RESUMO

Aim: This study aimed to evaluate the effects of polywave and monowave light-emitting diode curing units on the microtensile bond strength and failure types of three bulk-fill resin composites. Materials and Methods: This in vitro experimental study was performed on 180 microbars obtained from human third molars and were distributed into 12 groups according to the type of bulk-fill resin composite and the light-curing unit. Third molars were restored using Filtek One Bulk Fill Restorative, Tetric® N-Ceram Bulk Fill, and Opus Bulk Fill resin composites was light-cured with Elipar Deep Cure L and Valo in three modes: standard, high power, and extra power. Subsequently, microtensile analysis was carried out with a universal testing machine and the type of failure with an optical stereomicroscope. For statistical analysis, the Kruskal-Wallis H-test was used, with the Bonferroni post hoc test and Fisher's exact test, considering a significance of p<0.05. Results: There were significant differences in the microtensile bond strength between the Filtek One Bulk Fill restorative and Opus Bulk-Fill (p = 0.042) when light was cured with the polywave unit at standard power. On the other hand, the Filtek One Bulk Fill Restorative and Opus Bulk Fill resins showed significant differences in microtensile bond strength when light was cured with the monowave unit compared with the polywave unit (p<0.05). Conclusion: The presence of alternative photoinitiator systems that are more reactive than camphorquinone produced higher microtensile bond strength in Tetric N-Ceram Bulk Fill and Opus Bulk Fill resins when light-cured with a high and standard polywave unit, respectively, compared to Filtek One Bulk Fill resins. Finally, Tetric N-Ceram Bulk Fill and Opus Bulk Fill resins had the highest percentage of mixed failures, while Filtek One Bulk Fill resin had adhesive failures, which was related to its lower microtensile bond strength.

RESUMO

OBJECTIVES: To compare, in vitro, resin cement excess removal techniques at the veneer-tooth interface. MATERIALS AND METHODS: Anterior human teeth were restored with ceramic veneers and randomly divided according to the following techniques (n = 10): removal of excess resin cement with brush and dental floss, followed by light-curing with Valo (Group 1) or Elipar (Group 2) for 1 min and 40 s; tack-curing with Valo (Group 3) or Elipar (Group 4) for 1 s; and tack-curing with Valo (Group 5) or Elipar (Group 6) for 5 s. The tack-curing was followed by removal of excess with probe and dental floss and light-curing for 1 min and 40 s. The area of excess resin cement (mm2) was measured in micro-CT images using AutoCAD program. The failures at the cervical margin in the X, Y, and Z axes (µm) of greater value were measured using the DataViewer program. The specimens were submitted to microleakage with 2% basic fuchsin. RESULTS: According to the Kruskal-Wallis and multiple comparison test, the highest area of excess resin cement was found in Group 1 (5.06 mm2), which did not differ statistically from Groups 2 (3.70 mm2) and 5 (2.19 mm2). Groups 2, 3 (1.73 mm2), 4 (1.14 mm2), and 5 (2.18 mm2) did not differ statistically. Group 6 (0.77 mm2) obtained the lowest value, which did not differ statistically from Groups 3 and 4. According to the Kruskal-Wallis and Dunn test, there was no significant difference in failures in X (p = 0.981), Y (p = 0.860), and Z (p = 0.638) axes and no significant difference in microleakage (p = 0.203) among the groups. CONCLUSIONS: Tack-curing for 1 s or 5 s, followed by removal of excess resin cement using a probe and a dental floss, tended to result in a lower amount of excess material around the margin. CLINICAL RELEVANCE: The technique used for resin cement excess removal influences the amount of excess leaved at the veneer-tooth interface. Tack-curing for 1 s or 5 s is recommended to mitigate the excess resin cement.

