RESUMO

The present study evaluated the mechanical behavior of five designs of Morse taper (MT) connections with and without the application of loads. For this, the detorque of the fixing screw and the traction force required to disconnect the abutment from the implant were assessed. A total of 100 sets of implants/abutments (IAs) with MT-type connections were used, comprising five groups (n = 20/group): (1) Group Imp 11.5: IA sets with a cone angulation of 11.5°; (2) Group SIN 11.5: with a cone angulation of 11.5°; (3) Group SIN 16: with a cone angulation of 16°; (4) Group Neo 16: with a cone angulation of 16°; and (5) Group Str 15: with a cone angulation of 15°. All sets received the torque recommended by the manufacturer. After applying the torque, the counter torque of the fixing screws was measured in ten IA sets of each group without the application of cyclic loads (frequencies ≤ 2 Hz, 360,000 cycles, and force at 150 Ncm). The other ten sets of each group were subjected to cyclic loads, after which the detorque was measured. Afterwards, the force for disconnection between the implant and the abutment was measured by traction on all the samples. The untwisting of the abutment fixation screws showed a decrease in relation to the initial torque applied in all groups. In the unloaded samples, it was found to be -25.7% in Group 1, -30.4% in Group 2, -36.8% in Group 3, -29.6% in Group 4, and -25.7% in Group 5. After the applied loads, it was found to be -44% in Group 1, -43.5% in Group 2, -48.5% in Group 3, -47.2% in Group 4, and -49.8% in Group 5. The values for the IA sets were zero for SIN 16 (Group 3) and Neo16 (Group 4), both without and with loads. In the other three groups, without loads, the disconnection value was 56.3 ± 2.21 N (Group 1), 30.7 ± 2.00 N (Group 2), and 26.0 ± 2.52 N (Group 5). After applying loads, the values were 63.5 ± 3.06 N for Group 1, 34.2 ± 2.45 N in Group 2, and 23.1 ± 1.29 N in Group 5. It was concluded that in terms of the mechanical behavior of the five designs of MT IA sets, with and without the application of loads, the Imp 11.5, SIN 11.5, and Srt 15 groups showed better results compared to the SIN 16 and Neo 16 groups, showing that lower values of cone angulation increase the friction between the parts (IA), thus avoiding the need to maintain the torque of the fixing screw to maintain the union of the sets.

RESUMO

The present study compared three different implant and abutment sets of type Morse taper (MT) connection, with- and without-index, were analyzed regarding their mechanical behavior without and with cyclic load application simulating the masticatory function. Ninety implant and abutment (IA) sets were used in the present study, divided into three groups (n = 30 samples per group): Group A, Ideale solid straight abutment (one piece) without index; Group B, Ideale abutment with an angle of 30-degree (two pieces) without index; Group C, Ideale abutment with an angle of 30-degree (two pieces) with index. The abutment stability quotient (ASQ) values, detorque value and rotation angle were measured before and after the cycling load. Twenty IA sets of each group were submitted to mechanical load at 360,000 cycles. The ASQ without load were 64.7 ± 2.49 for the group A, 60.2 ± 2.64 for the group B, 54.4 ± 3.27 for the group C; With load were 66.1 ± 5.20 for the group A, 58.5 ± 6.14 for the group B, 58.9 ± 2.99 for the group C. Detorque values were lower in groups B and C compared to group A (p < 0.05). In conclusion, the presence of the index did not influence the stability values. However, solid straight abutments (group A) showed higher values of stability compared to groups of angled abutments (groups B and C).

