RESUMO

Objective: to investigate the effect of two natural cross-linkers on microtensile bond strength (µTBS) and evaluate their influence on the durability of the resin dentin bonds. Material and Methods: the Moringa oleifera and Centella asiatica plant extracts were qualitatively tested with high-performance thin layer chromatography (HPTLC) for the presence of phenols. The phenolic content ranged from 27 to 30 gallic acid equivalents (GAE), µg/mg of dry weight. After etching, two concentrations (5% and 1%) of these two extracts were prepared and used as pretreatment liners on dentin. They were applied for a min. After restoration with resin composite, dentin resin beams were prepared. The study groups were 5% Moringa, 1% Moringa 5% Centella 1% Centella, and control (without cross-linker application). For each group, half of the samples underwent µTBS testing after 24 hours, while the remaining half were immersed in artificial saliva to assess the bond's longevity after 6 months of ageing. Statistical analysis was performed using one-way ANOVA followed by Tukey's post hoc test. Results: both 5% and 1% Moringa showed a significant difference (p<0.05) compared to the other groups at both intervals. However, after ageing, the specimens in the control and 1% Centella groups resulted in a significant decrease in µTBS. Conclusion: overall, both concentrations of Moringa (5% and 1%) were effective in stabilising the bond during both intervals.(AU)

Objetivo: investigar o efeito de dois reticuladores naturais na resistência de união (µTBS) à microtração e avaliar sua influência na durabilidade da adesão da resina à dentina. Material e Métodos: extratos das plantas Moringa oleifera e Centella asiatica foram qualitativamente testados através de cromatografia em camada fina de alta performance (HPTLC) para a presença de fenóis. O conteúdo fenólico alcançou entre 27 a 30 equivalentes de ácido gálico (GAE), µg/mg de peso seco. Após o condicionamento, duas concentrações (5% e 1%) dos extratos foram preparadas e utilizadas como forros de pré-tratamento em dentina. Eles foram aplicados por um minuto. Após a restauração com resina composta, palitos de dentina e resina foram preparados. Os grupos foram 5% Moringa, 1% Moringa, 5% Centella, 1% Centella e controle (sem aplicação de reticulador). Para cada grupo, metade das amostras foram submetidas ao teste µTBS após 24 horas, enquanto a outra metade foi imersa em saliva artificial para avaliar a longevidade adesiva após 6 meses de envelhecimento. Foi realizada análise estatística através de ANOVA 1-fator, seguido do teste post hoc de Tukey. Resultados: ambas as concentrações de 5% e 1% de Moringa demonstraram diferença significativa (p<0.05) comparadas aos outros grupos em ambos os intervalos. No entanto, após o envelhecimento, os espécimes dos geupos controle e 1% de Centella resultaram em uma redução significativa de µTBS. Conclusão: no geral, ambas as concentrações de Moringa (5% e 1%) foram efetivas em estabelecer a adesão em ambos os intervalos (AU)

Assuntos

RESUMO

This work presents an add-on result of cross-linking using photoacoustic spectroscopy (PAS) phases in a multivariable process using the phase-resolved photoacoustic (PRPA) method. The method is tested to separate contributions from groupings -OH, -CH(2)-, -CH(3), and Si-OH overtones in the range from 700 to 2600 nm. Samples of the copolymers ethylene vinyltrimethoxysilane (EVS) and grafted vinyltrimethoxysilane (VTS) on low-density polyethylene (LDPE) were prepared having concentrations (C) of 3, 5, and 7% of catalyst and temperatures (T) of 70, 80, and 90 degrees C. By considering the condensation reaction, the reduction of -OH groups is monitored. The PRPA analysis was carried out using the surface response methodology and results indicated the optimum point for both answers (signal and phase-resolved) and for both factors of interest (C, T). For the copolymers, it was found that C approximately (5.00 +/- 1.14)% and T approximately (82.4 +/- 4.3) degrees C, while for grafted LDPE PE(g) it was found that C approximately (4.92 +/- 0.85)% and T approximately (80.8 +/- 2.5) degrees C. These results agreed with the chemical analysis for gel content, which showed as the optimum point 5% of catalyst and temperature of 80 degrees C. Further, it is an advantage that the photoacoustic method allows one to per- form a nondestructive analysis.

Assuntos