Can low-fusing glass application affect the marginal misfit and bond strength of Y-TZP crowns?
Braz. oral res. (Online)
; 32: e34, 2018. tab, graf
Article
em En
| LILACS
| ID: biblio-889480
Biblioteca responsável:
BR1.1
ABSTRACT
Abstract To evaluate the effect of different surface treatments on the marginal misfit and retentive strength between Y-TZP crowns and an epoxy resin. Forty (40) epoxy resin (G10) abutments (height 5mm, conicity 60, finish line large chamfer) with equal dimensions were milled and included in polyurethane to simulate the periodontal ligament. Next, 40 Y-TZP crowns (thickness 1mm) were milled (Cerec in Lab) and randomly divided into four groups (n=10) according to the surface treatment GS(glaze spray), GP(glaze powder/liquid), P(zirconia primer) and RS(tribochemical silica coating). The conditioned surfaces were cemented with dual self-adhesive cement, light cured and submitted to thermomechanical cycling (2x106, 100N, 4Hz, 5°/55°C). Marginal misfit was analyzed by a stereomicroscope and SEM. Retentive strength test was performed (1mm/min) until crown debonding. Glaze layer thickness was also performed to GS and GP groups. Marginal misfit data were analyzed by Kruskal Wallis and Dunn tests; one-way ANOVA and Tukey (5%) analyzed the tensile strength data. The marginal misfit of the GS (48.6±19.9μm) and GP (65.4±42.5μm) were statistically lower than the RS (96±62.9μm) and P (156±113.3μm) (p=0.001). The retentive strength of the GP (470.5±104.1N) and GS (416.8±170.2N) were similar to the P (342.1±109.7N), but statistically higher than those of the RS (208.9±110N). The GS and GP glaze layer was 11.64μm and 9.73μm respectively. Thus, glaze application promoted lower marginal discrepancy and higher retentive strength values than conventional techniques.
Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
LILACS
Assunto principal:
Ítrio
/
Zircônio
/
Colagem Dentária
/
Adaptação Marginal Dentária
/
Coroas
/
Resinas Epóxi
/
Vidro
Idioma:
En
Revista:
Braz. oral res. (Online)
Assunto da revista:
ODONTOLOGIA
Ano de publicação:
2018
Tipo de documento:
Article
País de afiliação:
Brasil
País de publicação:
Brasil