RESUMO

The present study aimed to characterize the microstructure of a temporary 3D printing polymer-based composite material (Resilab Temp), evaluating its optical properties and mechanical behavior according to different post-curing times. For the analysis of the surface microstructure and establishment of the best printing pattern, samples in bar format following ISO 4049 (25 × 10 × 3 mm) were designed in CAD software (Rhinoceros 6.0), printed on a W3D printer (Wilcos), and light-cured in Anycubic Photon for different lengths of time (no post-curing, 16 min, 32 min, and 60 min). For the structural characterization, analyses were carried out using Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM). The mechanical behavior of this polymer-based composite material was determined based on flexural strength tests and Knoop microhardness. Color and translucency analysis were performed using a spectrophotometer (VITA Easy Shade Advanced 4.0), which was then evaluated in CIELab, using gray, black, and white backgrounds. All analyses were performed immediately after making the samples and repeated after thermal aging over two thousand cycles (5-55 °C). The results obtained were statistically analyzed with a significance level of 5%. FT-IR analysis showed about a 46% degree of conversion on the surface and 37% in the center of the resin sample. The flexural strength was higher for the groups polymerized for 32 min and 1 h, while the Knoop microhardness did not show a statistical difference between the groups. Color and translucency analysis also did not show statistical differences between groups. According to all of the analyses carried out in this study, for the evaluated material, a post-polymerization time of 1 h should be suggested to improve the mechanical performance of 3D-printed devices.

RESUMO

Purpose: In case of need for esthetical improvement of zirconia restorations, an individualization using extrinsic staining can be applied. This study aimed to evaluate the surface roughness and fatigue strength (survival) of high-translucency zirconia (3Y-TZP, YZ®HT, Vita Zanhfabrik) with extrinsic characterization and/or glaze. Methods: Sixty (60) zirconia discs (12 × 1.2 mm) were obtained, sintered, and randomly distributed among three groups (n = 20) according to the surface finishing protocol: C (control), C + G (extrinsic characterization followed by a glaze layer), and G (glaze layer). The surface roughness (Ra) was analyzed with a contact profilometer. Subsequently, the specimens were subjected to a fatigue load profile starting at 120 N during 20,000 cycles at 4 Hz frequency, with a 5% increase at each step until failure. The failed specimens were evaluated under a stereomicroscope. Surface roughness analysis was evaluated by using one-way ANOVA and post hoc Tukey tests (95%); while fatigue survival probability was analyzed with Kaplan-Meier and Mantel-Cox (log- rank, 95%). Results: One-way ANOVA revealed that surface roughness was affected by the finishing protocol, where C + G showed the highest mean value (0.46 ± 0.18 µm)A followed by G (0.30 ± 0.10 µm)B, and C (0.19 ± 0.02 µm)C. While for fatigue strength, the G protocol presented a higher mean value (243.00, and 222.36-263.63)A, followed by C + G (192.75 and 186.61-198.88)B and C (172.50 and 159.43-185.56)C. Conclusion: Surface finishing protocols modify the surface roughness and fatigue strength of high-translucent zirconia. Regardless of the surface roughness, both glazing protocols improved the ceramic fatigue strength, favoring the restoration's long-term survival.

RESUMO

Com base no desenvolvimento da odontologia adesiva, restaurações minimamente invasivas em cerâmica são utilizadas como alternativas para restaurar um dente. As cerâmicas odontológicas são amplamente aplicadas na área odontológica principalmente devido à sua estética e resistência mecânica. Uma das propriedades da cerâmica a ser bem conhecida antes de seu uso, é a resistência ao desgaste que deve ser compatível com o comportamento de desgaste do antagonista para evitar desempenhos indesejados. Portanto, vários métodos têm sido realizados para avaliar o comportamento do desgaste dos materiais cerâmicos considerando diferentes condições presentes no complexo meio oral. Este estudo teve como objetivo compilar os métodos utilizados para investigar o desgaste das cerâmicas odontológicas e descrever os mecanismos de desgaste envolvidos nos mesmos. A obtenção e análise de dados também é abordada para discutir os resultados obtidos a partir de diferentes métodos, bem como a análise clínica do desgaste e perspectivas futuras sobre esse tema. Em conclusão, muitas metodologias estão disponíveis para medir o desgaste cerâmico. Portanto, os métodos devem ser selecionados com base na relevência clínica de cada estudo e devem seguir parâmetros previamente relatados para padronização, permitindo a comparação da literatura (AU)

