RESUMO
OBJECTIVE: To evaluate the effect of a Nisin-based dentin pretreatment solution on microtensile bond strength, antibacterial activity, and matrix metalloproteinase (MMP) activity of the adhesive interface. MATERIALS AND METHODS: 100 human molars were sectioned to expose dentin. The teeth were assigned to five groups (n = 20), according to the dentin pretreatment: 0.5%, 1.0%, or 1.5% Nisin; 0.12% chlorhexidine (positive control), and no solution (negative control), and divided into 2 subgroups: no aging, and thermomechanical aging. Specimens were etched with 37% H3PO4 for 15 s and submitted to the dentin pretreatment. Then, they were bonded with an adhesive (Adper Single Bond 2) and a resin composite for microtensile bond strength (µTBS) evaluation. Antibacterial activity against Streptococcus mutans was qualitatively examined using an agar diffusion test. Anti-MMP activity within hybrid layers was examined using in-situ zymography. Data were analyzed with two-factor ANOVA and post-hoc Tukey's test (α = 0.050). RESULTS: For µTBS, significant differences were identified for the factors "solutions" (p = 0.002), "aging" (p = 0.017), and interaction of the two factors (p = 0.002). In the absence of aging, higher µTBS was observed for the group 0.5% Nisin. In the presence of aging, all groups showed similar µTBS values. All Nisin concentrations were effective in inhibiting the growth of S. mutans. Endogenous MMP activity was more significantly inhibited using 0.5% and 1.0% Nisin (p < 0.050). CONCLUSION: 0.5% and 1.0% Nisin solutions do not adversely affect resin-dentin bond strength and exhibit a potential bactericidal effect against S. mutans. Both concentrations effectively reduce endogenous gelatinolytic activity within the hybrid layer. CLINICAL RELEVANCE: The use of 0.5% and 1.0% Nisin solutions for dentin pretreatment potentially contributes to preserving the adhesive interface, increasing the longevity of composite restorations.
Assuntos
Colagem Dentária , Nisina , Humanos , Nisina/farmacologia , Nisina/análise , Adesivos/análise , Dentina/química , Antibacterianos/farmacologia , Resinas Compostas/química , Resistência à Tração , Adesivos Dentinários/química , Cimentos de Resina/análise , Teste de MateriaisRESUMO
BACKGROUND: This study aimed to evaluate surface treatments, adhesives and composites for repairing silorane based restorations. MATERIAL AND METHODS: One hundred and twenty truncated cones (2 mm smaller diameter and 4 mm larger diameter) made of silorane composite were divided in 12 groups according with the surface treatment (diamond bur and oxide aluminum abrasion), the adhesive (Adper Scothbond Multipurpose (3M ESPE), Ecusit (Voco) and Filtek P90 Adhesive (3M ESPE)). Each group was subdivided in two according with the composite used for repair (methacrylate and silorane). The repair was made with a second truncated cone build over the first one and bond strength assssed by tensile strength. Data were submitted to ANOVA 3-way and Tukey's test (p<0.05). RESULTS: There was difference only for the adhesives and the composites, with conventional adhesives (Adper Scothbond Mutipurpose) and methacrylate-based composites (Filtek Z350) presenting superior tensile strength compared to the silorane ones (P90 Adhesive system and composite). CONCLUSIONS: Therefore, it must be concluded that silorane composite can be repaired with methacrylate base composites and adhesives. Key words:Silorane composites, composites, bond strength, minimal intervention.