Assuntos

RESUMO

OBJECTIVES: To evaluate the effect of mono and multi-wave light-curing units (LCUs) on the Knoop hardness of resin-based composites (RBC) that use different photoinitiators. METHODS: Central incisor-shaped specimens 12 mm long, 9 mm wide, and 1.5 mm thick were made from 2 RBCs that use different photoinitiators: Tetric N-Ceram (Ivoclar Vivadent) - and Vittra APS (FGM), both A2E shade. They were light-cured with 4 different LCUs: two claimed to be multi-wave - VALO Grand (Ultradent) and Emitter Now Duo (Schuster); and two were monowave - Radii Xpert (SDI) and Elipar DeepCure-L (3 M Oral Care) using 2 different light exposure protocols: one 40 s exposure centered over the specimen; and two 20 s light exposures that delivered light from two positions to better cover the entire tooth. 16 groups with 10 specimens in each group were made. The Knoop hardness (KH, kg/mm2) was measured at the top and bottom of the specimen in the center and at the cervical, incisal, mesial, and distal peripheral regions. The active tip diameters (mm) and spectral radiant powers (mW/nm) of the LCUs were measured with and without the interposition of the RBC, as well as the radiant exposure beam profiles (J/cm²) delivered to the top of the RBCs. The data was analyzed using Three-way ANOVA and Tukey's tests (α = 0.05). RESULTS: The VALO Grand (1029 mW) emitted twice the power of the Radii Xpert (500 mW). The KH values of VI and TN resin composite specimens were significantly affected by the LCU used (p < .001), the measurement location (p < .001), and the surface of the specimen (p < .001). LCUs with wider tip diameters produced greater Knoop hardness values at the peripheries of the 12 mm of long, 9 mm wide specimens. In general, the VALO Grand produced the highest KH values, followed by Elipar DeepCure-L, then by Radii Xpert. The Emitter Now Duo LCU produced the lowest values. Exposing the veneers from two locations reduced the differences between the LCUs and the effect of the measurement location. Only the VALO Grand could fully cover the composite veneer with light when the two locations were used. SIGNIFICANCE: The light tip must cover the entire restoration to photocure the RBC beneath the light tip.

Assuntos

RESUMO

OBJECTIVE: To evaluate the effect of delayed light-curing of dual-cure bulk-fill composites on internal adaptation and microhardness (KHN) in depth. MATERIALS AND METHODS: Bulk-fill composites were placed in 35 box-shaped preparations and cured according to the following protocols (n = 5): Filtek Bulk-Fill light-cured immediately after insertion (FBF); Bulk-EZ light-cured immediately after insertion (BEZ-I); Bulk-EZ light-cured 90 s after insertion (BEZ-DP); Bulk-EZ self-cured (BEZ-SC); HyperFIL light-cured immediately after insertion (HF-I); HyperFIL light-cured 90 s after insertion (HF-DP); HyperFIL self-cured (HF-SC). After 24 h, the samples were axially sectioned, and the internal adaptation was evaluated using replicas under a scanning electron microscope. The KHN was evaluated at six depths (0.3 mm, 1 mm, 2 mm, 3 mm, 4 mm, and 5 mm). The statistical analysis was performed using α = 0.05. RESULTS: The KHN significantly decreased with depth, except in self-curing mode, when it was similar at all depths. Delayed light-curing significantly increased the KHN at higher depths. The internal adaptation was material-dependent. Light-curing did not influence the internal adaptation of HyperFIL, whereas delayed light-curing significantly reduced the internal gaps (%) of Bulk-EZ. CONCLUSION: Delayed light-curing improved the depth of cure of dual-cure resin composites. Light-curing did not influence the internal adaptation of HyperFIL, but delayed light-curing improved the internal adaptation of Bulk-EZ. CLINICAL SIGNIFICANCE: Light-curing is fundamental for improving the mechanical properties of dual-cure resin composites. Moreover, depending on the dual-cure resin composite, the delay in light-curing can reduce the internal gaps.

Assuntos

RESUMO

OBJECTIVE: Evaluate the effect of thickness of high-translucency (HT) CAD/CAM materials on irradiance and beam profile from a blue light-emitting diode light-curing unit (LCU) and on the degree of conversion (DC) and maximum polymerization rate (Rpmax ) of a light-cured resin cement (LCC). MATERIAL AND METHODS: The direct output from the LCU, the light transmission and irradiance ratio (IR) through one conventional composite and nine HT CAD/CAM materials (0.5, 1.0, 1.5, or 2.0-mm thick; n = 5) were measured with a integrating sphere coupled to a spectrometer. The light beam was assessed with a beam profiler camera. The DC at 600 s and the Rpmax of one LCC was determined using a Fourier transform infrared spectrometer (n = 5). Data were analyzed by ANOVA followed by Tukey's tests, and Dunnett's test was also used for irradiance data (α = 0.05). RESULTS: A significant decrease in irradiance through all materials occurred as thickness increased. Thin CAD/CAM materials improved light homogeneity, which decreased with the increase in thickness. The DC of the LCC directly exposed to light was the same as when exposed to 45%, 25%, 15%, or 5% IRs. Rpmax decreased with the decrease in IR. CONCLUSIONS: Although the HT CAD/CAM materials reduced the irradiance from the LCU, minor effects were observed in the LCC's DC. CLINICAL SIGNIFICANCE: Despite the light attenuation of blue light through different CAD/CAM materials that were up to 2-mm thick, the degree of conversion of one brand of light-cured resin cement was clinically acceptable when the LCU was used for 30 s.