Based on the development of adhesive dentistry, minimally invasive restorations in ceramics are used as alternatives to restore a tooth. Dental ceramics are largely applied in the dentistry field mainly due to their esthetic and mechanical strength. One of the ceramic properties to be well known before its use is the wear resistance that should be compatible with the antagonist wear behavior to avoid unwanted performance. Therefore, several methods have been performed to assess the ceramic materials wear behavior considering different conditions present in the complex oral medium. This study aimed to compile the methods used to investigate dental ceramics wear and to describe the wear mechanisms involved on them. Obtaining and analyzing data is also addressed to discuss the results obtained from different methods, as well as the clinical analysis of wear and future perspectives on this topic. In conclusion, many methodologies are available to measure the ceramic wear. Therefore, the methods must be selected based on the clinical significance of each study and should follow previously reported parameters for standardization, allowing literature comparison. (AU)

Assuntos

RESUMO

Alternative surface treatments have been proposed for the cementation of lithium disilicate ceramics aiming to improve adhesive and flexural strength under fatigue. This study aimed to evaluate the slow crack growth (SCG) parameters of the lithium disilicate ceramic after hydrofluoric acid (HF) etching or air abrasion (AB) as surface treatments. Ceramic discs were treated with HF (5%, 20 s) or AB (30 µm silica-modified alumina particles, 2.8 bar, 10 mm distance, 15 s), and received a layer of resin cement. The surface roughness after surface treatment was evaluated (n = 5). Samples were tested in a piston-on-three-ball assembly to evaluate the flexural strength (n = 20), inert strength (n = 25), and to determine SCG parameters n and D (n = 35). The highest roughness (p < 0.01) was observed in the AB group, with the highest reliability according to the Weibull analysis, but the lowest SCG susceptibility. Flexural (p = 0.03) and inert strength (p < 0.01) were the greatest in the HF group. Despite exhibiting lower strength than 5% HF, air abrasion may be an alternative for the surface treatment of lithium disilicate surfaces, indicating the best prognosis over time.

RESUMO

Stains and glaze are effective procedures for achieving an aesthetic smoothness on indirect restorations. Thus, the effect of surface-etching treatments previous to the stain layer and the glaze application on the occlusal and antagonist wear of a hybrid ceramic were evaluated against different antagonists. Disc-shaped samples were prepared from polymer-infiltrated ceramic network (PICN) blocks. The specimens were divided into eight groups, according to the surface-etching treatment and glaze application: P (polished specimens); PG (polishing plus glaze); E (hydrofluoric acid etching plus stain); EG (acid etching plus stain plus glaze); A (aluminum oxide sandblasting plus stain); AG (sandblasting plus stain plus glaze); S (self-etching primer plus stain); SG (self-etching primer plus stain plus glaze). Half of the samples were subjected to a wear simulation with a steatite antagonist, and the other half was tested using a PICN antagonist. The test parameters were: 15 N, 1.7 Hz, 6 mm of horizontal sliding, 5000 cycles. The discs and the antagonists' masses were measured before and after the wear tests. The average roughness and spacing defects were evaluated. The etching treatment affected the surface and antagonist mass loss when tested against steatite. AG showed the highest mass loss. This influence was not detected when using the PICN antagonist. The glaze application after staining ensures a smoother surface and avoids antagonist wear.

RESUMO

This study aimed to evaluate the biomechanical behavior of Morse taper implants using different abutments (CMN abutment [(CMN Group] and miniconical abutments [MC Group]), indicated to support a screw-retained 3-unit fixed partial denture. For the in vitro test, polyurethane blocks were fabricated for both groups (n = 10) and received three implants in the "offset" configuration and their respective abutments (CMN or MC) with a 3-unit fixed partial denture. Four strain gauges were bonded to the surface of each block. For the finite element analysis, 3D models of both groups were created and exported to the analysis software to perform static structural analysis. All structures were considered homogeneous, isotropic, and elastic. The contacts were considered non-linear with a friction coefficient of 0.3 between metallic structures and considered bonded between the implant and substrate. An axial load of 300 N was applied in three points (A, B, and C) for both methods. The microstrain and the maximum principal stress were considered as analysis criteria. The obtained data were submitted to the Mann-Whitney, Kruskal-Wallis, and Dunn's multiple comparison test (α = 5%). The results obtained by strain gauge showed no statistical difference (p = 0.879) between the CMN (645.3 ± 309.2 µÎµ) and MC (639.3 ± 278.8 µÎµ) and allowed the validation of computational models with a difference of 6.3% and 6.4% for the microstrains in the CMN and MC groups, respectively. Similarly, the results presented by the computational models showed no statistical difference (p = 0.932) for the CMN (605.1 ± 358.6 µÎµ) and MC (598.7 ± 357.9 µÎµ) groups. The study concluded that under favorable conditions the use of CMN or MP abutments to support a fixed partial denture can be indicated.

