RESUMO
The purpose of this study was to investigate the tensile bond strength (TBS) and shear bond strength (SBS) between a zirconia core and fluoroapatite-pressed ceramic after the application of glass 46SP6 and AP40 via the ISO-17095:2013 methodology. Sintered zirconia beams (n = 120) were divided into four groups: (a) control: no treatment; (b) ZirL: IPS-E max ceram ZirLiner coating; (c) glass AP40 coating; and (d) glass 46SP6 coating. A fluoroapatite ceramic (IPS e.max Zir Press, Ivoclar Vivadent) beam was injected perpendicularly on top of each zirconia (Zenostar, Wieland Dental) beam forming a cross-bonded specimen. All groups were sub-divided into two for tensile and shear bond strength tests using a universal testing machine. Data were analyzed using the Kruskal-Wallis, Pearson Chi2, and Mann-Whitney U test (α = 0.05). The failure modes were measured using a stereomicroscope for each group. Scanning electron and atomic force microscopy were also employed. Zirconia surface modification with glass AP40 showed higher TBS values followed by the ZirL group with statistical differences (p < 0.05). SBS values showed no statistical differences between the groups. AFM analysis showed higher roughness values (Ra) in the 46SP6 and AP40 groups (p < 0.05). Glass coating AP40 exhibited promising bond strength results between zirconia and fluorapatite veneering ceramic, making it better for chemical and mechanical interlocking which may improve bilayered restorations longevity.