RESUMO

Background: The goal of this in vitro study was to compare three different surfaces: two types of implant surfaces commercially available ([a] smooth/machined and [b] acid-treated surface) versus (c) anodized surface. Discs were manufactured with commercially pure titanium (CP) grade IV, which were subsequently analyzed by scanning microscopy and fibroblastic and osteoblastic cell cultures. Methods: Ninety-nine discs (5 × 2 mm) were manufactured in titanium grade IV and received different surface treatments: (i) Mach group: machined; (ii) AA group: double acid etch; and (iii) AN group: anodizing treatment. Three discs from each group were analyzed by Scanning Electron Microscopy (SEM) to obtain surface topography images and qualitatively analyzed by EDS. Balb/c 3T3 fibroblasts and pre-osteoblastic cells (MC3T3-E1 lineage) were used to investigate each group's biological response (n = 10/cellular type). The data were compared statistically using the ANOVA one-way test, considered as a statistically significant difference p < 0.05. Results: The AA group had numerous micropores with diameters between 5 and 10 µm, while nanopores between 1 and 5 nm were measured in the AN group. The EDX spectrum showed a high titanium concentration in all the analyzed samples. The contact angle and wetting tension were higher in the AA, whereas similar results were observed for the other groups. A lower result was observed for base width in the AA, which was higher in the other two groups. The AN showed the best values in the fibroblast cells, followed by Mach and AA; whereas, in the culture of the MC3T3 cells, the result was precisely the opposite (AA > Mach > AN). There was similar behavior for cell adhesion for the test groups (Mach and AN), with greater adhesion of Balb/c 3T3 fibroblasts compared to MC3T3 cells; in the AA group, there was greater adherence for MC3T3 cells compared to Balb/c 3T3 fibroblasts. Conclusions: The findings suggest that different surface characteristics can produce different biological responses, possibly cell-line dependent. These findings have important implications for the design of implantable medical devices, where the surface characteristics can significantly impact its biocompatibility.

RESUMO

OBJECTIVE: The aim of the present in vitro study was to evaluate the resistance on quasi-static forces and in the fatigue mechanical cycling of a new implant design compared to two other conventional implant designs. MATERIALS AND METHODS: Eighty-eight implants with their respective abutments were tested and distributed into four groups (n = 22 per group): Morse taper connection implant (MT group), conventional external hexagon implant (EH con group), new Collo implant of external hexagon with the smooth portion out of the bone insertion (EH out group), and new Collo implant of external hexagon with the implant platform inserted to the bone level (EH bl group). All the sets were subjected to quasi-static loading in a universal testing machine, and we measured the maximum resistance force supported by each sample. Another 12 samples from each group were submitted to the cyclic fatigue test at 4 intensities of forces (n = 3 per force): 80%, 60%, 40%, and 20%. The number of cycles supported by each sample at each force intensity was evaluated. RESULTS: The three groups of implants with external hexagon connection had similar maximum strength values of the sets (p > 0.05). Meanwhile, samples from the MT group showed the highest resistance values in comparison to the other three groups (p < 0.05). In the fatigue test, the Collo out group supported a smaller number of cycles that led to the fracture than the other 3 groups proposed at loads of 80%, 60%, and 40%, and only at the load value of 20% all groups had the same performance. CONCLUSIONS: Within the limitations of the present in vitro study, the results showed that the new Collo implant performs better when installed at bone level.

Assuntos

RESUMO

BACKGROUND: The ideal installation technique or implant macrogeometry for obtaining an adequate osseointegration in low-density bone tissue follows a challenge in the implantology. AIMS AND OBJECTIVE: The aim of the present study was to evaluate the behavior of three osteotomy techniques and two implant macrogeometries in two low-density polyurethane blocks. The insertion torque (IT), initial stability, pullout resistance, and weight of the residual bone material deposited on the implants were assessed. MATERIALS AND METHODS: A total of 120 implants with two different macrogeometries were used. They were divided into six groups according to the implant macrogeometry and the drilling technique performed (n = 20 implants per group). The implants were installed in polyurethane blocks with pounds per cubic foot (PCF) 10 and PCF 20 densities. The IT, initial stability, pullout resistance, and weight residual bone were measured. RESULTS: Differences were found in the values referring to the macrogeometry of the implants and the type of osteotomy performed. In all groups, the initial stability of the PCF 10 blocks was quite low. The undersized osteotomies significantly increased the values measured in all tests in the PCF 20 density blocks. CONCLUSIONS: In conclusion, even when a modified (undersized) osteotomy technique is used, implants inserted in low-quality bone (type IV) can present problems for osseointegration due their low initial stability and bone resistance. However, the modification in the implant macrogeometry (with healing chambers) presented more quantity of bone on the surface after the pullout test.

