RESUMO

The aim of this study was to evaluate the effect of radiopacifier calcium tungstate and manipulation with distilled water (DW) or liquid with additives (LA) on calcium silicate clinker Angelus (CL) properties, compared with MTA (Angelus, Brazil) and MTA Repair HP (MTAHP, Angelus, Brazil). The physicochemical properties, cellular viability and bioactivity were evaluated. ANOVA/Tukey and Bonferroni tests were performed (α = 0.05). There was no difference in material setting time (p > 0.05). MTA and MTAHP were similar (p > 0.05) and had greater radiopacity than CL + DW and CL + LA (p < 0.05). All experimental materials showed mass increase, alkalinisation capacity, besides biocompatibility and bioactivity at 3 and 7 days. The different liquids had no influence in the biological properties and bioactivity of the calcium silicate clinker Angelus. Calcium tungstate provided radiopacity, without changing the setting time, maintaining the mass increase and alkalinisation ability of the calcium silicate materials.

Assuntos

RESUMO

The aim of this study was to evaluate the physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic material, Bio-C Repair (Angelus), in comparison with White MTA (Angelus) and Biodentine (Septodont). The physicochemical properties of setting time, radiopacity, pH, solubility, dimensional and volumetric changes were evaluated. Biocompatibility and bioactivity were assessed in Saos-2 osteoblast cell cultures by the MTT assay 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), Neutral Red (NR), Alizarin Red (ARS), and cell migration tests. Statistical analysis was performed by ANOVA, Tukey or Bonferroni tests (α = 0.05). Bio-C Repair had the longest setting time (p < 0.05), but radiopacity and solubility were accordance with the ISO 6876/2012 standards, besides linear expansion. Bio-C Repair and MTA had similar volumetric change (p > 0.05); lower than Biodentine (p < 0.05). All the materials evaluated had an alkaline pH. Bio-C Repair was cytocompatible and promoted mineralized nodule deposition in 21 days and cell migration in 3 days. In conclusion, Bio-C Repair had adequate radiopacity above 3mm Al, solubility less than 3%, dimensional expansion, and low volumetric change. In addition, Bio-C Repair promoted an alkaline pH and presented bioactivity and biocompatibility similar to MTA and Biodentine, showing potential for use as a repair material.

Assuntos

RESUMO

Abstract The aim of this study was to evaluate the physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic material, Bio-C Repair (Angelus), in comparison with White MTA (Angelus) and Biodentine (Septodont). The physicochemical properties of setting time, radiopacity, pH, solubility, dimensional and volumetric changes were evaluated. Biocompatibility and bioactivity were assessed in Saos-2 osteoblast cell cultures by the MTT assay 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), Neutral Red (NR), Alizarin Red (ARS), and cell migration tests. Statistical analysis was performed by ANOVA, Tukey or Bonferroni tests (α = 0.05). Bio-C Repair had the longest setting time (p < 0.05), but radiopacity and solubility were accordance with the ISO 6876/2012 standards, besides linear expansion. Bio-C Repair and MTA had similar volumetric change (p > 0.05); lower than Biodentine (p < 0.05). All the materials evaluated had an alkaline pH. Bio-C Repair was cytocompatible and promoted mineralized nodule deposition in 21 days and cell migration in 3 days. In conclusion, Bio-C Repair had adequate radiopacity above 3mm Al, solubility less than 3%, dimensional expansion, and low volumetric change. In addition, Bio-C Repair promoted an alkaline pH and presented bioactivity and biocompatibility similar to MTA and Biodentine, showing potential for use as a repair material.

