RESUMO
Color reintegration is a restoration treatment that involves applying paint or colored plaster to an object of cultural heritage to facilitate its perception and understanding. This study examines the impact of lighting on the visual appearance of one such restored piece: a tiled skirting panel from the Nasrid period (1238-1492), permanently on display at the Museum of the Alhambra (Spain). Spectral images in the range of 380-1080 nm were obtained using a hyperspectral image scanner. CIELAB and CIEDE2000 color coordinates at each pixel were computed assuming the CIE 1931 standard colorimetric observer and considering ten relevant illuminants proposed by the International Commission on Illumination (CIE): D65 plus nine white LEDs. Four main hues (blue, green, yellow, and black) can be distinguished in the original and reintegrated areas. For each hue, mean color difference from the mean (MCDM), CIEDE2000 average distances, volumes, and overlapping volumes were computed in the CIELAB space by comparing the original and the reintegrated zones. The study reveals noticeable average color differences between the original and reintegrated areas within tiles: 6.0 and 4.7 CIEDE2000 units for the yellow and blue tiles (with MCDM values of 3.7 and 4.5 and 5.8 and 7.2, respectively), and 16.6 and 17.8 CIEDE2000 units for the black and green tiles (with MCDM values of 13.2 and 12.2 and 10.9 and 11.3, respectively). The overlapping volume of CIELAB clouds of points corresponding to the original and reintegrated areas ranges from 35% to 50%, indicating that these areas would be perceived as different by observers with normal color vision for all four tiles. However, average color differences between the original and reintegrated areas changed with the tested illuminants by less than 2.6 CIEDE2000 units. Our current methodology provides useful quantitative results for evaluation of the color appearance of a reintegrated area under different light sources, helping curators and museum professionals to choose optimal lighting.
RESUMO
OBJECTIVE: To evaluate the optical properties and the relative translucency parameter of Ceramill ZI White (3Y-TZP) and Ceramill Zolid FX White (5Y-PSZ) zirconia ceramic systems and compare them with those of the bovine dentin and enamel/dentin structures. MATERIALS AND METHODS: 3Y-TZP and 5Y-PSZ zirconia ceramic systems were evaluated. A 0.5-mm-thick 3Y-TZP (3Y-NC.5), 0.5-mm-thick (5Y-NC.5), and 1.4-mm-thick (5Y-C.14) were used. A 0.5-mm-thick dentin specimens and 1.4-mm-thick enamel/dentin specimens (n = 5) were obtained from anterior bovine maxillary teeth. Scattering, absorption, transmittance, and albedo coefficient were calculated using Kubelka-Munk's model. Data were statistically analyzed using Kruskal-Wallis and Mann-Whitney tests (p < 0.001), and goodness-of-fit coefficient (GFC). Relative translucency parameter differences were evaluated using translucency thresholds. RESULTS: Reflectance, scattering, absorption, and transmittance properties were wavelength dependent. Good matches (GFC ≥ 0.999) in spectral reflectance were observed between 0.5-mm-thick dentin and 1.4-mm-thick enamel/dentin, and 3Y-NC.5 and 5Y-NC.5. Scattering was the main optical extinction process during light interaction with zirconia and dental structures, as indicated by albedo coefficient. Translucency differences were acceptable only for 3Y-NC.5 and the dentin structure, and 5Y-C.14 and the enamel/dentin structure. CONCLUSIONS: Optical properties of 3Y-TZP and 5Y-PSZ dental zirconia differed from each other and from bovine dental structures. Nevertheless, 3Y-TZP showed similar relative translucency parameter to bovine dentin. CLINICAL SIGNIFICANCE: To achieve the best esthetic results in restorative dentistry, it is crucial for clinicians to know about the optical properties of 3Y-TZP and 5Y-PSZ and to be able to compare these properties with those of dental structures.