Cariostáticos , Esmalte Dentário , Microscopia Confocal , Saliva , Fluoreto de Sódio , Desmineralização do Dente , Biofilmes/efeitos dos fármacos , Arginina/farmacologia , Fluoreto de Sódio/farmacologia , Esmalte Dentário/efeitos dos fármacos , Esmalte Dentário/microbiologia , Bovinos , Animais , Desmineralização do Dente/prevenção & controle , Desmineralização do Dente/microbiologia , Cariostáticos/farmacologia , Saliva/microbiologia , Saliva/metabolismo , Saliva/efeitos dos fármacos , Concentração de Íons de Hidrogênio , Viabilidade Microbiana/efeitos dos fármacos , Cálcio/análise , Cálcio/metabolismo , Streptococcus/efeitos dos fármacos , Xantenos/farmacologia , Contagem de Colônia Microbiana , Oxazinas/farmacologia

RESUMO

OBJECTIVE: To assess the protective effect of fluoride (F) gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMPmicro and TMPnano, respectively) against enamel erosion in vitro. METHODS: Bovine enamel blocks (n = 140) were selected according to their surface hardness, and randomly divided into seven groups (n = 20/group), according to the gels tested: Placebo (without F/TMP), 4,500 µg F/g (4500F), 9,000 µg F/g (9000F), 4500F plus 2.5 % TMPnano (2.5 % Nano), 4500F plus 5 % TMPnano (5 % Nano), 4500F plus 5 % TMPnano (Micro 5 %) and 12,300 µg F/g (Acid gel). Blocks were treated once during one minute with the gels, and submitted to erosive (ERO, n = 10/group) or erosive plus abrasive (ERO+ABR, n = 10/group) challenges 4 times/day, for 90 s for each challenge (under reciprocating agitation), during consecutive 5 days. Blocks were analyzed by profilometry, and by surface (SH) and cross-sectional hardness (∆KHN). Data were submitted to two-way ANOVA, and Fisher's LSD test (p < 0.05). RESULTS: For ERO, both TMPnano-containing gels promoted enamel wear significantly lower than Placebo and 4500F, reaching levels similar to both positive controls (9000F and acid gel); significantly lower softening was observed for enamel treated with 4500F+5 % Micro and 4500F+2.5 % Nano. Also, the lowest ∆KHN values were observed for 4500F+2.5 % TMPnano among the TMP-containing gels. For ERO+ABR, the lowest enamel wear was achieved by the use of 4500F+5 % Nano among all gels, including both positive controls; lower softening was observed for Placebo and 9000F groups. CONCLUSION: The addition of 5 % nano-sized TMP to a low-fluoride gel produced superior protective effects for enamel under both challenges conditions, when compared with micrometric TMP, reaching values similar to or superior than both positive controls, respectively for ERO and ERO+ABR. CLINICAL SIGNIFICANCE: The supplementation of low-F gels with TMP was shown to significantly improve their effects on enamel erosive wear, and the use of nano-sized TMP further enhances this protective action.

Assuntos

Cariostáticos , Esmalte Dentário , Géis , Dureza , Nanopartículas , Polifosfatos , Erosão Dentária , Animais , Bovinos , Esmalte Dentário/efeitos dos fármacos , Polifosfatos/farmacologia , Erosão Dentária/prevenção & controle , Cariostáticos/farmacologia , Cariostáticos/uso terapêutico , Distribuição Aleatória , Fluoretos/uso terapêutico , Placebos , Fatores de Tempo

RESUMO

This work assessed the influence of the amount of dentifrice and fluoride (F) concentration in the product on the pH and inorganic components of Streptococcus mutans and Candida albicans dual-species biofilms. The biofilms were treated with suspensions of fluoride dentifrices containing 550 or 1100 ppm of F (550 F or 1100 F, respectively) administered at comparable intensities: (i-1) 550 F/0.08 g or 1100 F/0.04 g; (i-2) 550 F/0.16 g or 1100 F/0.08 g; and (i-3) 550 F/0.32 g or 1100 F/0.16 g. A placebo dentifrice (without NaF, 0.32 g) was used as a negative control. After the last treatment, the biofilm pH was measured and the F, calcium (Ca), and phosphorus (P) concentrations were determined. Data were subjected to an ANOVA/Kruskal-Wallis test, and a Student-Newman-Keuls test. The highest biofilm pH and F concentrations (biomass and fluid) were observed for 1100 F at i-3. Overall, 1100 F resulted in F levels similar to 550 F for i-1 and i-2. In addition, 550 F applied at i-2 and i-3 led to higher F in the biomass/fluid compared to 1100 F applied at i-1 and i-2, respectively. In biomass, the lowest Ca concentrations were observed for 1100 F at i-3. The conclusion drawn is that the treatment intensity holds greater significance as a parameter compared to the concentration of F or the amount of dentifrice when considered individually.