Assuntos

RESUMO

Resumo OBJETIVO: Avaliar a resistência ao cisalhamento e o Índice de Remanescente Adesivo (IRA) de bráquetes metálicos colados com três diferentes fotopolimerizadores LED de alta potência, quando comparados ao LED convencional. MATERIAIS E MÉTODOS: 80 incisivos bovinos foram divididos aleatoriamente em 4 grupos (n=20), nos quais foram realizadas colagens dos bráquetes utilizando-se os seguintes LEDs de alta potência por 3s: Grupo 1 ­ LEDX ­ T 2400, Orthometric; Grupo 2 ­ Flashmax P4 PRO Ortho, Rock Moutain Orthodontics; Grupo 3 ­ VALO CORDLESS, Ultradent e Grupo 4 ­ LED convencional por 40s (controle) POLY-WIRELESS, Kavo. O teste de resistência ao cisalhamento foi realizado utilizando-se uma máquina de ensaio universal (AME-2kN, Oswaldo Filizola, São Paulo, Brasil) com velocidade de 0,5mm/min e célula de carga de 50N. A determinação da diferença estatística entre os grupos em relação ao cisalhamento foi realizada usando-se a análise de variância (ANOVA). Para avaliação do IRA, foi aplicado o teste Kruskal-Wallis. RESULTADOS: O grupo 2 apresentou resistência ao cisalhamento significativamente superior aos demais LEDs de alta potência e foi similar ao LED convencional. Em relação ao IRA, houve diferença estatisticamente significante entre os grupos e o único que não diferiu do grupo controle foi o 2, enquanto os demais LEDs de alta potência (Grupos 1 e 3) apresentaram mais falhas adesivas entre a resina e o esmalte. CONCLUSÃO: Houve diferença entre os três tipos de fotopolimerizadores LED de terceira geração, sendo que maior resistência ao cisalhamento e menos falhas adesivas foram observadas no LED que apresentou maior potência (AU)

Abstract OBJECTIVE: To evaluate shear strength and Adhesive Remnant Index (ARI) of metallic brackets bonded to three types of high-power LED light curing, when compared to conventional LED. MATERIALS AND METHODS: 80 bovine incisors were divided into 4 groups (n = 20), in which brackets were bonded using the following high-power LEDs for 3s: Group 1 ­ LEDX ­ T 2400, Orthometric; Group 2 ­ Flashmax P4 PRO Ortho, Rock Mountain Orthodontics; Group 3 ­ VALO CORDLESS, Ultradent; and Group 4 ­ conventional LED for 40s (control) POLY-WIRELESS, Kavo. The shear strength test was performed using a universal test machine (AME-2kN, Oswaldo Filizola, São Paulo, Brasil) with 0.5 mm/min speed and 50N load cell. The determination of statistical difference between the groups in relation to shear strength was performed using analysis of variance (ANOVA). The Kruskal-Wallis test was used to assess the IRA. RESULTS: Group 2 showed shear strength significantly higher than other high-power LEDs and was similar to conventional LED. Regarding ARI, there was a statistically significant difference between the groups and the only one that did not differ from the control group was 2, while the other high-power LEDs (Groups 1 and 3) had more adhesive failures between the resin and the enamel. CONCLUSION: There was a difference between the three types of third generation LED light curing agents, with greater shear strength and less adhesive failures observed in the LED that presented higher power. (AU)