Resumo O objetivo deste estudo foi avaliar as propriedades físico-químicas, citotoxicidade e bioatividade de um novo material biocerâmico pronto para uso, Bio-C Repair (Angelus), em comparação com MTA Branco (Angelus) e Biodentine (Septodont). Foram avaliadas as propriedades físico-químicas de tempo de presa, radiopacidade, pH, solubilidade, alterações dimensionais e volumétricas. A biocompatibilidade, bioatividade e capacidade de reparo foram avaliadas em culturas de células de osteoblastos Saos-2 pelo ensaio MTT brometo de 3-(4,5-dimetiltiazol-2-il)-2,5-difeniltetrazólio), vermelho neutro (NR), vermelho de alizarina ( ARS) e testes de migração celular. A análise estatística foi realizada pelos testes ANOVA, Tukey ou Bonferroni (α = 0,05). Bio-C Repair apresentou o maior tempo de presa (p < 0,05), mas radiopacidade e solubilidade de acordo com as normas ISO 6876/2012, além de expansão linear. Bio-C Repair e MTA tiveram variação volumétrica semelhante (p > 0,05), menor que Biodentine (p < 0,05). Todos os materiais avaliados apresentaram pH alcalino. Bio-C Repair foi citocompatível, além de promover deposição de nódulos mineralizados em 21 dias e migração celular em 3 dias. Em conclusão, o Bio-C Repair apresentou radiopacidade adequada acima de 3mmAl, solubilidade menor que 3%, expansão dimensional e baixa perda volumétrica.. Além disso, o Bio-C Repair promoveu um pH alcalino e apresentou bioatividade e biocompatibilidade semelhantes ao MTA e Biodentine, mostrando potencial para uso como material reparador

RESUMO

Modified formulations of calcium silicate repair materials with additives have been developed to enhance handling, consistency, biocompatibility and bioactivity. Considering the relevance of osteoblastic cell response to mineralized tissue repair, human osteoblastic cells (Saos-2 cells overexpressing BMP-2) were exposed to mineral trioxide aggregate (MTA) (with calcium tungstate - CaWO4), MTA HP Repair, Bio-C Repair and Bio-C Pulpo. Cell viability was assessed by 3-(4,5-dimethylthiazol)-2,5-diphenyltetrazolium bromide (MTT) and neutral red (NR), and cell death, by flow cytometry. Gene expression of bone morphogenetic protein 2 (BMP-2), runt-related transcription factor 2 (RUNX-2), and alkaline phosphatase (ALP) osteogenic markers were evaluated by real-time polymerase chain reaction (RT-qPCR). ALP activity and alizarin red staining (ARS) were used to detect mineralization nodule deposition. Bioactive cements presented no cytotoxic effect, and did not induce apoptosis at the higher dilution (1:12). MTA, Bio-C Repair and Bio-C Pulpo exhibited higher ALP activity than the control group (P < 0.05) after 7 days. MTA, MTA HP and Bio-C Pulpo affected the formation of mineralized nodules (p < 0.05). Exposure to all cement extracts for 1 day increased BMP-2 gene expression. RUNX-2 mRNA was greater in MTA, MTA HP and Bio-C Repair. MTA, MTA HP and Bio-C Pulpo increased the ALP mRNA expression, compared with BMP-2 unexposed cells (P < 0.05). Calcium silicate cements showed osteogenic potential and biocompatibility in Saos-2 cells transfected BMP-2, and increased the mRNA expression of BMP-2, RUNX-2, and ALP osteogenic markers in the BMP-2 transfected system, thereby promoting a cellular response to undertake the mineralized tissue repair.