RESUMO

OBJECTIVES: This study evaluated the effect of deep margin elevation (DME) and restorative materials (leucite-reinforced glass-ceramics [C] vs. indirect resin composite [R]) on the fatigue behavior and stress distribution of maxillary molars with 2-mm deep proximal margins restored with MOD inlay. METHODS: Fifty-two extracted human third molars were randomly assigned into four groups (n = 13): C; DME + C; R; and DME + R. Inlays were fabricated in CAD-CAM and bonded to all teeth. The fatigue behavior was assessed with the stepwise stress test (10,000 cycles/step; step = 50 N; 20 Hz; initial load = 200 N). Fatigue failure loads and the number of cycles were analyzed with 2-way ANOVA and Tukey's test (p < 0.05) and Kaplan-Meier survival plots. The stress distribution was assessed with finite element analysis. The models were considered isotropic, linear, and homogeneous, and presented bonded contacts. A tripod axial load (400 N) was applied to the occlusal surface. The stress distribution was analyzed with the maximum principal stress criterion. RESULTS: For fatigue, there was no difference for DME factor (p > 0.05). For the material factor, the load and number of cycles for failure were statistically higher in the R groups (p < 0.05). The finite element analysis showed that resin composite inlays concentrated more stress in the tooth structure, while ceramic inlays concentrated more stress in the restoration. Non-reparable failures were more frequent in the resin composite inlays groups. CONCLUSIONS: DME was not negative for fatigue and biomechanical behaviors. Resin composite inlays were more resistant to the fatigue test, although the failure mode was more aggressive. CLINICAL SIGNIFICANCE: DME does not impair mechanical behavior. Resin composite inlays failed at higher loads but with a more aggressive failure mode.

Assuntos

RESUMO

This study aimed to evaluate the biomechanical behavior, stress distributions and bone microstrain of fixed partial dentures (FPD) with ceramic abutments supported on monotype zirconia implants, titanium implants and two-piece zirconia implants, using finite element analysis. A three-dimensional model of the jaw was simulated containing 1.0 mm thick cortical bone and cancellous bone tissue. A FPD and implant models (4.1 x 10 mm) were modeled containing a cement-retained implant abutment. These models were replicated in three groups with similar geometries: Titanium Implant and Zirconia Abutment (Ti-Zr); Zirconia Implant and Zirconia Abutment (Zr-Zr) and Monotype Zirconia Implant (Zr-S). An axial load of 300 N was applied to the center of the first premolar. The microstrain (µÎµ) and the Von-Mises stress (MPa) were assumed as failures criteria. For the three groups, a higher stress concentration was observed in the region of FPD connectors. The Ti-Zr group showed a higher stress concentration in the prosthesis and implant when compared to the other groups. However, the smaller elastic modulus of the titanium implant, in relation to the zirconia, provided a lower stress in the abutment and in the prosthetic screw. The monotype implant system allowed a more homogeneous stress distribution and its strain were predominantly located in the cervical region of the peri-implant bone tissue. Monotype or two-piece zirconia implants can be used for rehabilitation with FPD. However, the absence of separation between implant and abutment in the monotype system avoids the stress concentration in the prosthetic screw and reduced the peri-implant bone strain.