RESUMO
Background: Burning mouth syndrome (BMS) is a non-neuropathic chronic orofacial pain condition, characterized by the presence of burning/warm sensation without specific mucosal lesions. Objective: The aim of the present clinical case report is to describe the positive outcome of dental treatment of a patient with BMS and followed up for 25 years. Data Treatment: This report describes the case of a 50-year-old black woman sought treatment for burning, and persistent swelling of tong (24h/day) occurring over years. Clinical evaluation of the oral environment revealed the tongue with cracking, darkened points areas, surrounded by whitish areas. Twelve teeth presented extensive amalgam restorations. Patch testing revealed a very strong hypersensitivity to Amalgam. All amalgam restorations were substituted by composite resin restorations. Results and Conclusion: Burning sensation disappeared completely after these restorations had been changed. After 25-year follow-up period, it was observed that burning sensation has never been felt anymore. Clinical Significance: Burning mouth syndrome is a chronic orofacial pain, usually without specific mucosal lesions. The etiology is complex and multifactorial and the treatment should be made specifically for each pacient. (AU)
Introdução: A síndrome de ardência bucal (SAB) é uma condição de dor orofacial crônica não neuropática, caracterizada pela presença de sensação de queimação/calor sem lesões específicas da mucosa. Objetivo: Oobjetivo do presente relato de caso clínico é descrever a evolução positiva do tratamento odontológico de uma paciente com SAB e o retorno após 25 anos. Tratamento dos Dados: Este relato descreve o caso de uma mulher negra de 50 anos que buscou tratamento por queimadura e edema persistente da língua (24h/dia) ocorrendo ao longo dos anos. A avaliação clínica da cavidade bucal revelou a língua com áreas fissuradas e áreas com pontos escurecidos circundadas por áreas esbranquiçadas. Doze dentes apresentavam restaurações extensas de amálgama de prata. O teste de contato revelou hipersensibilidade muito forte ao amálgama de prata. Todas as restaurações de amálgama de prata foram substituidas por restaurações de resina composta. Resultados e Conclusão: A sensação de queimação desapareceu completamente após a substituição das restaurações. Após um periodo de 25 anos, observou-se que a sensação de queimação nunca foi mais relatada. Significado Clínico: a síndrome da ardência bucal é uma dor orofacial crônica, geralmente sem lesões específicas da mucosa. A etiologia é complexa e multifatorial e o tratamento deve ser feito especificamente para cada paciente.(AU)
Assuntos
Humanos , Feminino , Adulto , Síndrome da Ardência Bucal , Resinas Compostas , Amálgama DentárioRESUMO
Dens invaginatus is a malformation affecting mainly the superior lateral incisors. It is defined as an infolding of the crown hard tissues, including the enamel and dentin, and can extend up to the root apex. Root canal treatment of this abnormality is considered difficult due to the complex anatomy presented by these teeth. This case series presents nonsurgical endodontic treatment in two cases of dens invaginatus (type II and III) in maxillary lateral incisors. This nonsurgical or conventional endodontic treatment results in healing of the periapical lesions associated with both cases, with no need for extra intervention e.g. surgical or invasive management. The manual instrumentation associated with sodium hypochlorite and calcium hydroxide were able to completely heal the lesions. Radiographic exams were carried out to control and asses the healing. Nonsurgical treatment was successful in both cases with adequate repair after a 6-year follow-up with radiographic and tomographic assessments.
Assuntos
Dens in Dente , Ápice Dentário , Criança , Dens in Dente/terapia , Feminino , Humanos , Masculino , Tratamento do Canal RadicularRESUMO
Introduction:This study serves as a warning to dentists and researchers that dual-cured resin cements may not polymerize completely under some prosthetic crowns. Objective: The aim of this study was to analyse the polymerization degree of dual-cured resin cements under prosthetic barrier, by microhardness test. Material and method: Three cements (Bistite II, RelyX ARC and Variolink II) were light-cured through different barriers, placed between the cement and the light source: G1: without barrier; G2: composite resin (Cesead); G3: Inceram alumina; G4: IPS Empress; G5: Inceram zirconia; G6: tooth fragment. Photopolymerization was carried out using a halogen light unit (650 mW/cm2); microhardness was evaluated using the Microhardness Tester FM 700, under a load of 50gf with a dwell time of 15s, at two evaluation times (30min and 24h). Result: The results were submitted to ANOVA and Tukey tests (5%). Both Inceram alumina and Inceram zirconia ceramic barriers hindered polymerization. Bistite, followed by RelyX and Variolink, exhibited the highest microhardness values (p< 0.05). As the highest values were obtained without a barrier, it was determined that the barrier, followed by the tooth, influenced microhardness. Both Empress and Cesead had the smallest microhardness values but with no statistically significant difference between them. Conclusion: The barrier negatively affected the microhardness of dual-cured resin cements; evaluation time did not affect microhardness values for most of the conditions tested. There is a limited effect of the chemical activator on the polymerization of some dual-cured cements, and their performance is product specific.