Assuntos

RESUMO

OBJECTIVE: To assess the effects of different peracetic acid (PAA) formulations on smear layer (SL) removal, dentine erosion, cytotoxicity, and antibiofilm activity. METHODOLOGY: SL removal and dentine erosion were assessed using 90 premolars, distributed into six groups, according to final irrigation: PAA formulations (1% Sigma, 1% Bacterend OX, 1% Arposept, and 0.09-0.15% Anioxyde), 17% ethylenediaminetetraacetic acid (EDTA), and water (control). Cytotoxicity was assessed by methyl-thiazol-tetrazolium (MTT) and neutral red assays. Antibacterial and antibiofilm effectiveness was evaluated against Enterococcus faecalis. For cytotoxicity and antibiofilm activity assessment, the 2.5% NaOCl was also included. RESULTS: EDTA, Sigma, and Bacterend OX removed more SL than Arposept, Anioxyde, and water (p<0.05). EDTA caused more severe dentine erosion than Sigma and Bacterend OX (p<0.05). Sigma and Bacterend OX had higher cytotoxicity than the other solutions (p<0.05). NaOCl, Bacterend OX, Sigma, and Anioxyde significantly reduced E. faecalis colony-forming units (CFU) (p<0.05). The 2.5% NaOCl solution promoted greater biofilm biomass reduction (p<0.05) than the other solutions. All PAA formulations promoted greater biomass reduction than 17% EDTA (p<0.05). CONCLUSIONS: Although Sigma and Bacterend OX had higher cytotoxicity, they had a SL removal capability similar to that of EDTA, were as effective as NaOCl against E. faecalis biofilm, and promoted less dentine erosion than EDTA. Arposept and Anioxyde failed to remove the SL, had lower cytotoxicity, and showed less bacterial activity than NaOCl.

Assuntos

RESUMO

This study evaluated the physicochemical and biological properties of novel reparative materials composed of pure tricalcium silicate (Ca3 SiO5 ), Ca3 SiO5 doped with fluoride ions (Ca3 SiO5 -F) and their association with ZrO2 (Ca3 SiO5 + ZrO2 , Ca3 SiO5 -F + ZrO2 ), in comparison with Biodentine (BIO). Setting time radiopacity, pH, solubility, and dimensional change were evaluated based on ISO 6876 Standard. Volumetric change and flow/filling were assessed by microcomputed tomography (micro-CT). Biological properties were evaluated by the MTT assay 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), Neutral Red (NR), cell migration, alkaline phosphatase activity (ALP), and Alizarin Red Staining (ARS) assays. Statistical analysis was performed by ANOVA, Tukey, or Bonferroni tests (α = .05). Ca3 SiO5 -F + ZrO2 had higher radiopacity, shorter setting time, and lower solubility and volumetric loss than BIO (p < .05). Ca3 SiO5 -F + ZrO2 had flow and filling capacity similar to BIO (p > .05). All the cements evaluated had an alkaline pH. Ca3 SiO5 -F + ZrO2 demonstrated cell viability similar to negative control (p > .05), increase in ALP activity in 7 days, mineralized nodule production in 21 days and repair capacity according to cell migration. In conclusion, Ca3 SiO5 -F + ZrO2 had adequate setting time, radiopacity, solubility, and dimensional change. This material presented low volumetric change besides flow and filling capacity in micro-CT assessment. In addition, Ca3 SiO5 -F + ZrO2 was biocompatible and bioactive, suggesting its use as reparative material.

Assuntos

RESUMO

Abstract: Modified formulations of calcium silicate repair materials with additives have been developed to enhance handling, consistency, biocompatibility and bioactivity. Considering the relevance of osteoblastic cell response to mineralized tissue repair, human osteoblastic cells (Saos-2 cells overexpressing BMP-2) were exposed to mineral trioxide aggregate (MTA) (with calcium tungstate - CaWO4), MTA HP Repair, Bio-C Repair and Bio-C Pulpo. Cell viability was assessed by 3-(4,5-dimethylthiazol)-2,5-diphenyltetrazolium bromide (MTT) and neutral red (NR), and cell death, by flow cytometry. Gene expression of bone morphogenetic protein 2 (BMP-2), runt-related transcription factor 2 (RUNX-2), and alkaline phosphatase (ALP) osteogenic markers were evaluated by real-time polymerase chain reaction (RT-qPCR). ALP activity and alizarin red staining (ARS) were used to detect mineralization nodule deposition. Bioactive cements presented no cytotoxic effect, and did not induce apoptosis at the higher dilution (1:12). MTA, Bio-C Repair and Bio-C Pulpo exhibited higher ALP activity than the control group (P < 0.05) after 7 days. MTA, MTA HP and Bio-C Pulpo affected the formation of mineralized nodules (p < 0.05). Exposure to all cement extracts for 1 day increased BMP-2 gene expression. RUNX-2 mRNA was greater in MTA, MTA HP and Bio-C Repair. MTA, MTA HP and Bio-C Pulpo increased the ALP mRNA expression, compared with BMP-2 unexposed cells (P < 0.05). Calcium silicate cements showed osteogenic potential and biocompatibility in Saos-2 cells transfected BMP-2, and increased the mRNA expression of BMP-2, RUNX-2, and ALP osteogenic markers in the BMP-2 transfected system, thereby promoting a cellular response to undertake the mineralized tissue repair.