RESUMO

OBJECTIVE: The study assessed the effect of low-fluoride gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. DESIGN: Bovine dentin blocks (n = 154) were selected by surface microhardness and randomly allocated into seven groups (n = 22/group), according to the gels: Placebo; 4500 ppm F (4500F); 9000 ppm F (9000F); 5% TMP microparticulate plus 4500F (5TMPm+4500F); 2.5% TMP nanoparticulate plus 4500 F (2.5TMPn+4500F); 5% TMP nanoparticulate plus 4500F (5TMPn+4500F); and 12,300 ppm F acid gel (APF). All blocks were treated only once for 60 s and cyclically eroded (ERO, citric acid, 4 × 90 s/day) or eroded and brushed (4 × 15 s/day, five strokes/s, ERO+ABR) over five days (each subgroup n = 11). Dentin wear and integrated hardness loss in depth (ΔKHN) were determined, and the data were submitted to two-way ANOVA, followed by Tukey's test, and Spearman's correlation (p < 0.05). RESULTS: For ERO, all gels containing 4500F supplemented with TMP significantly reduced dentin wear compared with their counterpart without TMP, reaching values similar to 9000F. For ERO+ABR, 5TMPn+ 4500F gel led to significantly lower wear than all its counterparts, reaching values similar to 9000F and APF. As for ΔKHN, all gels containing TMP promoted superior protective effects compared with 4500F, reaching values similar to 9000F and APF under both challenges. A positive correlation between dentin wear and mineral content in depth was verified. CONCLUSIONS: Gels containing 4500F supplemented with TMP significantly reduced dentin erosive wear compared with pure 4500F, with additional benefit from the use of nanoparticles.

Assuntos

Dentina , Fluoretos , Géis , Nanopartículas , Polifosfatos , Erosão Dentária , Polifosfatos/farmacologia , Animais , Bovinos , Erosão Dentária/prevenção & controle , Dentina/efeitos dos fármacos , Fluoretos/farmacologia , Técnicas In Vitro , Dureza , Distribuição Aleatória , Propriedades de Superfície

RESUMO

The literature is conflicting regarding salivary nitrite (NO2-)/nitrite and nitrate (NO2- and NO3-) levels in children affected by dental caries. For this reason, a systematic review to provide a consensus on the subject was propose, whose objective is to verify whether these molecules could be used as biomarkers in children with caries. A comprehensive search was performed on online database and eleven articles were included in the meta-analysis. The methodological quality of studies was assessed by Newcastle-Ottawa Scale recommended for case-control studies and by AXIS tool for cross-sectional studies. Grading of Recommendations Assessment, Development and Evaluation was used for the assessment of the certainty of the evidence for each outcome. The results showed lower NO2- levels in the group of children affected by dental caries (SMD = -2.18 [-3.24, -1.13], p < 0.01). Age, saliva collection and methods of evaluation can impact the results. When evaluating the severity of the condition, an important variation was detected in relation to the different evaluation methods NO2-/NO2- and NO3-. In conclusion, based on the evidence presented, the results suggest that NO2- levels in saliva are a possible biomarker of dental caries. Results should be evaluated with caution due to the very low evidence from primary studies. Longitudinal studies are necessary to strengthen this hypothesis.

