RESUMO
Aim: To evaluate the protection offered by commercial mouthwashes containing sodium fluoride or stannous chloride associated with sodium fluoride to enamel and dentin, prior to erosive and abrasive cycling. Materials and Methods: Enamel and dentin samples were obtained from bovine incisors and subdivided into 3 groups (n=10), according to the fluoridated ingredient tested: FS (sodium fluoride - NaF (225 ppm)); FE (tin fluoride - NaF + SnCl2 (800 ppm Sn2+)); control (distilled water). The samples were submitted to an erosive/abrasive cycle with immersion in citric acid (lemon soda for 5 min, 4×/day, 5 days, with remineralization intervals in artificial saliva for 60 min). Abrasion was carried out with an electric brush (200 g/force) after the first and last cycles, 2x/day, and immediately afterward immersed in the tested solutions. Structure loss was obtained by optical profilometry. The data were subjected to analysis of variance and multiple comparison for each substrate separately. Results: For enamel there was a difference between the groups (p = 0.027), with the FS showing less loss of structure compared to the control 2.02 (±0.48). The FE group showed similar loss to the control and FS 2.32 (±0.58)ab. For dentin there was a difference between the groups (p = 0.011), with FE showing less loss of structure compared to the other groups, 0.82 (25% - 0.34; 75% - 0.95). Discussion: The protection of fluorides in erosive/abrasive challenges depends on the type and dental substrate. Conclusion: Mouthwash with sodium fluoride prior to erosive/abrasive challenges caused less loss of enamel surface, while for dentin, sodium fluoride associated with stannous chloride caused less loss of structure.
Objetivo: Avaliar a proteção oferecida por soluções para bochecho de fluoreto de sódio ou cloreto de estanho associado ao fluoreto de sódio ao esmalte e à dentina, previamente à ciclagem erosiva e abrasiva. Materiais e Métodos: Amostras de esmalte e dentina foram obtidas a partir de incisivos bovinos e subdivididas em 3 grupos (n=10), de acordo com o princípio ativo fluoretado testado: FS (fluoreto de sódio - NaF (225 ppm)); FE (fluoreto de estanho - NaF + SnCl2 (800 ppm Sn2+)); controle (água destilada). As amostras foram submetidas a um ciclo erosivo/abrasivo com imersão em ácido cítrico (refrigerante de limão por 5 min, 4×/dia, 5 dias, com intervalos de remineralização em saliva artificial por 60 min). A abrasão foi realizada com escova elétrica (200 g/força) após o primeiro e o último ciclos, 2×/dia, e logo em seguida imersos nas soluções testadas. A perda de estrutura foi obtida por perfilometria óptica. Os dados foram submetidos à análise de variância e comparação múltipla para cada substrato separadamente. Resultados: Para esmalte houve diferença entre os grupos (p = 0,027), tendo o FS apresentados menor perda de estrutura comparado ao controle 2,02 (±0,48). O grupo FE apresentou perda similar ao controle e ao FS 2,32 (±0,58)ab. Para dentina houve diferença entre os grupos (p = 0,011), sendo que o FE apresentou menor perda de estrutura comparado aos demais grupos 0,82 (25% - 0,34; 75% - 0,95). Discussão: A proteção dos fluoretos em desafios erosivos/abrasivos depende do tipo e do substrato dental. Conclusão: O bochecho com fluoreto de sódio previamente aos desafios erosivos/abrasivos apresentou menor perda de superfície em esmalte, enquanto para dentina o fluoreto de sódio associado ao cloreto de estanho apresentou menor perda de estrutura.
RESUMO
Recent evidence suggests that head-and-neck radiotherapy (HNRT) increases active forms of matrix metalloproteinase-20 (MMP-20) in human tooth crowns, degrading the dentin-enamel junction (DEJ) and leading to enamel delamination, which is a pivotal step in the formation of radiation-related caries (RRC). Additional participation of enzymatic degradation of organic matrix components in caries progression was attributed to MMP-20 in dentin. Therefore, the current study tested the hypothesis that MMP-20 is overexpressed in the DEJ, dentin-pulp complex components, and carious dentin of post-HNRT patients, leading to detectable micromorphological changes to the enamel and dentin. Thirty-six teeth were studied, including 19 post-HNRT specimens and 17 nonirradiated controls. Optical light microscopy was used to investigate the micromorphological components of the DEJ, dentin-pulp complex components, and carious dentin. The samples were divided into 2 subgroups: nondemineralized ground sections (n = 20) and demineralized histological sections (n = 16). In addition, immunohistochemical analysis using the immunoperoxidase technique was conducted to semiquantitatively assess MMP-20 expression in the DEJ, dentin-pulp complex components, and carious dentin. No apparent damage to the DEJ microstructure or other dentin-pulp complex components was observed and no statistically significant differences were detected in MMP-20 expression (p > 0.05) between the irradiated and control groups. This study rejected the hypothesis that MMP-20 is overexpressed in the DEJ, dentin-pulp complex components, and carious dentin of post-HNRT patients, leading to detectable micromorphological changes. Hence, direct effects of radiation may not be regarded as an independent factor to explain aggressive clinical patterns of RRC.