Assuntos

RESUMO

Aim: To describe through a clinical case report the surgical sequence of rehabilitation with 3D-printed implants associated with maxillary sinus floor lift with synthetic regenerative materials, including biphasic bioceramic. Case Report: Patient had an agenesis of the upper left premolars (#12 and #13), a vertical bone deficiency caused by maxillary sinus' pneumatization, and a horizontal alveolar resorption around the missing teeth area. During the surgical procedures, incisions, detachment, and osteotomy were performed in the lateral region of the maxillary sinus. The sinus membrane was detached and lifted 10 mm. Then, a thick poly(dioxanone)-based synthetic resorbable membrane (Plenum) was inserted and adapted inside the sinus to protect the sinus membrane. After the osteotomies with sub-instrumentation, 3D-printed implants (Plenum) were installed in the #12 area (3.5mm x 11.5 mm; 30N) and #13 area (4.0mm x 10mm; 20N). The maxillary sinus was entirely filled with a biphasic bioceramic, HA/ß-TCP (70:30) 500-1000 µm (Plenum) and covered by the same synthetic resorbable membrane. Connective tissue graft from the palatal area was positioned internally to the flap and stabilized with sutures to improve the vestibular tissue architecture. The entire surgical wound was sutured, and the tissues stabilized. No complications occurred in the postoperative period. Conclusion: The use of synthetic regenerative memberane and 3D-printed implants seems to be a promising option in areas of deficient bone remnants (AU)

Objetivo: Descrever por meio de um relato de caso clínico a sequência cirúrgica de reabilitação com implantes obtidos por impressão 3D associados à elevação do assoalho do seio maxilar com materiais regenerativos sintéticos, incluindo uma biocerâmica bifásica. Relato de Caso: Paciente apresentava agenesia dos pré-molares superiores esquerdos (24 e 25), deficiência óssea vertical causada pela pneumatização do seio maxilar e reabsorção alveolar horizontal ao redor da área dos dentes ausentes. Durante os procedimentos cirúrgicos foram realizados incisões, descolamento e osteotomia na região lateral do seio maxilar. A membrana sinusal foi descolada e elevada 10 mm. Em seguida, uma membrana reabsorvível sintética à base de poli(dioxanona) espessa (Plenum) foi inserida e adaptada dentro do seio para proteger a membrana do seio. Após as osteotomias com subinstrumentação, implantes impressos em 3D (Plenum) foram instalados na área do 24 (3,5mm x 11,5mm; 30N) e na área do 25 (4,0mm x 10mm; 20N). O seio maxilar foi inteiramente preenchido com biocerâmica bifásica, HA/ß-TCP (70:30)500-1000 µm (Plenum) e recoberto pela mesma membrana sintética reabsorvível. O tecido conjuntivo da região palatina foi posicionado internamente ao retalho e estabilizado com suturas para melhorar a arquitetura do tecido vestibular. Toda a ferida cirúrgica foi suturada e os tecidos estabilizados. Não ocorreram complicações no pós-operatório. Conclusão:A utilização de biomateriais regenerativos sintéticos e implantes impressos parece ser uma opção promissora em áreas de remanescentes ósseos deficientes.(AU)

Assuntos

RESUMO

The present study was a prospective, controlled, randomized, clinical short-term trial aiming to evaluate the clinical performance of adhesively luted, lithium disilicate and feldspathic glass-ceramics onlays over a period up to 2 years. A total of 11 patients (7 female, 4 male; age range: 18-60 years, mean age: 39 years) were selected for this study. Each patient received a maximum of two restorations per group in a split-mouth-design. LD: Eleven onlays, performed with lithium disilicate-based ceramic (IPS e.max CAD, Ivoclar Vivadent, Schaan, Liechtenstein), and FP: Eleven onlays, performed with feldspathic ceramic (Vita Mark II, Vita Zanhfabrik, Bad Säckingen). Recalls were performed at 2 weeks (baseline = R1), 1 year (R2) and 2 years (R3) after the cementation by three calibrated blinded independent investigators using mirrors, magnifying eyeglasses, probes and bitewing radiographs. The postoperative sensitivity, secondary caries, marginal integrity, marginal discoloration, color match, surface roughness, tooth integrity, and restoration integrity were evaluated. The Friedman test was used to determine if there was a statistically significant difference in time-to-time comparison of the parameters in the ceramics restorations. A total of 95.4% of the restorations were clinically acceptable at the 2-year recall, without a difference for any evaluation parameter for both ceramic materials. Based on the 2-year data, the CAD-CAM onlays manufactured with feldspathic and lithium-disilicate based ceramics showed similar clinical performance.