RESUMO

The objective of our in vivo study was to compare the effects of the osteotomy on the thermal alterations, the bone healing and count of polymorphonuclear cells, comparing the drill design (cylindrical or conical) using continuous or intermittent movement. Twelve rabbits were used, which were made four osteotomies (n = 2 per tibia) to simulate the surgical drilling sequence for the installation of a dental implant at 8 mm of length and regular diameter. Four groups were proposed: group G1, cylindrical drill with continuous movement; group G2, cylindrical drill with intermittent movement; group G3, conical drill with continuous movement; and, group G4, conical drill with intermittent movement. Thermal mean variation was 6.91 ± 1.4 °C in group 1, 4.30 ± 1.3 °C in group 2, 2.78 ± 0.6 °C in group 3, and 2.77 ± 0.7 °C in group 4. Whereas the mean area of new bone formation was 1.00 ± 0.3 mm2 in group 1, 1.48 ± 0.3 mm2 in group 2, 2.20 ± 0.4 mm2 in group 3, and 2.43 ± 0.4 mm2in group 4. The mean count of polymorphonuclear cells, in the group 1 was 62.4 ± 5.9 cells, group 2 was 50.7 ± 4.2 cells, group 3 was 44.4 ± 3.7 cells, and group 4 was 42.4 ± 3.7 cells. The conical drill sequence produced a significantly smaller increase in temperature during both techniques (continuous and intermittent), more effective new bone formation and a smaller number of polymorphonuclear cells. During the osteotomy for the installation of implants, the professional must take to consider the drill design to perform a less traumatic surgical technique, which can improve and facilitate the healing of peri-implant tissues.

Assuntos

RESUMO

The purpose of the present study was to measure and compare the insertion torque, removal torque, and the implant stability quotient by resonance frequency analysis in different polyurethane block densities of two implant macrogeometries. Four different polyurethane synthetic bone blocks were used with three cortical thickness: Bone 1 with a cortical thickness of 1 mm, Bone 2 with a cortical thickness of 2 mm, Bone 3 with a cortical thickness of 3 mm, and Bone 4, which was totally cortical. Four groups were created in accordance with the implant macrogeometry (n = 10 per group) and surface treatment: G1-regular implant design without surface treatment; G2-regular implant design with surface treatment; G3-new implant design without surface treatment; G4-new implant design with surface treatment. All implants used were 4 mm in diameter and 10 mm in length and manufactured in commercially pure titanium (grade IV) by Implacil De Bortoli (São Paulo, Brazil). The implants were installed using a computed torque machine, and following installation of the implant, the stability quotient (implant stability quotient, ISQ) values were measured in two directions using Osstell devices. The data were analyzed by considering the 5% level of significance. All implant groups showed similar mean ISQ values without statistical differences (p > 0.05), for the same synthetic bone block: for Bone 1, the value was 57.7 ± 3.0; for Bone 2, it was 58.6 ± 2.2; for Bone 3, it was 60.6 ± 2.3; and for Bone 4, it was 68.5 ± 2.8. However, the insertion torque showed similar higher values for the regular macrogeometry (G1 and G2 groups) in comparison with the new implant macrogeometry (G3 and G4 groups). The analysis of the results found that primary stability does not simply depend on the insertion torque but also on the bone quality. In comparison with the regular implant macrogeometry, the new implant macrogeometry decreased the insertion torque without affecting the implant stability quotient values.