Assuntos

RESUMO

Objective: The present study aims to evaluate the color stability and degree of conversion of amine-free dual cured resin cement compared to light cured and amine-containing dual cured resin cements used with two different translucencies of thin esthetic restorations. Material and Methods: A total of 120 specimens were prepared for color stability testing (n=60). The specimens were divided into three main groups according to the resin cement type. Group 1: amine-free dual cured, Group 2: light cured, Group 3: amine-containing dual cured. Each group was further subdivided according to the ceramic translucency into two subgroups: high and low translucency. Color stability was assessed by a spectrophotometer before and after thermal aging. For the degree of conversion assessment (n=60), Fourier transform infrared spectroscopy was used at three different time intervals. Statistical analysis was performed using multi-factorial ANOVA, followed by one-way ANOVA with Bonferroni correction. Results: Amine-containing resin cement showed significantly higher ΔEab and ΔE00in both translucencies (4.5±0.3, 3.5±0.3 respectively for high translucency ceramic and 3.8±0.4, 3.0±0.3 respectively for low translucency) than the other tested cements (p<0.001). The highest degree of conversion (DC) was shown after 2 weeks by the amine-free dual cured resin cement (86.27±0.74). Conclusion: Amine-free dual cured resin cement can be an alternative to light cured one for cementation of thin veneers since it showed comparable color stability and high degree of conversion (AU)

Objetivo: O presente estudo tem como objetivo avaliar a estabilidade de cor e o grau de conversão do cimento resinoso dual sem amina em comparação com cimentos resinosos fotopolimerizáveis contendo amina usados com duas translucidezes diferentes em restaurações estéticas definitivas. Material e Métodos: Um total de 120 espécimes foram preparados para teste de estabilidade de cor (n=60). Os espécimes foram divididos em três grupos principais de acordo com o tipo de cimento resinoso. Grupo 1: polimerização dupla sem amina, Grupo 2: fotopolimerização, Grupo 3: polimerização dupla contendo amina. Cada grupo foi ainda subdividido de acordo com a translucidez da cerâmica em dois subgrupos: alta e baixa translucidez. A estabilidade da cor foi avaliada por um espectrofotômetro antes e após o envelhecimento térmico. Para a avaliação do grau de conversão (n=60), a espectroscopia de infravermelho com transformada de Fourier foi usada em três intervalos de tempo diferentes. A análise estatística foi realizada usando ANOVA multifatorial, seguida de ANOVA um faot com correção de Bonferroni. Resultados: O cimento resinoso contendo amina apresentou ΔEab e ΔE00 significativamente maiores em ambas as translucidezes (4,5±0,3, 3,5±0,3 respectivamente para cerâmica de alta translucidez e 3,8±0,4, 3,0±0,3 respectivamente para baixa translucidez) do que os outros cimentos testados (p< 0,001). O maior grau de conversão (DC) foi mostrado após 2 semanas pelo cimento resinoso dual sem amina (86,27±0,74). Conclusão: O cimento resinoso dual sem amina pode ser uma alternativa ao cimento polimerizável na restauração de facetas finas, uma vez que apresentou estabilidade de cor comparável e alto grau de conversão. (AU).

Assuntos

RESUMO

Objective: Evaluate the mechanical properties of experimental adhesive models with different photoinitiators (PI) polymerized by LED units of different power densities. Material and Methods: Three groups of adhesive models based on HEMA/BisGMA (45/55) were prepared in association with different PI combinations: G2 (control) ­ 2 PI: 0.5% CQ, 0.5% EDMAB; G3 - 3 PI: 0.5% CQ; 0.5% DMAEMA, 0.5% DPIHP; G4 - 4 PI: 0.5% CQ; 0.5% EDMAB; 0.5% DMAEMA; 0.5% DPIHP. The three formulations were polymerized at two different LED power densities: 550 mW/cm2 and 1200 mW/cm2. The degree of conversion (DC) of adhesive monomers was monitored in situ through the FTIR for 600 s. Specimens were prepared for each formulation for analysis mong adhesive systems (G2

Objetivo: Avaliar as propriedades mecânicas de modelos adesivos experimentais com diferentes fotoiniciadores (PI) polimerizados por unidades de LED de diferentes densidades de energia. Material e Métodos: Três grupos de modelos adesivos baseados em HEMA/BisGMA (45/55) foram preparados em associação com diferentes combinações de PI: G2 (controle) ­ 2 PI: 0,5% CQ, 0,5% EDMAB; G3 - 3PI: 0,5% CQ; 0,5% DMAEMA, 0,5% DPIHP; G4 - 4 PI: 0,5% CQ; 0,5% EDMAB; 0,5% DMAEMA; 0,5% DPIHP. As três formulações foram polimerizadas em duas densidades de potência de LED: 550 mW/cm2 e 1200 mW/cm2. O grau de conversão (DC) dos monômeros adesivos foi monitorado in situ através do FTIR durante 600 s. Amostras foram preparadas para cada formulação para análise de resistência à flexão (FS), módulo de elasticidade (ME), sorção (SOR) e solubilidade (SOL). Os dados foram submetidos aos testes ANOVA 2-fatores e Tukey (5%). Resultados: DC: houve diferença significativa entre os sistemas adesivos (G2

