RESUMO
The aim of this study is to evaluate the temperature change on specimens of primary enamel irradiated with different pulse duration of Nd:YAG laser. Fifteen sound primary molars were sectioned mesiodistally, resulting in 30 specimens (3.5 × 3.5 × 2.0 mm). Two small holes were made on the dentin surface in which K-type thermocouples were installed to evaluate thermal changes. Specimens were randomly assigned in 3 groups (n = 10): A = EL (extra long pulse, 10.000 µs), B = LP (long pulse, 700 µs), and C = SP (short pulse, 350 µs). Nd:YAG laser (λ = 1.064 µm) was applied at contact mode (10 Hz, 0.8 W, 80 mJ) and energy density of 0.637 mJ/mm(2). Analysis of variance (ANOVA) was performed for the statistical analysis (P = 0.46). Nd:YAG laser pulse duration provided no difference on the temperature changes on primary enamel, in which the following means were observed: A = EL (23.15°C ± 7.75), B = LP (27.33°C ± 11.32), and C = SP (26.91°C ± 12.85). It can be concluded that the duration of the laser pulse Nd:YAG increased the temperature of the primary enamel but was not influenced by different pulse durations used in the irradiation.
Assuntos
Esmalte Dentário/fisiologia , Lasers de Estado Sólido , Temperatura , Humanos , Lasers de Estado Sólido/normas , Fatores de TempoRESUMO
The preservation and restoration of severely weakened pulpless teeth is a difficult and relatively unpredictable procedure. This study evaluated the resistance to fracture of experimentally weakened bovine roots internally reconstructed with different filling materials in combination with prefabricated post compared with restored roots that were relatively intact. The roots of 75 mandibular bovine incisors with similar bulks were selected. Of these, 60 were internally prepared to standardized dimensions, thereby simulating weakness. All roots were filled with different restorative materials. The specimens were submitted to the fracture resistance testing with the application of a tangential compressive loading at an angle of 135 degrees in relation to the long axes of the roots. Results indicated statistically significant differences in relation to the root conditions. Weakened roots were less resistant to fracture than were controls. The roots restored with the resin cement demonstrated the lowest fracture resistance values, but statistically significant differences were observed only when compared with those restored by the resin-modified glass-ionomer cement. Resin-modified glass-ionomer cement, polyacid-modified resin composite and resin composite behaved similarly without statistically significant differences among them. None of the materials evaluated were capable of achieving the fracture resistance recorded for unweakened controls.
Assuntos
Análise do Estresse Dentário/métodos , Cimentos de Resina/análise , Fraturas dos Dentes/prevenção & controle , Raiz Dentária/fisiologia , Análise de Variância , Animais , Bovinos , Cimentos de Ionômeros de Vidro/análiseRESUMO
The preservation and restoration of severely weakened pulpless teeth is a difficult and relatively unpredictable procedure. This study evaluated the resistance to fracture of experimentally weakened bovine roots internally reconstructed with different filling materials in combination with prefabricated post compared with restored roots that were relatively intact. The roots of 75 mandibular bovine incisors with similar bulks were selected. Of these, 60 were internally prepared to standardized dimensions, thereby simulating weakness. All roots were filled with different restorative materials. The specimens were submitted to the fracture resistance testing with the application of a tangential compressive loading at an angle of 135 in relation to the long axes of the roots. Results indicated statistically significant differences in relation to the root conditions. Weakened roots were less resistant to fracture than were controls. The roots restored with the resin cement demonstrated the lowest fracture resistance values, but statistically significant differences were observed only when compared with those restored by the resin-modified glass-ionomer cement. Resin-modified glass-ionomer cement, polyacid-modified resin composite and resin composite behaved similarly without statistically significant differences among them. None of the materials evaluated were capable of achieving the fracture resistance recorded for unweakened controls