Introdução: Este trabalho serve como um alerta para dentistas e pesquisadores, que alguns cimentos resinosos duais podem não polimerizar completamente sob alguns tipos de coroas protéticas. Objetivo: Analisar o grau de polimerização de cimentos resinos duais, sob barreiras protéticas, por teste de microdureza. Material e método: Três cimentos: Bistite II, RelyX ARC e Variolink II, foram fotopolimerizados através da interposição de vários tipos de barreiras, interpostas entre o cimento e a fonte de luz, formando os grupos: G1: sem barreira; G2: Resina composta Cesead; G3: Inceram alumina/Allceram; G4: IPS Empress; G5: Inceram zircônia/Allceram; G6: fragmento dental. Utilizou-se a luz halógena (650 mW/cm2) para fotoativação e a microdureza foi avaliada: 50gf durante 15s (MicrohardnessTester FM 700), em dois períodos (30min e 24h) pós ativação. Os dados foram submetidos à ANOVA e teste de Tukey (5%). As interposições de Inceram alumina e Inceram zircônia resultaram na polimerização deficiente dos cimentos, impossibilitando a realização dos ensaios. Resultado: Para o fator cimento, o Bistite revelou a maior microdureza, seguido do RelyX e do Variolink (p< 0,05). A barreira influenciou a microdureza, sendo que os maiores valores foram obtidos sem barreira, seguida do dente. Empress e Cesead proporcionaram os menores valores de microdureza e não diferiram entre si. Conclusão: A barreira afetou negativamente a microdureza dos cimentos resinosos duais; o período de avaliação não afetou os valores de microdureza para quase todas as condições testadas; existe um fator limitante do ativador químico na polimerização de alguns cimentos resinosos duais, e seu desempenho é dependente do produto.
Assuntos
Cimentos de Resina , Coroas , Polimerização , Análise de Variância , CimentaçãoRESUMO
Objetivo: Avaliar a resistência de união entre a resina composta e diferentes substratos de esmalte: hígido, esmalte desmineralizado submetido ou não a remineralização, e desmineralizado infiltrado com Icon (DMG). Material e Métodos: 120 dentes bovinos, cujas raízes foram removidas e o esmalte vestibular foi lixado. Os espécimes foram divididos em: Grupo A, controle, (n=24) que recebeu os procedimentos adesivos e restauradores para posterior teste de microtração; Grupo B (n=96), onde os corpos de prova (cdps) permaneceram imersos em solução desmineralizadora para produzir lesões subsuperficiais de cárie artificial, sendo subdividido em 4: B1, cdps somente desmineralizados; B2, cdps imersos em saliva artificial (8 semanas); B3, cdps imersos em solução de fluoreto 0,05% (1 minuto diariamente por 8 semanas); B4, cdps infiltrados com material resinoso (Icon, DMG). Todos os grupos receberam aplicação do sistema adesivo Clearfil S3 Bond Plus (Kuraray) ou Single Bond Universal (3M ESPE), seguida da resina composta Filtek Z 350 XT (3M ESPE). Os espécimes foram submetidos a ciclagem térmica e seccionados em prismas com dimensões aproximadas de 1mm² de base e submetidos ao teste de microtração. Resultados: os dados foram submetidos à ANOVA e ao Teste de Tukey (α= 5%).As médias em Mpa (±desvio padrão) foram: Clearfill S3 Bond Plus: Grupo Controle (17,17±3,52); B1 (11,60±0,74); B2 (6,83±1,87); B3 (8,38±1,59) e B4 (27,00±1,76); Single Bond Universal: Grupo Controle (26,26±3,19); B1 (10,94±2,00); B2 (11,05±1,74); B3 (15,63±1,25) e B4 (22,60±2,29). Conclusão: a superfície infiltrada com Icon não interferiu negativamente na resistência de união da resina composta ao esmalte e os grupos que foram desmineralizados e remineralizados com flúor e saliva artificial apresentaram valores estatisticamente inferiores aos demais.
