RESUMO
Bone regeneration and natural repair are long-standing processes that can lead to uneven new tissue growth. By introducing scaffolds that can be autografts and/or allografts, tissue engineering provides new approaches to manage the major burdens involved in this process. Polymeric scaffolds allow the incorporation of bioactive agents that improve their biological and mechanical performance, making them suitable materials for bone regeneration solutions. The present work aimed to create chitosan/beta-tricalcium phosphate-based scaffolds coated with silk fibroin and evaluate their potential for bone tissue engineering. Results showed that the obtained scaffolds have porosities up to 86%, interconnectivity up to 96%, pore sizes in the range of 60-170 µm, and a stiffness ranging from 1 to 2 MPa. Furthermore, when cultured with MC3T3 cells, the scaffolds were able to form apatite crystals after 21 d; and they were able to support cell growth and proliferation up to 14 d of culture. Besides, cellular proliferation was higher on the scaffolds coated with silk. These outcomes further demonstrate that the developed structures are suitable candidates to enhance bone tissue engineering.
Assuntos
Quitosana , Fibroínas , Fosfatos de Cálcio , Proliferação de Células , Fibroínas/química , Porosidade , Seda/química , Engenharia Tecidual/métodos , Alicerces Teciduais/químicaRESUMO
BACKGROUND: The use of scanning electron microscopy (SEM) and energy-dispersive spectrometry (EDS) was investigated to understand the wear mechanisms from a metal-on-polyethylene bearing couple. Morphological features of femoral head acetabular liner, and isolated particles resulting from hip wear testing were evaluated. EDS was proposed to investigate the polymeric nature of the particles isolated from the wear testing. METHODS: In this work, 28-mm conventional ultra-high-molecular-weight polyethylene acetabular liners paired with metallic heads were tested in a hip wear simulator over 2 million cycles. SEM-EDS was employed to investigate wear mechanisms on hip implant components and associated wear debris. RESULTS: SEM showed worn surfaces for both hip components, and a significant volume of ultra-high-molecular-weight polyethylene wear particles resulting from hip wear testing. Particles were classified into 3 groups, which were then correlated to wear mechanisms. Group I had particles with smooth surfaces, group II consisted of particles with rough surfaces, and group III comprised aggregate-like particles. Group I EDS revealed that particles from groups I and II had a high C/O ratio raising a concern about the particle source. On the other hand, particles from group III had a low C/O ratio, supporting the hypothesis that they resulted from the wear of acetabular liner. Most of particles identified in group III were in the biologically active size range (0.3 to 20 µm). CONCLUSION: The use of optical and electron microscopy enabled the morphological characterization of worn surfaces and wear debris, while EDS was essential to elucidate the chemical composition of isolated debris.