RESUMO

Threads of dental implants with healing chamber configurations have become a target to improve osseointegration. This biomechanical and histometric study aimed to evaluate the influence of implant healing chamber configurations on the torque removal value (RTv), percentage of bone-to-implant contact (BIC%), bone fraction occupancy inside the thread area (BAFO%), and bone and osteocyte density (Ost) in the rabbit tibia after two months of healing. Titanium implants with three different thread configurations were evaluated: Group 1 (G1), with a conventional "v" thread-shaped implant design; Group 2 (G2), with square threads; and Group 3 (G3), the experimental group with longer threads (healing chamber). Ten rabbits (4.5 ± 0.5 kg) received three implants in each tibia (one per group), distributed in a randomized manner. After a period of two months, the tibia blocks (implants and the surrounding tissue) were removed and processed for ground sectioning to evaluate BIC%, BAFO%, and osteocyte density. The ANOVA one-way statistical test was used followed by the Bonferoni's multiple comparison test to determine individual difference among groups, considering a statistical difference when p < 0.05. Histometric evaluation showed a higher BAFO% values and Ost density for G3 in comparison with the other two groups (G1 and G2), with p < 0.05. However, the RTv and BIC% parameters were not significantly different between groups (p > 0.05). The histological data suggest that the healing chambers in the implant macrogeometry can improve the bone reaction in comparison with the conventional thread design.

RESUMO

The physical characteristics of an implant surface can determine and/or facilitate osseointegration processes. In this sense, a new implant surface with microgrooves associated with plus double acid treatment to generate roughness was evaluated and compared in vitro and in vivo with a non-treated (smooth) and double acid surface treatment. Thirty disks and thirty-six conical implants manufactured from commercially pure titanium (grade IV) were prepared for this study. Three groups were determined, as described below: Group 1 (G1), where the samples were only machined; group 2 (G2), where the samples were machined and had their surface treated to generate roughness; and test group 3 (G3), where the samples were machined with microgrooves and the surface was treated to generate the roughness. For the in vitro analysis, the samples were submitted to scanning microscopy (SEM), surface profilometry, the atomic force microscope (MFA) and the surface energy test. For the in vivo analyses, thirty-six implants were placed in the tibia of 9 New Zealand rabbits in a randomized manner, after histological and histomorphometric analysis, to determine the level of contact between the bone and implant (BIC%) and the bone area fraction occupancy (BAFO%) inside of the threads. The data collected were statistically analyzed between groups (p < 0.05). The in vitro evaluations showed different roughness patterns between the groups, and the G3 group had the highest values. In vivo evaluations of the BIC% showed 50.45 ± 9.57% for the G1 group, 55.32 ± 10.31% for the G2 group and 68.65 ± 9.98% for the G3 group, with significant statistical difference between the groups (p < 0.0001). In the BAFO% values, the G1 group presented 54.97 ± 9.56%, the G2 group 59.09 ± 10.13% and the G3 group 70.12 ± 11.07%, with statistical difference between the groups (p < 0.001). The results obtained in the evaluations show that the surface with microgrooves stimulates the process of osseointegration, accelerating the healing process, increasing the contact between the bone and the implant and the area of new bone formation.

RESUMO

OBJECTIVES: The aim of this study was to perform an in vivo histological comparative evaluation of bone formation around titanium (machined and treated surface) and zirconia implants. For the present study were used 50 commercially pure titanium implants grade IV, being that 25 implants with a machined surface (TiM group), 25 implants with a treated surface (TiT group) and, 25 implants were manufactured in pure zirconia (Zr group). The implants (n = 20 per group) were installed in the tibia of 10 rabbits. The implants distribution was randomized (n = 3 implants per tibia). Five implants of each group were analyzed by scanning electron microscopy and an optical laser profilometer for surface roughness characterization. Six weeks after the implantation, 10 implants for each group were removed in counter-torque for analysis of maximum torque value. The remaining samples were processed, included in historesin and cut to obtain non-decalcified slides for histomorphological analyses and histomorphometric measurement of the percentage of bone-implant contact (BIC%). Comparisons were made between the groups using a 5% level of significance (p < 0.05) to assess statistical differences. The results of removal torque values (mean ± standard deviation) showed for the TiM group 15.9 ± 4.18 N cm, for TiT group 27.9 ± 5.15 N cm and for Zr group 11.5 ± 2.92 N cm, with significant statistical difference between the groups (p < 0.0001). However, the BIC% presented similar values for all groups (35.4 ± 4.54 for TiM group, 37.8 ± 4.84 for TiT group and 34.0 ± 6.82 for Zr group), with no statistical differences (p = 0.2171). Within the limitations of the present study, the findings suggest that the quality of the new bone tissue formed around the titanium implants present a superior density (maturation) in comparison to the zirconia implants.