Objective: To evaluate the bond strength between resin composite and differentenamel substrates: sound enamel; demineralized enamel submitted or not to remineralization; and demineralized enamel infiltrated with an infiltrating resin. Materials and Methods: 120 bovine teeth were selected, the root portion was removed and the enamel finished. Specimens were divided into the following groups:(A) Control (n=24): adhesively treated and restored; (B) (n=96): the samples were immersed in a demineralization solution to create white spot lesions and divided into four subgroups: (B1)demineralized enamel; (B2) samples were stored in artificial saliva (8 weeks); (B3) samples were stored in a 0.05% sodium fluoride solution (1 minday/8 weeks); (B4) samples were treated with an infiltrantresin (Icon, DMG). The groups were treated with one of the following adhesives: Clearfil S3 Bond Plus (Kuraray) or Single Bond Universal (3M ESPE), followed by the resin composite application (Filtek Z 350 XT, 3M ESPE). The specimens were submitted to thermalcycling aging (10,000 ×; 2±5ºC, 50±55ºCand 37°±2°C). The specimens were sectioned into prism shapes with ~1mm² of base and submitted tomicrotensile test. The collected data were submitted to ANOVA and Tukey´s test (α= 5%). Results: The Means (±SD) in MPawere: Clearfill S3 BondPlus: Control (17.17±3.52); B1 (11.60±0.74); B2 (6.83±1.87); B3 (8.38±1.59) and B4 (27.00±1.76);Single Bond Universal: Control (26.26±3.19); B1 (10.94±2.00); B2 (11.05±1.74); B3 (15.63±1.25) and B4 (22.60±2.29). Conclusion: The surfaceinfiltrated withaninfiltrating resin(Icon) did not negatively affect the bond strength between resin composite and enamel. The demineralized and remineralized groups with sodium fluoride and artificial saliva presented statistically lower results when compared to the other groups
Assuntos
Animais , Bovinos , Cárie Dentária , Esmalte DentárioRESUMO
The aim of this study was to investigate the effects of Er:YAG and Nd:YAG lasers on the shear bond strength of composite resin to dentin. The coronal portion of 56 human molars was divided into three parts, and the dentin thickness was standardized at 2 mm. A 3-mm hole was marked in the center of each tooth with sealing tape paper. The specimens (n = 14) were then divided into four groups: (1) acid etching + Single Bond (SB) (control), (2) acid etching + SB + Nd:YAG laser irradiation (before adhesive curing), (3) thermal etching with the Er:YAG laser + SB, and (4) thermal etching with the Er:YAG laser + SB + Nd:YAG laser irradiation (before adhesive curing). A composite resin cylinder was built into the delimited area for conducting the shear bond strength test on the universal testing machine. The means ± standard deviations were: group 1, 17.05 ± 4.15 MPa; group 2, 16.90 ± 3.36 MPa; group 3, 12.12 ± 3.85 MPa; and group 4, 12.92 ± 2.73 MPa. Groups 1 and 2 presented significantly higher values than groups 3 and 4. It was concluded that conventional etching with 37% phosphoric acid yielded significantly higher bond strength values compared to thermal etching with the Er:YAG laser. The Nd:YAG laser did not significantly influence the bond strength.
