RESUMO
This paper proposes the study of a solar-based photocatalytic ozonation process for the degradation of salicylic acid (SA) using a novel S-scheme ZnO/Cu2O/CuO/carbon xerogel photocatalyst. The incorporation of CuO and Cu2O aims to enhance charge mobility through the formation of p-n heterojunctions with ZnO, whereas the carbon xerogel (XC) was selected due to its eco-friendly nature, capacity to stabilize S-scheme heterojunctions as a solid-state electron mediator, and ability to function as a reducing agent under high temperatures. The characterization of the composites demonstrates that the presence of the XC during the calcination step led to the reduction of a fraction of the CuO into Cu2O, forming a ternary semiconductor heterojunction system. In terms of photocatalysis, the XC/ZnO-CuxO 5% composite achieved the best efficiency for salicylic acid degradation, mainly due to the stabilization of the S-scheme charge transfer pathway between the ZnO/CuO/Cu2O semiconductors by the XC. The total organic carbon (TOC) removal during heterogeneous photocatalysis was 80% for the solar-based process and 68% for the visible light process, after 300 min. The solar-based photocatalytic ozonation process was highly successful regarding the degradation of SA, achieving a 75% increase in the apparent reaction rate constant when compared to heterogeneous photocatalysis. Furthermore, a 78% TOC removal was achieved after 150 min, which is half the time required by the heterogeneous photocatalysis to obtain the same result. Temperature, salinity, and turbidity had major effects on the efficiency of the photocatalytic ozonation process; the system's pH did not cause any major performance variation, which holds relevance for industrial applications.
Assuntos
Ozônio , Óxido de Zinco , Temperatura , Salinidade , Carbono , Ácido Salicílico , Concentração de Íons de HidrogênioRESUMO
The main objective of this study is to develop a novel dual-purpose material based on carbon xerogel microspheres (CXMs) that permits the delayed release of cannabidiol (CBD) and the removal of aflatoxin. The CXMs were prepared by the sol-gel method and functionalized with phosphoric acid (CXMP) and melamine (CXMN). The support and the modified materials were characterized by scanning electronic microscopy (SEM), N2 adsorption at -196 °C, X-ray photoelectron spectroscopy (XPS), and zeta potential. For the loading of the cannabidiol (CBD) in the porous samples, batch-mode adsorption experiments at 25 °C were performed, varying the concentration of CBD. The desorption kinetics was performed at two conditions for simulating the gastric (pH of 2.1) and intestinal (pH of 7.4) conditions at 37 °C based on in vitro CBD release. Posteriorly, the samples obtained after desorption were used to study aflatoxin removal, which was evaluated through adsorption experiments at pH = 7.4 and 37 °C. The adsorption isotherms of CBD showed a type I(b) behavior, with the adsorbed uptake being higher for the support than for the modified materials with P and N. Meanwhile, the desorption kinetics of CBD at gastric conditions indicated release values lower than 8%, and the remaining amount was desorbed at pH = 7.4 in three hours until reaching 100% based on the in vitro experiments. The results for aflatoxin showed total removal in less than 30 min for all the materials evaluated. This study opens a broader landscape in which to develop dual-purpose materials for the delayed release of CBD, improving its bioavailability and allowing aflatoxin removal in gastric conditions.