Assuntos

RESUMO

Objective: Compare the pH values and calcium ion release of calcium hydroxide-based liner materials before and after light-curing. Material and Methods: The materials evaluated were: hydrox-cal white (HW), hydrox-cal dentin (HD), Biocal (BC) and UltraBlend Plus (UB). 120 samples of the liner materials were inserted into a PVC tube (n=15). The samples from HW+A, HD+A, BC+A and UB+A were subjected to photoactivation. The other groups HW+N, HD+N, BC+N and UB+N were only inserted in a glass tube with deionized water. The pH was measured 24 hours and 14 days after the inclusion of the samples with the aid of a pH meter. The calcium release was analyzed with the aid of an atomic absorption spectophotometer at 24h and 14 days. The results were submitted to the Shapiro-Wilk test, followed by ANOVA and Tukey test (p=0.05). Results: In 24h, the groups that were not light cured showed the highest pH values (p<0.05). In 14 days, BC+N and BC+A demonstrated the lowest pH values. The groups that were not light cured also showed higher calcium release values in 24h and 14 days (p<0.05). Conclusion: Photoactivation of calcium hydroxide-based liner materials negatively interferes with calcium ion release, as well as with pH.(AU)

Objetivo: Comparar os valores de pH e liberação de íons cálcio de materiais forradores à base de hidróxido de cálcio antes e depois da fotopolimerização. Material e métodos: Os materiais avaliados foram: Hidrox-cal branco (HW), Hidrox-cal dentina (HD), Biocal (BC) e UltraBlend Plus (UB). 120 amostras dos materiais de revestimento foram inseridas em um tubo de PVC (n=15). As amostras de HW +A, HD+A, BC+A e UB+A foram submetidas à fotoativação. Os demais grupos HW +N, HD+N, BC+N e UB+N foram inseridos apenas em um tubo de vidro com água deionizada. O pH foi medido 24 horas e 14 dias após a inclusão das amostras com o auxílio de um medidor de pH. A liberação de cálcio foi analisada com o auxílio de um espectrofotômetro de absorção atômica em 24h e 14 dias. Os resultados foram submetidos ao teste de Shapiro-Wilk, seguido de ANOVA e teste de Tukey (p=0,05). Resultados: Em 24h, os grupos não fotopolimerizados apresentaram os maiores valores de pH (p<0,05). Em 14 dias, BC+N e BC+A apresentaram os menores valores de pH. Os grupos não fotopolimerizados também apresentaram maiores valores de liberação de cálcio em 24h e 14 dias (p<0,05). Conclusão: A fotoativação de materiais de revestimento à base de hidróxido de cálcio interfere negativamente na liberação de íons cálcio e no pH (AU)

Assuntos

RESUMO

OBJECTIVE: To evaluate the influence of shades of a multilayered zirconia on light transmission, resin cement degree of conversion, and shear bond strength of resin cement. MATERIALS AND METHODS: The light transmission through opaque (OPQ) and translucent (TNS) regions of Katana UTML zirconia (Kuraray Noritake Dental) were evaluated for using a spectroradiometer (n = 5). Degree of conversion of dual-cure resin cement (Panavia V5, Kuraray Noritake Dental) was measured after light-activation through OPQ or TNS regions and direct exposure. Composition of the zirconia was analyzed with energy dispersive x-ray spectroscopy (EDS). Shear bond strength (SBS) was evaluated on the OPQ and TNS regions after 24 h and 1 year from specimen preparation (n = 15). RESULTS: The OPQ region produced higher irradiance loss (95.1%) than TNS one (92.9%), and lower degree of conversion (52.4%) than TNS (71.2%) at 24 h post-light activation. EDS analysis did not show differences on the microstructure of the OPQ and TNS regions. There were no significant differences on the SBS between zirconia regions. For both zirconia regions, a significant reduction on the SBS occurred after aging, being 31.7% for OPQ and 38% for TNS. CONCLUSION: Both OPQ and TNS regions affected the light transmission through the multilayered zirconia. The OPQ region yielded the highest light attenuation and the lowest degree of conversion of resin cement. Different regions of the zirconia did not influence the SBS. Clinical significance Although opaque and translucent regions of the multilayered zirconia reduced the light transmission from LED curing unit and the degree of conversion of resin cement, the regions did not affect the resin cement adhesion.

Assuntos