RESUMO
Biosilicate is a bioactive glass-ceramic used in medical and dental applications. This study evaluated novel reparative materials composed of pure tricalcium silicate (TCS), 30% zirconium oxide (ZrO2 ) and 10 or 20% biosilicate, in comparison with Biodentine. Setting time was evaluated based on ISO 6876 standard, radiopacity by radiographic analysis, solubility by mass loss, and pH by using a pH meter. Cytotoxicity was evaluated by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide and NR assays. Alkaline phosphatase (ALP) activity and alizarin red were used to evaluate cell bioactivity. Antimicrobial activity was assessed on Enterococcus faecalis by the direct contact test. The data were submitted to analysis of variance (ANOVA)/Tukey; Bonferroni and Kruskal-Wallis, and Dunn tests (α = 0.05). The association of Biosilicate with TCS + ZrO2 had appropriate setting time, radiopacity, and solubility, alkaline pH, and antimicrobial activity. TCS and Biodentine showed higher ALP activity in 14 days than the control (serum-free medium). All cements produced mineralized nodules. In conclusion, Biosilicate + TCS ZrO2 decreased the setting time and increased the radiopacity in comparison to TCS. Biosilicate + TCS ZrO2 presented lower solubility and higher radiopacity than Biodentine. In addition, these experimental cements promoted antimicrobial activity and mineralization nodules formation, suggesting their potential for clinical use.
Assuntos
Compostos de Cálcio/química , Vidro/química , Silicatos/química , Zircônio/química , Fosfatase Alcalina , Antraquinonas , Materiais Biocompatíveis , Cimentos Ósseos , Neoplasias Ósseas/patologia , Compostos de Cálcio/farmacologia , Compostos de Cálcio/toxicidade , Linhagem Celular Tumoral , Cimentos Dentários , Enterococcus faecalis/efeitos dos fármacos , Humanos , Concentração de Íons de Hidrogênio , Teste de Materiais , Osteossarcoma/patologia , Cimento de Silicato , Silicatos/farmacologia , Silicatos/toxicidade , Solubilidade , Zircônio/farmacologia , Zircônio/toxicidadeRESUMO
OBJECTIVE: To evaluate the cytotoxicity, genotoxicity and antibacterial activity of poly(vinyl alcohol)-coated silver nanoparticles (AgNPs-PVA) and farnesol (FAR). DESIGN: The cytotoxicity (% of cell viability) was evaluated by MTT assay and the genotoxicity (% of DNA in the tail) was evaluated by Comet assay. Root canal disinfection with different irrigating protocols was evaluated ex vivo in human teeth contaminated with Enterococcus faecalis for 21days. Three microbiological samples were collected: initial (after contamination); post-irrigation (after irrigation); and final (after 7days). After each sample, the number of log 10 CFU mL-1 was determined. Statistical analyses was performed using two-way ANOVA and Bonferroni post-hoc tests for MTT assay, Kruskal-Wallis and Dunn post-hoc tests for Cometa and antibacterial assays (α=0.05). RESULTS: The MTT assay showed that AgNPs and FAR were less cytotoxic that sodium hypochlorite (NaOCl) and showed a lower% of DNA in the tail, in comparison with H2O2 (positive control - C+). In the post-irrigation microbiological sample, all the irrigating protocols were more effective than C+ (without irrigation). NaOCl/saline, NaOCl/saline/AgNPs-PVA and NaOCl/saline/FAR led to complete bacterial elimination (p >0.05). In comparison with the initial sample, both the post-irrigation and the final samples showed microbial reduction (p < 0.05). CONCLUSIONS: AgNPs-PVA and FAR showed low cytotoxicity and genotoxicity, and exhibit potential for use as a final endodontic irrigation protocols.