RESUMO

Abstract Objective: To assess the effects of different peracetic acid (PAA) formulations on smear layer (SL) removal, dentine erosion, cytotoxicity, and antibiofilm activity. Methodology: SL removal and dentine erosion were assessed using 90 premolars, distributed into six groups, according to final irrigation: PAA formulations (1% Sigma, 1% Bacterend OX, 1% Arposept, and 0.09-0.15% Anioxyde), 17% ethylenediaminetetraacetic acid (EDTA), and water (control). Cytotoxicity was assessed by methyl-thiazol-tetrazolium (MTT) and neutral red assays. Antibacterial and antibiofilm effectiveness was evaluated against Enterococcus faecalis. For cytotoxicity and antibiofilm activity assessment, the 2.5% NaOCl was also included. Results: EDTA, Sigma, and Bacterend OX removed more SL than Arposept, Anioxyde, and water (p<0.05). EDTA caused more severe dentine erosion than Sigma and Bacterend OX (p<0.05). Sigma and Bacterend OX had higher cytotoxicity than the other solutions (p<0.05). NaOCl, Bacterend OX, Sigma, and Anioxyde significantly reduced E. faecalis colony-forming units (CFU) (p<0.05). The 2.5% NaOCl solution promoted greater biofilm biomass reduction (p<0.05) than the other solutions. All PAA formulations promoted greater biomass reduction than 17% EDTA (p<0.05). Conclusions: Although Sigma and Bacterend OX had higher cytotoxicity, they had a SL removal capability similar to that of EDTA, were as effective as NaOCl against E. faecalis biofilm, and promoted less dentine erosion than EDTA. Arposept and Anioxyde failed to remove the SL, had lower cytotoxicity, and showed less bacterial activity than NaOCl.

RESUMO

The aim of this study was to evaluate the physicochemical properties, cytocompatibility and antibiofilm activity of a new calcium silicate-based endodontic sealer, Sealer Plus BC (MK Life, Brazil), in comparison with TotalFill BC Sealer (FKG Dentaire SA, Switzerland) and AH Plus (Dentsply, Germany). Setting time and flow were evaluated based on ISO 6876 standard. The pH was evaluated after different periods, and radiopacity by radiographic analysis (mmAl). Solubility (% mass loss) and volumetric change (by micro-CT) were assessed after 30 days of immersion in distilled water. Cytocompatibility was assessed by methyltetrazolium (MTT) and neutral red (NR) assays, after exposure of Saos-2 cells to the sealer extract for 24 h. An additional analysis was performed by using MTT assay after 1, 3 and 7 days of exposure of Saos-2 to the sealers 1:8 dilution extracts. Antibiofilm activity against Enterococcus faecalis and/or Candida albicans was evaluated by crystal violet assay and modified direct contact test. The physicochemical properties were analyzed using ANOVA/Tukey tests; MTT and NR data were analyzed by ANOVA and Bonferroni tests; the antimicrobial tests were analyzed by Kruskal-Wallis and Dunn tests (α=0.05). Sealer Plus BC had proper setting time, radiopacity, flow and alkalization capacity. Sealer Plus BC was significantly more soluble than AH Plus (p<0.05) and presented volumetric change similar to AH Plus and TotalFill BC (p>0.05). Sealer Plus BC presented antibiofilm activity and no cytotoxic effect. In conclusion, although Sealer Plus BC had higher solubility, this sealer showed proper physicochemical properties, cytocompatibility, and antibiofilm activity.

