RESUMO
OBJECTIVE: To determine the effect of airborne particle abrasion (APA) on micro-tensile bond strength (µTBS) to dentin using different air-abrasion/polishing powders. METHODS: The bonding effectiveness of G2 Bond Universal (G2B), used in etch-and-rinse (E&R) and self-etch mode (SE), was tested on bur-cut dentin and dentin air abraded/polished using six different powders (aluminum oxide 29 µm (AO29) and 53 µm (AO53), aluminum trihydroxide (AT), sodium bicarbonate (SB), sodium bicarbonate soft (SBsoft) and bioactive glass (BG); Velopex). Adhesive-composite resin specimens were immersed in distilled water at 37 °C for one week and cut into microspecimens. Half of the specimens were subjected to 50,000 thermocycles (aged). Immediate and aged µTBS to dentin were measured. Statistical analysis was performed using linear mixed-effects (LME) modeling (p < 0.05). RESULTS: Comparing the aged bond strengths to air-abraded/polished dentin with bur-cut dentin, pretreatment with SB and SBsoft in combination with G2B used in E&R mode, and BG air polishing in combination with both application modes (E&R, SE), resulted in a significantly higher bond strength. Dentin bond strength was only significantly lower when air abraded with AO29 and using G2B in SE mode. Aging did not significantly influence bond strength for both application modes (E&R, SE), except for AO29 and AT-treated dentin, where bond strengths decrea sed significantly using G2B in SE mode. In general, G2B reached significantly higher bond strengths on air-abraded/polished dentin in E&R mode than in SE mode. CONCLUSION: Air-abrasion/polishing did not impair dentin bond strength using G2B, except when dentin was air abraded with AO29 and using G2B in SE mode. Air polishing positively influenced the bond strength to dentin in specific groups. CLINICAL SIGNIFICANCE: APA is safe concerning bonding to dentin. The E&R application mode is preferred using G2B as adhesive on air-abraded/polished dentin. Air polishing with BG positively influenced dentin bond strength for both application methods.
Assuntos
Abrasão Dental por Ar , Resinas Compostas , Colagem Dentária , Adesivos Dentinários , Dentina , Teste de Materiais , Cimentos de Resina , Propriedades de Superfície , Resistência à Tração , Colagem Dentária/métodos , Humanos , Resinas Compostas/química , Adesivos Dentinários/química , Cimentos de Resina/química , Análise do Estresse Dentário , Condicionamento Ácido do Dente/métodos , Polimento Dentário/métodos , Estresse Mecânico , Materiais Dentários/química , PósRESUMO
This study aimed to compare the fracture toughness of molars with wide mesio-occlusal-distal (MOD) cavities restored with regular and flowable bulk-fill resin composite and a conventional resin composite after 250,000 mechanical cycles of chewing simulation. Thirty-two extracted mandibular third molars were selected and class II MOD cavities involving 2/3 of the intercuspal width and 4 mm depth were prepared. Teeth were divided into four groups based on resin composite type and insertion technique (n=8): (1) CT, unprepared teeth (control); (2) CV, conventional resin composite (Tetric N-Ceram, Ivoclar Vivadent) with incremental technique; (3) R-BF, regular bulk-fill resin composite (Tetric N-Ceram Bulk Fill, Ivoclar Vivadent) with a single increment; and (4) F-BF, flowable bulk-fill resin composite (Tetric N-Flow Bulk Fill, Ivoclar Vivadent) with a single increment, except for a 1-mm-thick layer at the occlusal surface, restored with conventional resin composite (Tetric N-Ceram). All specimens were evaluated to detect the presence and propagation of enamel cracks using a LED transilluminator before and after 250,000 mechanical cycles (SD Mechatronic GmbH). After a chewing simulation, they were subjected to a compressive force in a universal testing machine (DL-2000, EMIC) until fracture. The maximum fracture load of the specimens was measured (N) and the fracture patterns were classified based on the fracture site (above or below the cementoenamel junction [CEJ]). Data were statistically analyzed with one-way ANOVA. All specimens survived after 250,000 mechanical cycles, and no statistically significant differences among groups were observed regarding the fracture toughness (p<0.05). The fracture analysis demonstrated that failures below the CEJ were more common in CV (75%), while CT, R-BF, and F-BF showed this type of failure in 38%, 63%, and 63% of the specimens, respectively. The results of the crack analysis showed that the occurrence of new cracks and crack propagation was also higher in CV (33.3%), followed by R-BF, F-BF, and CT (14%, 14%, and 11% of the specimens, respectively). Teeth restored with regular and flowable bulk-fill composites showed similar fracture toughness after the chewing simulation compared to those restored with the conventional resin composite and unprepared teeth. Furthermore, teeth restored with both regular and flowable bulk-fill composites showed a lower incidence of enamel cracks and fractures below the CEJ compared to those restored with the conventional resin composite.
Assuntos
Resinas Compostas , Mastigação , Resinas Compostas/uso terapêutico , Resinas Acrílicas , Poliuretanos , Dente Molar , Teste de Materiais , Restauração Dentária Permanente/métodosRESUMO
This clinical case describes an esthetic rehabilitation of a young patient presenting with erosive tooth wear. The etiological factors for the erosion in this clinical case was excessive carbonated beverages and lemon water intake. The patient's main complaint was the yellowish aspect of her smile. The treatment procedure selected was direct resin composite veneers in the six maxillary anterior teeth. A three-year follow-up of the case is presented. The three-year follow-up showed a successful clinical performance of the treatment procedure after a finishing/polishing protocol.