Assuntos
Colagem Dentária , Dentina/ultraestrutura , Lasers de Estado Sólido/uso terapêutico , Condicionamento Ácido do Dente/métodos , Adesividade , Adulto , Bis-Fenol A-Glicidil Metacrilato/química , Resinas Compostas/química , Corrosão Dentária/métodos , Materiais Dentários/química , Análise do Estresse Dentário/instrumentação , Dentina/efeitos da radiação , Adesivos Dentinários/química , Humanos , Teste de Materiais , Ácidos Fosfóricos/química , Resistência ao Cisalhamento , Dióxido de Silício/química , Estresse Mecânico , Propriedades de Superfície , Temperatura , Fatores de Tempo , Água/química , Zircônio/químicaRESUMO
Tooth darkening compromised oral aesthetics and bleaching is a conservative and efficient method to reestablish it. The aim of this study was to assess the action of 35% hydrogen peroxide in specimens pigmented with different substances. Twenty fragments obtained from chicken eggshell measuring 0.5 x 0.5 cm were randomly divided into 5 groups (G1, G2, G3, G4 and G5) with 4 specimens each. These were previously photographed and pigmented respectively with coffee, cola-based soft drink, wine, beetroot and tobacco for a 48-hour period. In groups 1, 2 and 3, the specimens were directly immersed respectively into the first three substances. In group 4, beetroot was mixed with water to obtain a solution. In group 5, the specimens were submitted to tobacco smoke by the same period. The groups were again photographed and then submitted to bleaching with 35% hydrogen peroxide and photo-activated by laser for 20 min. After the final photographs, the images were analyzed thorugh Adobe Photoshop CS5 software. It was observed that wine most pigmented the specimens (33.34%), followed by coffee (10.35%), beetroot (9.56%), cola-based soft drink (8.85%) and tobacco (0.61%). The bleaching action was more effective on the specimens of G1 (93.9%) and G2 (91.55%), followed by G3 (71.09%), G4 (62.74%) and G5 (57.38%). It was concluded that the methodology was efficient in comparing the effectiveness of the bleaching agent on the pigments tested. The specimens pigmented with tobacco were those which exhibited the greater resistance to bleaching. Taking into consideration the use of this biological material, further studies are necessary to simulate the effects of many other substances onto tooth enamel
O escurecimento dos dentes compromete a estética bucal. O clareamento é um método conservador e eficaz para restabelecê-la. Neste trabalho foi avaliada a ação do peróxido de hidrogênio 35% em espécimes pigmentados com diferentes substâncias. Vinte fragmentos obtidos da casca do ovo, medindo 0,5 x 0,5 cm, foram divididos aleatoriamente em 5 grupos (G1, G2, G3, G4 e G5) com 4 espécimes em cada. Estes foram previamente fotografados e pigmentados respectivamente com café, refrigerante a base de cola, vinho, beterraba e cigarro, por um período de 48 horas. Nos grupos 1, 2 e 3 os espécimes foram imersos diretamente nas respectivas substâncias. No grupo 4, a beterraba foi batida com água para obtenção da solução. No grupo 5 os espécimes ficaram acondicionados na fumaça do cigarro pelo mesmo período. Os grupos foram novamente fotografados e posteriormente submetidos ao clareamento com peróxido de hidrogênio 35%, ativado com laser, por 20 min. Após as fotografias finais, as imagens foram analisadas no programa Adobe Photoshop CS5. Observou-se que o vinho foi o que mais pigmentou os espécimes (33,34%), seguido pelo café (10,35%), beterraba (9,56%), refrigerante a base de cola (8,85%) e cigarro (0,61%). A ação clareadora foi mais efetiva nos espécimes dos grupos G1 (93,9%) e G2 (91,55%), seguidos pelos grupos G3 (71,09%), G4 (62,74%) e por último o grupo G5 (57,38%). Concluiu-se que o método foi eficaz para comparar a efetividade do agente clareador nos pigmentos testados, sendo os espécimes impregnados com fumaça de cigarro os que apresentaram maior resistência ao clareamento>