Assuntos

RESUMO

Abstract The aim of this study was to evaluate the physicochemical properties, cytocompatibility and antibiofilm activity of a new calcium silicate-based endodontic sealer, Sealer Plus BC (MK Life, Brazil), in comparison with TotalFill BC Sealer (FKG Dentaire SA, Switzerland) and AH Plus (Dentsply, Germany). Setting time and flow were evaluated based on ISO 6876 standard. The pH was evaluated after different periods, and radiopacity by radiographic analysis (mmAl). Solubility (% mass loss) and volumetric change (by micro-CT) were assessed after 30 days of immersion in distilled water. Cytocompatibility was assessed by methyltetrazolium (MTT) and neutral red (NR) assays, after exposure of Saos-2 cells to the sealer extract for 24 h. An additional analysis was performed by using MTT assay after 1, 3 and 7 days of exposure of Saos-2 to the sealers 1:8 dilution extracts. Antibiofilm activity against Enterococcus faecalis and/or Candida albicans was evaluated by crystal violet assay and modified direct contact test. The physicochemical properties were analyzed using ANOVA/Tukey tests; MTT and NR data were analyzed by ANOVA and Bonferroni tests; the antimicrobial tests were analyzed by Kruskal-Wallis and Dunn tests (α=0.05). Sealer Plus BC had proper setting time, radiopacity, flow and alkalization capacity. Sealer Plus BC was significantly more soluble than AH Plus (p<0.05) and presented volumetric change similar to AH Plus and TotalFill BC (p>0.05). Sealer Plus BC presented antibiofilm activity and no cytotoxic effect. In conclusion, although Sealer Plus BC had higher solubility, this sealer showed proper physicochemical properties, cytocompatibility, and antibiofilm activity.

Resumo O objetivo deste estudo foi avaliar as propriedades físico-químicas, a citocompatibilidade e a atividade antibiofilme de um novo cimento endodôntico à base de silicato de cálcio, Sealer Plus BC (MK Life, Brasil), em comparação com TotalFill BC Sealer (FKG Dentaire SA, Suíça) e AH Plus (Dentsply, Alemanha). O tempo de presa e o escoamento foram avaliados com base nas normas ISO 6876. O pH foi avaliado após diferentes períodos, e a radiopacidade por análise radiográfica (mmAl). A solubilidade (% de perda de massa) e alteração volumétrica (por micro-CT) foram avaliadas após 30 dias de imersão em água destilada. Citocompatibilidade foi avaliada pelos ensaios metiltetrazólio (MTT) e vermelho neutro (NR), após exposição das células Saos-2 ao extrato de cimento por 24 horas. Análise adicional foi realizada através do ensaio MTT após 1, 3 e 7 dias de exposição das células Saos-2 aos extratos dos cimentos na diluição de 1:8. Atividade antibiofilme contra Enterococcus faecalis e/ou Candida albicans foi avaliada pelos ensaios cristal violeta e contato direto modificado. As propriedades físico-químicas foram analisadas utilizando os testes ANOVA e Tukey; MTT e NR foram analisados pelos testes ANOVA e Bonferroni; os ensaios antimicrobianos foram analisados pelos testes Kruskal-Wallis e Dunn (α=0.05). Sealer Plus BC apresentou tempo de presa, radiopacidade e escoamento adequados, além de capacidade de alcalinização. Sealer Plus BC foi significantemente mais solúvel que AH Plus (p<0.05) e apresentou alteração volumétrica similar à de AH Plus e TotalFill BC (p>0.05). Sealer Plus BC apresentou atividade antibiofilme, sem efeito citotóxico. Como conclusão, embora Sealer Plus BC apresente maior solubilidade, este cimento apresentou propriedades físico-químicas adequadas, citocompatibilidade e atividade antibiofilme.

Assuntos