Assuntos

Biomarcadores , Cárie Dentária , Nitratos , Nitritos , Saliva , Humanos , Cárie Dentária/metabolismo , Cárie Dentária/diagnóstico , Saliva/química , Saliva/metabolismo , Biomarcadores/metabolismo , Biomarcadores/análise , Criança , Nitratos/análise , Nitratos/metabolismo , Nitritos/análise , Nitritos/metabolismo

RESUMO

INTRODUCTION: This study investigated the changes in the acquired enamel pellicle (AEP) proteome when this integument is formed in vivo after treatment with sugarcane-derived cystatin (CaneCPI-5), hemoglobin (HB), and a statherin-derived peptide (StN15), or their combination and then exposed to an intrinsic acid challenge. The effectiveness of these treatments in preventing intrinsic erosion was also evaluated. METHODS: Ten volunteers, after prophylaxis, in 5 crossover phases, rinsed with the following solutions (10 mL, 1 min): control (deionized water-H2O) - group 1, 0.1 mg/mL CaneCPI-5 - group 2, 1.0 mg/mL HB - group 3, 1.88 × 10-5M StN15 - group 4, or a blend of these - group 5. Following this, AEP formation occurred (2 h) and an enamel biopsy (10 µL, 0.01 m HCl, pH 2.0, 10 s) was conducted on one incisor. The biopsy acid was then analyzed for calcium (Arsenazo method). The vestibular surfaces of the other teeth were treated with the same acid. Acid-resistant proteins in the residual AEP were then collected and analyzed quantitatively via proteomics. RESULTS: Compared to control, treatment with the proteins/peptide, mixed or isolated, markedly enhanced acid-resistant proteins in the AEP. Notable increases occurred in pyruvate kinase PKM (11-fold, CaneCPI-5), immunoglobulins and submaxillary gland androgen-regulated protein 3B (4-fold, StN15), Hb, and lysozyme C (2-fold, StN15). Additionally, a range of proteins not commonly identified in the AEP but known to bind calcium or other proteins were identified in groups treated with the tested proteins/peptide either in isolation or as a mixture. The mean (SD, mM) calcium concentrations released from enamel were 3.67 ± 1.48a, 3.11 ± 0.72a, 1.94 ± 0.57b, 2.37 ± 0.90a, and 2.38 ± 0.45a for groups 1-5, respectively (RM-ANOVA/Tukey, p < 0.05). CONCLUSIONS: Our findings demonstrate that all treatments, whether using a combination of proteins/peptides or in isolation, enhanced acid-resistant proteins in the AEP. However, only HB showed effectiveness in protecting against intrinsic erosive demineralization. These results pave the way for innovative preventive methods against intrinsic erosion, using "acquired pellicle engineering" techniques.

Assuntos

Cálcio , Erosão Dentária , Humanos , Cálcio/metabolismo , Película Dentária , Peptídeos , Proteoma , Erosão Dentária/prevenção & controle , Hemoglobinas/metabolismo

RESUMO

Abstract This study evaluated the effect of fluoride varnishes containing micrometric or nanosized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. Bovine root dentin blocks were selected by surface hardness and randomly divided into five experimental groups/varnishes (n = 20/group): placebo, 5% sodium fluoride (NaF); 5% NaF+5% micrometric TMP; 5% NaF+2.5% nanosized TMP; and 5% NaF+5% nanosized TMP. Half of the surface of all blocks received a single application of the assigned varnish, with subsequent immersion in artificial saliva for 6 h. Varnishes were then removed and the blocks were immersed in citric acid (90 s, 4×/day, 5 days). After each erosive cycle, ten blocks of each group were immersed in a placebo dentifrice for 15 s (ERO), while the other ten blocks were subjected to abrasion by brushing (ERO+ABR). Dentin erosive wear was assessed by profilometry. Data were submitted to 2-way ANOVA and to the Holm-Sidak test (p<0.05). Dentin erosive wear was significantly higher for ERO+ABR than for ERO for all varnishes. TMP-containing varnishes promoted superior effects against dentin erosive wear compared with 5% NaF alone; and 5% nanosized TMP led to the lowest wear among all varnishes. In conclusion, the addition of TMP to conventional fluoride varnish (i.e., varnish containing only NaF) enhanced its protective effects against bovine root dentin erosion and erosion+abrasion. Additionally, the use of 5% nanosized TMP led to superior effects in comparison to 5% micrometric TMP, both for erosion and erosion+abrasion in vitro.