Assuntos
Peróxido de Hidrogênio , Clareamento Dental , Descoloração de DenteRESUMO
Objectives: To evaluate in vitro the degree of marginal leakage in class V cavities irradiated with Nd:YAG laser onto enamel and dentin pretreated with bonding system (Single Bond, 3M ESPE) without light-curing. Material & Methods: Class V cavities were performed and standardized in 60 bovine incisors. After the acid etching, the teeth were divided into three groups: G1 Application of bonding system, irradiation with Nd:YAG laser at 140 mJ/pulse without light-curing. G2 Application of bonding system, irradiation with Nd:YAG laser at 200 mJ/pulse without light-curing. Group C Application of bonding system and light-curing. Next, resin composite restorations were executed and thermocycled at alternated baths from 2 to 50 ºC (± 2 ºC), totalizing 500 cycles. To assess the microleakage, the teeth were submersed into 50% silver nitrate solution for 24 h, cut at 1 mm of thickness and analyzed through stereoscopy. The following leakage criterion scores were employed: 0 none leakage; 1 gingival or incisal wall; 2 axial wall towards the pulp. Results : It was observed a high leakage frequency with score 1 among the experimental conditions. There was a higher predominance of score 2 leakage for control group at cementum. Concerning to enamel and cementum, Group C was similar to G1. By comparing control group with G2, and G1 with G2, it was verified statistically significant differences. Conclusion: The laser energy provided a reduction of the marginal leakage at enamel and dentin/ cementum; however, the energy density increase resulted in smaller marginal leakage at enamel and dentin/cementum.
Objetivo: A presença de infiltração marginal é considerada a principal causa de fracasso clínico para restaurações em resina composta. Devido a isso alternativas para promover melhor vedação das margens foram desenvolvidas, como a utilização da energia do Nd:YAG laser. Portanto o objetivo deste estudo foi avaliar in vitro o grau de infiltração marginal em cavidades classe V irradiadas com Nd:YAG laser sobre esmalte e dentina bovinos pré-tratados com sistema adesivo Single Bond (3M ESPE) não-polimerizado. Material e métodos: Cavidades classe V padronizadas foram realizadas em 60 incisivos bovinos. Após realizar o condicionamento ácido, lavagem e secagem os dentes foram aleatoriamente divididos em 3 grupos: G1 Aplicação do sistema adesivo, irradiação com Nd:YAG laser a 140 mJ/pulso em seguida a fotopolimerização. G2 Aplicação do sistema adesivo, irradiação do Nd:YAG laser a 200 mJ/ pulso e fotopolimerização. Grupo C (Controle) Aplicação do sistema adesivo, seguido da fotopolimerização. Restaurações em resina composta foram realizadas e em seguida submetidas a termociclagem em banhos alternados de 2º a 50ºC(±2ºC), totalizando 500 ciclos. Para a avaliação da microinfiltração, os dentes foram submersos em solução de nitrato de prata 50% por 24 h, os dentes foram cortados com 1 mm de espessura e então analisados os níveis de infiltração marginal ocorrida na interface dente-restauração, por meio de de lupa estereoscópica. Os critérios para a análise de infiltração foram: grau 0 nenhuma infiltração; grau 1 parede gengival ou incisal; grau 2 parede axial em direção a polpa. Resultados: Observou-se alta frequência de infiltração marginal grau 1 entre as condições experimentais. Houve predomínio da infiltração grau 2 somente para o grupo controle em cemento. Nos grupos esmalte e cemento, o Grupo C não apresentou diferença estatística entre o G1...