BACKGROUND: Radiotherapy can affect healthy cells, resulting in side effects. This study aimed to assess the impact of radiotherapy on soft tissue in surgical wounds in rats. METHODS: The animals were divided into four groups: control (S) group without irradiation, immediate irradiation (S-IIr) group receiving irradiation right after surgery, late irradiation (S-LIr) group receiving irradiation four weeks after surgery, and early irradiation (Ir-S) group receiving irradiation before surgery. The irradiated groups underwent two fractional stages of 15 Gy. Muscle contractibility (EMG) was evaluated at two different time points, and after 2 and 7 weeks, the animals were euthanized for histological analysis of the muscles and skin. RESULTS: There was no significant difference between the EMG1 and EMG2 values of the S and S-LIr groups, but both S-IIr and Ir-S groups exhibited a statistically significant difference. The S group demonstrated a larger diameter of muscle fiber compared to other groups, showing a significant difference. In terms of skin analysis, the S-IIr group had the least inflammatory infiltrate and the highest amount of red fibers, differing significantly from the other groups. CONCLUSIONS: Regardless of the duration, radiotherapy was found to have effects on the surrounding soft tissues, as concluded by this study.
RESUMO
OBJECTIVES: The purpose of this study was to evaluate the flexural strength and Vickers hardness of a microwave energy heat-cured acrylic resin by adding different concentrations of silane surface-treated nanoparticle silica. METHODS: Acrylic resin specimens with dimensions of 65 × 10 × 2.5 mm were formed and divided into five experimental groups (n = 10) according to the silica concentration added to the acrylic resin mass (weight %) prior to polymerisation : G1, without silica; G2, 0.1% silica; G3, 0.5% silica; G4, 1.0% silica; and G5, 5.0% silica. The specimens were submitted to a three-point flexural strength test and to the Vickers hardness test (HVN). The data obtained were statistically analysed by anova and the Tukey test (α = 0.05). RESULTS: Regarding flexural strength, G5 differed from the other experimental groups (G1, G2, G3 and G4) presenting the lowest mean, while G4 presented a significantly higher mean, with the exception of group G3. Regarding Vickers hardness, a decrease in values was observed, in which G1 presented the highest hardness compared with the other experimental groups. CONCLUSION: Incorporating surface-treated silica resulted in direct benefits in the flexural strength of the acrylic resin activated by microwave energy; however, similar results were not achieved for hardness.